In this study, the experimental characterization of cerium oxide (CeO₂) powders doped with Ag at various amounts of 1, 2, 3, and 4 at.% was done using X-ray diffraction (XRD), differential thermal analysis (DTA), thermogravimetric analysis (TGA), Fourier transform infrared (FTIR) spectroscopy, Raman analysis, scanning electron microscopy (SEM), energy dispersive X-ray (EDX), and vibrating sample magnetometry (VSM). The formation of the single phase of CeO₂, having the cubic crystal structure, for all samples was observed. The phase structure was not affected by the as-used Ag contents. The addition of Ag caused an increase in the lattice parameter and a decrease in the crystallinity. In addition to these, non-gradual changes in the crystallite size were observed. The thermal stability for each sample was seen for each sample until 1000 °C. The morphology composed of the microparticles was observed. The magnetization and magnetic susceptibility values were affected by the amount of Ag dopant.

在这项研究中，使用X射线衍射（XRD），差热分析（​​DTA）对掺有各种浓度分别为1，2、3和4 at。％的Ag的氧化铈（CeO ₂）粉末进行了实验表征，热重分析（TGA），傅立叶变换红外（FTIR）光谱，拉曼分析，扫描电子显微镜（SEM），能量色散X射线（EDX）和振动样品磁强（VSM）。CeO ₂单相的形成对于所有样品，均具有立方晶体结构。相结构不受所用Ag含量的影响。Ag的添加引起晶格参数的增加和结晶度的降低。除此之外，观察到微晶尺寸的非逐渐变化。在1000℃之前观察到每个样品的每个样品的热稳定性。观察到由微粒组成的形态。磁化率和磁化率值受Ag掺杂量的影响。