Synthesis and optical properties of a new double-perovskite Rb2KInF6:Mn4+ red phosphor used for blue LED pumped white lighting
Optical Materials ( IF 3.8 ) Pub Date : 2022-04-12 , DOI: 10.1016/j.optmat.2022.112307
Yong Liu 1 , Anqi Huang 1 , Shengchun Yang 1 , Zhenjuan Duan 1 , Zhengui Li 1 , Zongtao Li 1 , Hai Lan 1 , Anzhong Peng 1 , Xiaodong Wen 1 , Zhengliang Wang 2
Affiliation  

High-efficiency narrow-band red phosphor plays a profound part in stimulating illumination quality for white light-emitting diodes (WLEDs). In this work, a series of novel double-perovskite Rb2KInF6:Mn4+ red phosphors was successfully prepared by using a facile co-precipitation technique. The crystallization, particle morphology, photoluminescence properties, and thermal quench behavior of the as-synthesized powder samples were investigated systematically. During the illumination with blue (λmax = 468 nm) and ultraviolet light (λmax = 370 nm), the prepared Rb2KInF6:Mn4+ phosphors emited a series of narrowband red signals in the range 590–660 nm with strong zero-phonon line (ZPL) emission. Meanwhile, the optimum Mn4+ concentration of at the 2Eg4A2g transitions was also studied. Moreover, the fluorescence decay lifetimes of the prepared Rb2KInF6:Mn4+ products were milliseconds. Finally, by coating Rb2KInF6:Mn4+ with commercially yellow Y3Al5O12:Ce3+ (YAG:Ce3+) phosphors on the commercially available InGaN blue chip, the intense warm white light with suitable correlated color temperature (CCT, 3491 K) and high color-rendering index (Ra, 85.1) can be manufactured at a driving current of 20 mA. All of these consequences point out that the novel double-perovskite red-emitting Rb2KInF6:Mn4+ phosphors are promising in the perspective of WLEDs applications.



中文翻译:

用于蓝色 LED 泵浦白光照明的新型双钙钛矿 Rb2KInF6:Mn4+ 红色荧光粉的合成及光学性能

高效窄带红色荧光粉在提高白光发光二极管 (WLED) 的照明质量方面发挥着重要作用。在这项工作中,采用简便的共沉淀技术成功制备了一系列新型双钙钛矿 Rb 2 KInF 6 :Mn 4+红色荧光粉。系统地研究了合成后的粉末样品的结晶、颗粒形态、光致发光性质和热猝灭行为。在蓝光(λ max  = 468 nm)和紫外光(λ max  = 370 nm)的照射下,制备的Rb 2 KInF 6 :Mn 4+荧光粉在 590-660 nm 范围内发射一系列窄带红色信号,具有强零声子线 (ZPL) 发射。同时,还研究了2 E g4 A 2g转变时的最佳Mn 4+浓度。此外,制备的Rb 2 KInF 6 :Mn 4+产物的荧光衰减寿命为毫秒。最后,通过用商业黄色 Y 3 Al 5 O 12 :Ce 3+ (YAG:Ce 3+ ) 涂覆 Rb 2 KInF 6 :Mn 4+) 荧光粉在市售的 InGaN 蓝芯片上,可以在 20 mA 的驱动电流下制造出具有合适相关色温(CCT,3491 K)和高显色指数(Ra,85.1)强暖白光所有这些结果表明,新型双钙钛矿红光 Rb 2 KInF 6 :Mn 4+荧光粉在 WLED 应用方面很有前景。