Characterization of carbon fiber-reinforced poly(phenylene sulfide) composites prepared with various compatibilizers
Journal of Composite Materials ( IF 2.3 ) Pub Date : 2019-06-27 , DOI: 10.1177/0021998319859063
Bedriye U Durmaz 1 , Ayse Aytac 1, 2
Affiliation  

The aim of this study was to investigate the effects of different compatibilizers on the properties of polyamide-sized carbon fiber-reinforced poly(phenylene sulfide) composites. The composites were prepared by using melt blending and injection molding methods by using three different compatibilizers at various loading levels. The characterization of composites was performed by Fourier transform infrared spectroscopy, tensile test, dynamic mechanical analysis, differential scanning thermometer, thermogravimetric analysis and scanning electron microscope. According to tensile test results, the highest increment in tensile strength and strain at break values of composites was observed with the addition of Joncryl. According to scanning electron microscope and dynamic mechanical analysis results, the best interfacial adhesion between carbon fiber and poly(phenylene sulfide) was obtained by using Joncryl as the compatibilizer.

中文翻译:

用各种增容剂制备的碳纤维增强聚苯硫醚复合材料的表征

本研究的目的是研究不同增容剂对聚酰胺尺寸碳纤维增强聚苯硫醚复合材料性能的影响。复合材料是通过使用熔融共混和注射成型方法制备的,使用三种不同的增容剂在不同的负载水平。通过傅里叶变换红外光谱、拉伸试验、动态力学分析、差示扫描温度计、热重分析和扫描电子显微镜对复合材料进行表征。拉伸试验结果表明,加入 Joncryl 后,复合材料的拉伸强度和断裂应变值增量最大。根据扫描电镜和动态力学分析结果,