Effect of synthesis pH on the physicochemical properties of a synthesized Bi 2 WO 6 and the type of substrate chosen, in assessing its photo-catalytic activities
Arabian Journal of Chemistry ( IF 5.3 ) Pub Date : 2020-01-01 , DOI: 10.1016/j.arabjc.2017.05.014
C. Jaramillo-Páez , J.A. Navío , M.C. Hidalgo

Abstract Crystalline orthorhombic Bi2WO6 powders were synthesized by a hydrothermal method from aqueous solutions of Bi(NO3)3·5H2O and Na2WO4·2H2O over a range of three selected pH values (2.0, 5.0 and 7.0), using NaOH as precipitating agent. The as-prepared catalysts were characterized by XRD, BET, FE-SEM, TEM, XPS and UV-vis spectroscopy. The effect of pH-synthesis on crystallinity, morphologies, surface area and optical absorption properties, were investigated. Although the pH has a marked influence on morphology, the nature of the precipitating agent (NaOH or TEA) also influences the morphology and surface structure composition, as it is observed in the present work. Three different probe molecules were used to evaluate the photo-catalytic properties under two illumination conditions (UV and Visible): Methyl Orange and Rhodamine B were chosen as dye substrates and Phenol as a transparent substrate. The photo-catalytic activities are strongly dependent not only on the pH used in the synthesis but also on the nature of the chosen substrate in assessing the photo-catalytic activities. Results were compared with those obtained when using TiO2(P25, Evonik) in the same experimental conditions. The photo-catalytic activity of one of the synthesised samples has been evaluated by exposing a mixture of Rhodamine B and Phenol in water, to different illumination conditions. Our results provide new evidences about the issue of whether dyes are suitable substrates to assess the activity of a photo-catalyst.

中文翻译:

合成 pH 值对合成的 Bi 2 WO 6 理化性质和所选底物类型的影响,以评估其光催化活性

摘要 以氢氧化钠为沉淀剂,在三个选定的 pH 值范围内(2.0、5.0 和 7.0),以 Bi(NO3)3·5H2O 和 Na2WO4·2H2O 的水溶液为原料,通过水热法合成了结晶正交 Bi2WO6 粉末。通过XRD、BET、FE-SEM、TEM、XPS和UV-vis光谱对所制备的催化剂进行表征。研究了 pH 合成对结晶度、形态、表面积和光吸收特性的影响。尽管 pH 值对形态有显着影响,但沉淀剂(NaOH 或 TEA)的性质也会影响形态和表面结构组成,正如在目前的工作中所观察到的。三种不同的探针分子用于评估两种光照条件(紫外线和可见光)下的光催化性能:选择甲基橙和罗丹明 B 作为染料基材,选择苯酚作为透明基材。光催化活性不仅很大程度上取决于合成中使用的 pH 值,而且还取决于在评估光催化活性时所选底物的性质。结果与在相同实验条件下使用 TiO2(P25,赢创)时获得的结果进行了比较。通过将罗丹明 B 和苯酚在水中的混合物暴露在不同的光照条件下,评估了其中一个合成样品的光催化活性。我们的研究结果为染料是否适合评估光催化剂活性的问题提供了新的证据。光催化活性不仅很大程度上取决于合成中使用的 pH 值,而且还取决于在评估光催化活性时所选底物的性质。结果与在相同实验条件下使用 TiO2(P25,赢创)时获得的结果进行了比较。通过将罗丹明 B 和苯酚在水中的混合物暴露在不同的光照条件下,评估了其中一个合成样品的光催化活性。我们的研究结果为染料是否适合评估光催化剂活性的问题提供了新的证据。光催化活性不仅很大程度上取决于合成中使用的 pH 值,而且还取决于在评估光催化活性时所选底物的性质。结果与在相同实验条件下使用 TiO2(P25,赢创)时获得的结果进行了比较。通过将罗丹明 B 和苯酚在水中的混合物暴露在不同的光照条件下,评估了其中一个合成样品的光催化活性。我们的研究结果为染料是否适合评估光催化剂活性的问题提供了新的证据。通过将罗丹明 B 和苯酚在水中的混合物暴露在不同的光照条件下,评估了其中一个合成样品的光催化活性。我们的研究结果为染料是否适合评估光催化剂活性的问题提供了新的证据。通过将罗丹明 B 和苯酚在水中的混合物暴露在不同的光照条件下,评估了其中一个合成样品的光催化活性。我们的研究结果为染料是否适合评估光催化剂活性的问题提供了新的证据。