纳米级固体超酸偶联的聚苯并咪唑膜对流动电池具有高离子选择性,ACS Sustainable Chemistry & Engineering

当前位置： X-MOL 学术 › ACS Sustain. Chem. Eng. › 论文详情

Our official English website, www.x-mol.net, welcomes your feedback! (Note: you will need to create a separate account there.)

纳米级固体超酸偶联的聚苯并咪唑膜对流动电池具有高离子选择性
ACS Sustainable Chemistry & Engineering ( IF 7.1 ) Pub Date : 2020-10-26 , DOI: 10.1021/acssuschemeng.0c05359
Lei Hu _{1,

2} , Yue Du _{1,

3} , Li Gao ₁ , Mengting Di ₁ , Ning Zhang _{1,

2} , Yu Pan _{1,

2} , Xiaoming Yan _{1,

2,

4} , Baigang An ₃ , Gaohong He _{1,

2,

4}

Affiliation

将纳米级固体超强酸SO ₄^2- / ZrO ₂ / WO ₃偶联到咪唑-羟基-季铵共官能化聚苯并咪唑（PG112）中，以解决膜在大规模液流电池应用中的权衡效果。具有高磺酸基的纳米级SO ₄^2- / ZrO ₂ / WO ₃颗粒作为氧化还原活性离子屏障和质子载体分散在膜中，从而减轻了电解质的渗透并保持了高离子电导率。制备的膜的VO ²⁺渗透性（7.86×10 ^–10 cm ² s ^–1）显着低于PG112（3.93×10 ^–9 cm ² s ^–1）和Nafion 212（7.76×10 ^–8 cm ² s ^–1）膜。与Nafion 212（35 h）和PG112（88 h）膜相比，带有该膜的钒液流电池具有更长的自放电持续时间231 h。40–120 mA cm ^–2时的高库仑效率为97.5–99.2％制备的膜的N-离子比Nafion 212（78.0-92.8％）和PG112膜（96.2-98.6％）更高。还观察到稳定的循环性能和低的保留容量，表明所制备的膜在钒液流电池操作中具有优异的化学稳定性。这项工作为提高液流电池的性能提供了一种可应用的前瞻性膜。

"点击查看英文标题和摘要"

Nanoscale Solid Superacid-Coupled Polybenzimidazole Membrane with High Ion Selectivity for Flow Batteries

Nanoscale solid superacid SO₄^2–/ZrO₂/WO₃ is coupled into imidazole-hydroxyl-quaternary ammonium co-functionalized polybenzimidazole (PG112) to address the trade-off effect of membrane for large-scale flow battery application. Nanoscale SO₄^2–/ZrO₂/WO₃ particles with high sulfonic groups are dispersed in membrane as redox-active ion barriers and proton carriers, which mitigate the electrolyte crossover and maintain high ion conductivity. The VO²⁺ permeability of the prepared membrane (7.86 × 10^–10 cm² s^–1) is significantly lower than those of PG112 (3.93 × 10^–9 cm² s^–1) and Nafion 212 (7.76 × 10^–8 cm² s^–1) membranes. The vanadium flow battery with this membrane exhibits a longer self-discharge duration time of 231 h compared with Nafion 212 (35 h) and PG112 (88 h) membranes. High coulombic efficiencies of 97.5–99.2% at 40–120 mA cm^–2 are obtained for the prepared membrane, which are higher than those for Nafion 212 (78.0–92.8%) and PG112 membranes (96.2–98.6%). Stable cycle performance and low retention capacity are also observed, suggesting the excellent chemical stability of the prepared membrane in vanadium flow battery operation. This work provides a prospective and applicable membrane to enhance the performance of flow battery.