The possibility of obtaining zirconia ceramic fibers by electrospinning was examined. The factors affecting the fiber diameter and the presence of tape inclusions were determined. It was shown that under the action of an electric field the forming solutions make it possible to obtain fibers in a wide range of viscosities. For forming solution viscosity 0.45 – 0.69 Pa ∙ sec the fiber production process stabilizes and the fiber diameter is comparable to that of conventionally produced fibers (0.9 – 1.5 μm).

中文翻译：

---

氧化锆纤维的静电纺丝

研究了通过静电纺丝获得氧化锆陶瓷纤维的可能性。确定了影响纤维直径和带状夹杂物存在的因素。结果表明，在电场作用下，成形溶液可以得到粘度范围很宽的纤维。成型液粘度为0.45 – 0.69 Pa∙sec时，纤维生产过程稳定，纤维直径可与传统生产的纤维（0.9 – 1.5μm）相媲美。