Materials Chemistry and Physics ( IF 4.3 ) Pub Date : 2021-09-17 , DOI: 10.1016/j.matchemphys.2021.125251 A.A. Prokhorov 1 , R. Minikayev 2 , D.V. Savchenko 1, 3 , J. Lančok 1 , A.D. Prokhorov 4
New data about the electronic state of Tb3+ doping ions in the Tb-doped EuAl3(BO3)4 and EuGa3(BO3)4 borate single crystals have been obtained from the electron paramagnetic resonance (EPR) spectra measurements at X- and Q-band frequency range in the wide temperature interval. Prior to the EPR study, the X-ray diffraction (XRD) techniques the structural and elastic properties of Tb3+ doped EuAl3(BO3)4 and EuGa3(BO3)4 single crystals were determined at T = 300–1073 K. The following spin Hamiltonian parameters for Tb3+ ions were obtained: gz = 17.064 ± 0.019, Az = 6.231 ± 0.012 GHz, Δ = 7.333 ± 0.016 GHz in EuAl3(BO3)4:Tb crystals and gz = 17.664 ± 0.011, Az = 6.251 ± 0.012 GHz, Δ = 3.891 ± 0.035 GHz in EuGa3(BO3)4:Tb crystals. The temperature dependence of the EPR linewidth for Tb3+ ions in EuAl3(BO3)4:Tb and EuGa3(BO3)4:Tb crystals was described by an exponential law that is characteristic of the Aminov-Orbach processes. It was concluded that the Tb3+ ions substitute for the three-valence europium ones in EuGa3(BO3)4:Tb/EuAl3(BO3)4:Tb crystal lattice.
中文翻译:
铝和硼酸镓单晶掺杂Tb3+离子的结构和磁性能对比研究
已从 X 处的电子顺磁共振 (EPR) 光谱测量中获得了关于 Tb 掺杂的 EuAl 3 (BO 3 ) 4和 EuGa 3 (BO 3 ) 4硼酸盐单晶中 Tb 3+掺杂离子的电子态的新数据- 以及宽温度区间内的 Q 波段频率范围。在 EPR 研究之前,X 射线衍射 (XRD) 技术分析了 Tb 3+掺杂的 EuAl 3 (BO 3 ) 4和 EuGa 3 (BO 3 ) 4的结构和弹性特性单晶在 T = 300–1073 K 下测定。获得了以下 Tb 3+离子的自旋哈密顿参数:g z = 17.064 ± 0.019,A z = 6.231 ± 0.012 GHz,Δ = 7.333 ± 0.016 GHz (EuAl 3 BO 3 ) 4 :Tb 晶体和 g z = 17.664 ± 0.011, A z = 6.251 ± 0.012 GHz, Δ = 3.891 ± 0.035 GHz 在 EuGa 3 (BO 3 ) 4 :Tb 晶体中。的EPR线宽为Tb的温度依赖性3+离子在EuAl 3(BO 3)4 Tb和EuGa:3(BO 3) 4 :Tb 晶体由指数定律描述,这是 Aminov-Orbach 过程的特征。得出的结论是,Tb 3+离子替代了EuGa 3 (BO 3 ) 4 :Tb/EuAl 3 (BO 3 ) 4 :Tb 晶格中的三价铕离子。