Corrosion release behavior of alloy 690 and its application in high-temperature water with Zn injection
Nuclear Engineering and Technology ( IF 2.6 ) Pub Date : 2021-09-09 , DOI: 10.1016/j.net.2021.09.009
Jiapeng Liao 1 , Yousen Hu 1 , Jinggang Li 1 , Desheng Jin 1 , Shuqi Meng 1 , Tianming Ruan 1 , Yisong Hu 1 , Ziyu Zhang 2
Affiliation  

Corrosion release behavior of Alloy 690 in high-temperature water was investigated under the conditions of injected Zn concentrations of 0 ppb, 10 ppb and 50 ppb. A protective oxide film composed of Zn(FexCr1-x)2O4 and Cr2O3 was formed with Zn injection, resulting in a better corrosion resistance. In comparison with the Zn-free condition, the corrosion release rate under the Zn-injection conditions was smaller. The corrosion release inhibiting factors were 1.7 and 1.9 under the conditions of 10 ppb and 50 ppb Zn-injection respectively. A foreseen application of the corrosion and corrosion release rates has been proposed and discussed.



中文翻译:

690合金的腐蚀释放行为及其在喷锌高温水中的应用

研究了在注入锌浓度为 0 ppb、10 ppb 和 50 ppb 的条件下合金 690 在高温水中的腐蚀释放行为。Zn注入形成了由Zn(Fe x Cr 1-x ) 2 O 4和Cr 2 O 3组成的保护性氧化膜,具有更好的耐腐蚀性。与无锌条件相比,注锌条件下的腐蚀释放速率较小。在注锌量为 10 ppb 和 50 ppb 的条件下,缓蚀释放因子分别为 1.7 和 1.9。已经提出并讨论了腐蚀和腐蚀释放速率的可预见应用。