Mo 5 SiB 2 -Based Ceramics by Forced SHS Compaction and Hot Pressing of SHS-Produced Powders: Features of Phase-Formation Processes
International Journal of Self-Propagating High-Temperature Synthesis ( IF 0.5 ) Pub Date : 2020-10-02 , DOI: 10.3103/s1061386220030073
A. Yu. Potanin , Yu. S. Pogozhev , S. I. Rupasov , A. V. Novikov , D. Yu. Kovalev

Abstract—

Mo5SiB2-based ceramics were fabricated from elemental powders by forced SHS compaction and hot pressing of SHS-produced powders and specific features of product patterning were characterized by XRD, time-resolved XRD, SEM/EDS, and TEM/EDS. Best results were obtained upon hot pressing of SHS-produced Mo–Si–B powders: resultant material was single-phased Mo5SiB2 with a mean grain size of 2–10 μm.