Combustion Behavior of the Inorganic Nitrates‐Based Compositions Part I
Propellants, Explosives, Pyrotechnics ( IF 1.7 ) Pub Date : 2020-07-16 , DOI: 10.1002/prep.202000053 Anatoly P. Denisyuk 1 , Nguyen Duy Tuan 1 , Vladimir A. Sizov 1
Propellants, Explosives, Pyrotechnics ( IF 1.7 ) Pub Date : 2020-07-16 , DOI: 10.1002/prep.202000053 Anatoly P. Denisyuk 1 , Nguyen Duy Tuan 1 , Vladimir A. Sizov 1
Affiliation
|
Combustion behavior of inorganic nitrates (KNO3, NaNO3, CsNO3, Ba(NO3)2, Sr(NO3)2, Pb(NO3)2, and NH4NO3) based energetic materials in wide range of pressure (0.1–18 MPa) was studied. Samples have the same binder and differ in combustion temperature due to a change of oxidizer excess ratio (α). It is shown that compositions differ in the burning rate, in its dependence on pressure. The extreme dependence of burning rate on α is established. The combustion temperature of the samples was experimentally determined.
中文翻译：
基于无机硝酸盐的组合物的燃烧行为
无机硝酸盐（KNO 3，NaNO 3，CsNO 3，Ba（NO 3）2，Sr（NO 3）2，Pb（NO 3）2和NH 4 NO 3）含能材料在较大压力范围内的燃烧行为（0.1-18 MPa）进行了研究。样品具有相同的粘合剂，并且由于氧化剂过量比（α）的变化而导致燃烧温度不同。结果表明，组成对燃烧速度的影响取决于压力。建立了燃烧速率对α的极端依赖性。通过实验确定样品的燃烧温度。