Processes in Ceramic Material, Based on Raw Materials with Heightened Fe2O3 Content, at Temperatures 950 – 1050°C
Glass and Ceramics ( IF 0.6 ) Pub Date : 2021-09-20 , DOI: 10.1007/s10717-021-00380-2
A. K. Kairakbaev 1 , V. Z. Abdrakhimov 2 , E. S. Abdrakhimova 3
Affiliation  

M125-make ceramic brick based on low-grade clay (loess loam) was obtained using overburden pyrite copper-zinc ore at firing temperature 1000°C. Hematite, magnetite, anorthite, and glass phase appear on firing the ceramic material at temperature 950°C, cristobalite appears at 1000°C. Except for higher content of cristobalite, anorthite, and the glass phase, raising the firing temperature to 1050°C does not lead to special changes. Mullite, which imparts strength to ceramic materials, appears at firing temperature 1100°C.



中文翻译:

在 950 – 1050°C 温度下,以 Fe2O3 含量较高的原材料为基础的陶瓷材料工艺

使用上覆黄铁矿铜锌矿石在 1000°C 的烧成温度下获得基于低品位粘土(黄土壤土)的 M125 陶瓷砖。在 950°C 的温度下烧制陶瓷材料时会出现赤铁矿、磁铁矿、钙长石和玻璃相,而在 1000°C 时会出现方石英。除了方石英、钙长石和玻璃相含量较高外,将烧成温度提高到 1050°C 不会导致特殊变化。赋予陶瓷材料强度的莫来石出现在 1100°C 的烧制温度下。