Pulsed-field magnetisation of Y-Ba-Cu-O bulk superconductors fabricated by the infiltration growth technique
Superconductor Science and Technology ( IF 3.7 ) Pub Date : 2020-10-01 , DOI: 10.1088/1361-6668/abb590
Devendra K Namburi 1 , K Takahashi 2 , T Hirano 2 , T Kamada 2 , H Fujishiro 2 , Y-H Shi 1 , D A Cardwell 1 , J H Durrell 1 , M D Ainslie 1
Affiliation  

Raw data obtained from the experiments carried out, are analysed and used for preparing some of the figures in the present manuscript are provided here. The data sets are provided in excel files, corresponding to respective figures. The files 'For figure-2(a)' and 'For figure-2(b)' contains columns with labels as trapped field magnitude, positions of X, and Y. These data are used to construct the 3-axis trapped field profiles as shown in Figures-2(a) and 2(b) in the paper. The files 'For Figure-3(b)' and 'For Figure-3(c), contains the columns indicating the magnetic field H (in the units of Oe) and Jc at respective temperatures of 85 K, 77 K, 65 K, 50 K, and 30 K as appropriate are provided in respective columns with columns as H and Jc at 85 K, for instance. These data are used for making X-Y plots representing the performance of 1-step BA-TSIG YBCO and 2-step BA-TSIG YBCO samples, as shown in figures 3(b) and 3(c). The file 'For figure-4(b)' contains columns with Temperature and Normalised magnetization data obtained from specimens extracted from different locations in the sample i.e. 1tb, 1td, 1tf, 1th, and 1tj. Details of these positions are indicated in figure-4(a) of the manuscript. The file 'For Figure-4(c)' contains data of applied field H (in Oe) and current density Jc (in A/cm2) for three different positions: 1td, 3td, and 5td i.e. along the a-growth region of the 2-step BA-TSIG YBCO sample. These data are plotted together to obtain figure-4(c). The file 'For Figure-4(d)' contains data of applied field H (in Oe) and current density Jc (in A/cm2) for five different positions: 1tb, 1td, 1tf, 1th, and 1tj i.e. along the c-growth region of the 2-step BA-TSIG YBCO sample. These data are plotted together to obtain figure-4(d).

中文翻译:

通过渗透生长技术制造的 Y-Ba-Cu-O 块状超导体的脉冲场磁化

从进行的实验中获得的原始数据进行了分析,并用于准备本手稿中的一些数字,此处提供。数据集在excel文件中提供,对应于各自的数字。文件“对于图 2(a)”和“对于图 2(b)”包含标签为俘获场幅度、X 和 Y 位置的列。这些数据用于构建 3 轴俘获场剖面如论文中的图 2(a) 和 2(b) 所示。文件“对于图 3(b)”和“对于图 3(c)”包含指示磁场 H(以 Oe 为单位)和 Jc 在各自温度 85 K、77 K、65 K 下的列例如,在相应的列中提供适当的 、50 K 和 30 K,其中列如 H 和 Jc 在 85 K。这些数据用于制作代表 1 步 BA-TSIG YBCO 和 2 步 BA-TSIG YBCO 样品性能的 XY 图,如图 3(b) 和 3(c) 所示。文件“对于图 4(b)”包含从样本中不同位置(即 1tb、1td、1tf、1th 和 1tj)提取的样本获得的温度和归一化磁化数据的列。这些职位的详细信息显示在手稿的图 4(a) 中。文件“对于图 4(c)”包含三个不同位置的外加场 H(以 Oe 为单位)和电流密度 Jc(以 A/cm2 为单位)的数据:1td、3td 和 5td,即沿 a-growth 区域两步 BA-TSIG YBCO 样本。将这些数据绘制在一起以获得图 4(c)。文件“对于图 4(d)” 包含五个不同位置的外加场 H(以 Oe 为单位)和电流密度 Jc(以 A/cm2 为单位)的数据:1tb、1td、1tf、1th 和 1tj,即沿 2 步 BA-TSIG 的 c-growth 区域YBCO 样品。将这些数据绘制在一起以获得图 4(d)。