Influence of Thermal Treatment on Microstructure and Corrosion Behavior of Amorphous Fe 40 Ni 40 B 12 Si 8 Alloy
Metallurgical and Materials Transactions A ( IF 2.2 ) Pub Date : 2020-11-17 , DOI: 10.1007/s11661-020-06079-3
Milica M. Vasić , Tomáš Žák , Naděžda Pizúrová , Ivana Stojković Simatović , Dragica M. Minić

Microstructural evolution of thermally treated melt-quenched amorphous Fe40Ni40B12Si8 alloy was studied in terms of its influence on corrosion behavior of the alloy. Alloy structure was transformed gradually from purely amorphous and chemically homogeneous to fully crystalline, yielding γ-(Fe,Ni), Ni31Si12 and (Fe,Ni)2B phases as the final products. Corrosion study of the alloy in amorphous, partially crystalline as well as fully crystalline form, performed by electrochemical measurements in 0.5 M NaCl, together with the morphology examination, revealed that the microstructure and phase composition are crucial factors determining the corrosion resistance of the alloy in corrosive environment.



中文翻译:

热处理对非晶态Fe 40 Ni 40 B 12 Si 8合金的组织和腐蚀行为的影响

研究了热处理后的非晶态Fe 40 Ni 40 B 12 Si 8非晶态合金的微观组织演变对合金腐蚀行为的影响。合金结构逐渐从纯非晶态和化学均质转变为完全结晶,产生γ-(Fe,Ni),Ni 31 Si 12和(Fe,Ni)2B阶段作为最终产品。通过在0.5 M NaCl中进行电化学测量,对非晶态,部分晶态和全晶态的合金进行腐蚀研究,并进行形态学检查,结果表明,显微组织和相组成是决定合金耐腐蚀性能的关键因素。腐蚀性环境。