Abstract Ordinary recycled soda lime glass powder was densified via cold sintering process with the aid of concentrated NaOH solution. Increase in processing time, temperature and concentration of the NaOH solution resulted in the formation of monolithic glass artifacts with higher relative densities. The sample densified the most (95.2%) was obtained when the sintering was performed at 250˚C with a 20 min dwell time using 15 M NaOH solution.

中文翻译：

---

钠钙玻璃的冷烧结

摘要 普通再生钠钙玻璃粉在浓NaOH溶液的辅助下，通过冷烧结工艺致密化。NaOH 溶液处理时间、温度和浓度的增加导致形成具有更高相对密度的整体玻璃制品。当使用 15 M NaOH 溶液在 250°C 下进行烧结并保持 20 分钟时，样品的致密化程度最高 (95.2%)。