Interrelation of the Phase and Chemical Compositions with the Longevity of the Ceramic Material of the > 600 yr Old Barcelona Catholic Cathedral
Glass and Ceramics ( IF 0.6 ) Pub Date : 2020-05-25 , DOI: 10.1007/s10717-020-00232-5
E. S. Abdrakhimova , V. Z. Abdrakhimov

The elemental chemical composition showed a heightened weight content of calcium (Ca = 5.9%) in the samples, which promotes formation of anorthite, which increases the strength of articles, and a heightened weight content of carbon (C = 14.79%) attests the introduction of fuel into the green part body. The heightened weight content of fuel in the green body promotes uniform sintering of the ceramic inside the sample. A heightened weight content of iron (Fe = 2.98%) and alkali (R2O = Na2O + K2O = 2.57%) in the sample will promote formation of a liquid phase at 950°C. X-ray phase analysis was confirmed by elemental analysis indicating that the heightened calcium content promotes the formation of anorthite.

中文翻译:

相和化学成分与> 600年古巴塞罗那天主教大教堂陶瓷材料的寿命之间的相互关系

元素化学成分显示样品中钙的重量含量增加(Ca = 5.9%),这促进了钙长石的形成,增加了制品的强度,碳的重量含量增加(C = 14.79%)证明了引入燃料注入绿色零件主体。生坯中燃料重量的增加会促进样品内部陶瓷的均匀烧结。样品中铁(Fe = 2.98%)和碱(R 2 O = Na 2 O + K 2 O = 2.57%)的重量含量增加将促进在950°C形成液相。通过元素分析证实了X射线相分析,表明钙含量的增加促进了钙长石的形成。