Phase transformation and magnetic properties of fully dense Sm(Fe0.8Co0.2)11Ti bulk magnets
Scripta Materialia ( IF 5.3 ) Pub Date : 2021-03-01 , DOI: 10.1016/j.scriptamat.2020.10.030 Hui-Dong Qian , Jung Tae Lim , Jong-Woo Kim , Yang Yang , Kyung Mox Cho , Jihoon Park , Chul-Jin Choi
Scripta Materialia ( IF 5.3 ) Pub Date : 2021-03-01 , DOI: 10.1016/j.scriptamat.2020.10.030 Hui-Dong Qian , Jung Tae Lim , Jong-Woo Kim , Yang Yang , Kyung Mox Cho , Jihoon Park , Chul-Jin Choi
Abstract High density sintered Sm(Fe0.8Co0.2)11Ti bulk magnets were successfully produced using a newly developed high pressure pressing fabrication method. The purity of the hard magnetic ThMn12 phase in the bulk magnet reached to higher than 97 wt.%. The phase transformation behavior from amorphous to ThMn12 phase during heat treatment was systematically investigated by transmission electron microscopy. The remanent magnetization and maximum energy product of a bulk magnet were 96.0 emu/g and 12.22 MGOe, respectively. To the best of our knowledge, the achieved maximum energy product is the highest among all the SmFe12-based bulk magnets reported.
中文翻译:
全致密Sm(Fe0.8Co0.2)11Ti块状磁铁的相变和磁性能
摘要 采用新开发的高压压制制造方法成功制备了高密度烧结Sm(Fe0.8Co0.2)11Ti块状磁铁。块状磁铁中硬磁 ThMn12 相的纯度达到 97% 以上。通过透射电子显微镜系统地研究了热处理过程中从非晶态到 ThMn12 相的相变行为。块状磁铁的剩磁和最大能积分别为 96.0 emu/g 和 12.22 MGOe。据我们所知,达到的最大能量积是所有 SmFe12 基块状磁铁中最高的。