The exceptional efficiency of combining clay additives with introduction of thinning additives of a complex organomineral thinner (COMT) is observed. Values of 14 – 15% initial porosity of compacted high-alumina ceramic concrete with a compaction pressure of 30 MPa are achieved. Depending on mix composition and clay additive content with a comparable moisture content during static compaction material porosity with the addition of COMT is approximately equal to that of material without the additive under a compaction pressure, 3 – 6 times lower than that on material with additive.

中文翻译：

---

粘土和复合有机稀释剂（COMT）的组合添加在陶瓷混凝土技术中的协同效应（综述文章）

观察到将粘土添加剂与引入复杂的有机矿物稀释剂（COMT）的稀释剂结合使用的非凡效率。在压实压力为30 MPa的情况下，压实的高铝陶瓷混凝土的初始孔隙率为14 – 15％。取决于混合料的组成和粘土添加剂的含量，以及在静态压实过程中水分含量相当的情况下，添加COMT的材料孔隙率大约等于在压实压力下不含添加剂的材料的孔隙率，比含添加剂的材料的孔隙率低3-6倍。