Li 2 Zn 3 Ti 4 O 12 Low-Temperature Co-Fired Ceramic with Li 2 O–B 2 O 3 –SiO 2 Additive
Glass and Ceramics ( IF 0.6 ) Pub Date : 2020-05-25 , DOI: 10.1007/s10717-020-00234-3 D. I. Vershinin , I. N. Khusainov , N. A. Makarov
Glass and Ceramics ( IF 0.6 ) Pub Date : 2020-05-25 , DOI: 10.1007/s10717-020-00234-3 D. I. Vershinin , I. N. Khusainov , N. A. Makarov
Amaterial for low-temperature co-fired ceramic technology was developed in the Li2O–ZnO–TiO2 system for use in the manufacture of electronic components. The sintering temperature of the material was lowered from 1075 to 950°C by introducing 3% of a sintering additive with a eutectic composition in the Li2O–B2O3–SiO2 system. The developed ceramic obtained at 950°C is characterized by density 4.14 g/cm3 together with the following dielectric properties: permittivity ε = 23.1 and dielectric Q factor Q f = 832 MHz.
中文翻译:
含Li 2 O–B 2 O 3 –SiO 2的Li 2 Zn 3 Ti 4 O 12低温共烧陶瓷
Li 2 O–ZnO–TiO 2系统中开发了用于低温共烧陶瓷技术的材料,用于制造电子元件。通过在Li 2 O–B 2 O 3 –SiO 2系统中引入3%具有共晶成分的烧结添加剂,材料的烧结温度从1075降低到950°C 。在950℃下获得的显影陶瓷的特征在于密度为4.14g / cm 3,同时具有以下介电性能:介电常数ε= 23.1,介电Q因子Qf= 832MHz。