Abstract In metal‒rich borides, numerous boron fragments Bn (n = 2, 3, 4, 5, 6) have been discovered, the B4 units being the most versatile with four different shapes (bent, zigzag, trigonal planar and tetrahedral). We report on the new boride series Ti2-xM1+x–δIr3+δB3 (x = 0.5 for M = V–Mn, x = 0 for M = Mn–Ni and δ 6 ‾ 2m, no. 189) to the Ti1+xRh2‒x+yIr3‒yB3‒type (Pbam, no. 55) leads to a change of B4 shape from trigonal planar B4 (M = V–Mn) to zigzag B4 fragment (M = Mn–Ni). Even though there is no group‒subgroup relationship between the two structures, we present how the Ti1+xOs2‒xRuB2‒type structure can easily be geometrically derived from the Ti1+xRh2-x+yIr3-yB3‒type.

中文翻译：

---

在新硼化物系列 Ti2–xM1+x–δIr3+δB3 中将三角形平面 B4 转变为锯齿形 B4 单元（对于 M = V–Mn，x = 0.5，对于 M = Mn–Ni 和 x = 0，δ < 0.2）

摘要 在富金属硼化物中，发现了大量硼碎片 Bn (n = 2, 3, 4, 5, 6)，其中 B4 单元最为通用，具有四种不同的形状（弯曲、锯齿形、三角平面和四面体）。我们向 Ti1+ 报告了新的硼化物系列 Ti2-xM1+x–δIr3+δB3（对于 M = V–Mn，x = 0.5，对于 M = Mn–Ni，x = 0 和 δ 6 ‾ 2m，编号 189） xRh2-x+yIr3-yB3-type (Pbam, no. 55) 导致 B4 形状从三角形平面 B4 (M = V-Mn) 变为锯齿形 B4 片段 (M = Mn-Ni)。尽管这两种结构之间没有群-亚群关系，但我们展示了如何从 Ti1+xRh2-x+yIr3-yB3-型轻松地从几何上推导出 Ti1+xOs2-xRuB2-型结构。