Samples of titanium alloy VT6 obtained by the method of cold gas dynamic spraying (CGDS) and subjected to hot isostatic pressing (HIP) for lowering the porosity and improving the mechanical properties are studied. The HIP is conducted at a temperature of 900°C and a pressure of 110 MPa. This reduces the volume fraction of pores from 8 to 0.5% and raises the ultimate strength of the samples from 70 to 950 MPa and the elongation by 12%.

中文翻译：

---

热等静压对冷气动态喷涂VT6合金制品组织和性能的影响

对采用冷气动态喷涂(CGDS) 方法获得的钛合金VT6 样品进行热等静压(HIP) 以降低孔隙率和改善机械性能的研究。HIP 在 900°C 的温度和 110 MPa 的压力下进行。这将孔隙的体积分数从 8% 降低到 0.5%，并将样品的极限强度从 70 MPa 提高到 950 MPa，伸长率提高了 12%。