Progress in Rubber, Plastics and Recycling Technology ( IF 1.1 ) Pub Date : 2019-12-26 , DOI: 10.1177/1477760619895015 Soumya Ghosh Chowdhury 1 , Koushik Pal 1 , Hirak Satpathi 1 , Abhijit Bandyopadhyay 2 , Rabindra Mukhopadhyay 1 , Sanjay K. Bhattacharyya 1
Potential of Sumilink-200 was investigated in a typical natural rubber-based tread compound in connection with its ability to act as a coupling agent for carbon black to reduce hysteresis loss of the compound. Optimum physical properties were obtained at 2 phr loading of Sumilink-200. At this loading, tensile modulus at 300% elongation improved by 9.6% with a reduction in visco-elastic energy dissipation (loss tangent) at 60°C by 8.3% over the control compound. The abrasion resistance properties of the compounds found to remain unaffected with the introduction of Sumilink-200.