In vitro degradation and apatite formation of magnesium and zinc incorporated calcium silicate prepared by sol-gel method
Materials Technology ( IF 2.9 ) Pub Date : 2020-05-13 , DOI: 10.1080/10667857.2020.1762352 J. Ma 1, 2, 3 , C. Z. Wang 1 , B. X. Huang 1 , X. C. Zhao 1 , C. Z. Chen 2, 3 , H. J. Yu 3, 4
Materials Technology ( IF 2.9 ) Pub Date : 2020-05-13 , DOI: 10.1080/10667857.2020.1762352 J. Ma 1, 2, 3 , C. Z. Wang 1 , B. X. Huang 1 , X. C. Zhao 1 , C. Z. Chen 2, 3 , H. J. Yu 3, 4
Affiliation
The high degradation rate limits the clinical applications of calcium silicate bioceramics. In this paper, Ca2MgSi2O7 and Ca2ZnSi2O7 were successfully prepared using sol-gel method by incorporating...
中文翻译:
溶胶-凝胶法制备的掺镁锌硅酸钙体外降解及磷灰石形成
高降解率限制了硅酸钙生物陶瓷的临床应用。本文采用溶胶-凝胶法成功制备了Ca2MgSi2O7和Ca2ZnSi2O7。...
更新日期:2020-05-13
中文翻译:
溶胶-凝胶法制备的掺镁锌硅酸钙体外降解及磷灰石形成
高降解率限制了硅酸钙生物陶瓷的临床应用。本文采用溶胶-凝胶法成功制备了Ca2MgSi2O7和Ca2ZnSi2O7。...