International Journal of Metalcasting ( IF 2.6 ) Pub Date : 2020-11-21 , DOI: 10.1007/s40962-020-00540-0 M. F. Moreira , L. B. Fantin , F. Beneduce Neto , C. R. F. Azevedo
Inconel 713C as-cast test pieces were produced by investment casting. The tensile properties at 25 and 650 °C were obtained along with microstructural and microfractographic characterization. The tensile testing results followed the requirements of the AMS 5391D standard. Additionally, stress-rupture testing at 982 °C and 152 MPa, and 815 °C and 305 MPa was carried. The aged γ − γ′ microstructures were compared and discussed in terms of rafting kinetics. The stress-rupture results followed the AMS 5391D requirements. The relationship between the as-cast and aged microstructures and the mechanical properties was discussed.