Preparation and Properties of RDX/Aluminum Composites by Spray-Drying Method
Journal of Nanomaterials Pub Date : 2020-11-04 , DOI: 10.1155/2020/1083267
Hongyan Sun 1 , Xiaodong Li 1 , Pengfei Wu 1 , Changgui Song 1 , Yue Yang 1
Affiliation  

RDX/aluminum composites were prepared by the spray-drying method with F2602 as a binder. The morphology and covering effect of composites were characterized by scanning electron microscopy (SEM) and X-ray photoelectron spectroscopy (XPS). The effect of the processing parameters on the morphology of the samples was investigated. The impact sensitivity and thermal decomposition behavior of RDX/aluminum composites were also measured and analyzed. Optimal morphology of samples was achieved when the inlet temperature, nitrogen flow rate, and suspension feed flow rates were 80°C, 473 L·h-1, and 4.5 mL·min-1, respectively. In addition, RDX/aluminum composites with the same content were prepared by a coverage-mixing method for comparative analysis. Experimental results showed that the thermal sensitivity and the impact sensitivity of RDX/aluminum composites prepared by the spray-drying method were significantly lower than those of RDX/aluminum composites prepared by the coverage-mixing method.

中文翻译:

喷雾干燥法制备RDX /铝复合材料的性能

用F 2602作为粘合剂通过喷雾干燥法制备RDX /铝复合材料。通过扫描电子显微镜(SEM)和X射线光电子能谱(XPS)表征了复合材料的形貌和覆盖效果。研究了加工参数对样品形态的影响。还测量和分析了RDX /铝复合材料的冲击敏感性和热分解行为。当入口温度,氮气流速和悬浮液进料流速分别为80°C,473 L·h -1和4.5 mL·min -1时,样品的形态最佳。, 分别。另外,通过覆盖混合法制备具有相同含量的RDX /铝复合材料以进行比较分析。实验结果表明,喷雾干燥法制备的RDX /铝复合材料的热敏性和冲击敏感性明显低于覆盖-混合法制备的RDX /铝复合材料的热敏性和冲击敏感性。