Remarkable isosteric heat of hydrogen adsorption on Cu(I)-exchanged SSZ-39
International Journal of Hydrogen Energy ( IF 8.1 ) Pub Date : 2020-04-03 , DOI: 10.1016/j.ijhydene.2020.03.083
Bahar Ipek , Ismihan Altiparmak

Hydrogen storage capacity on Cu(I)-exchanged SSZ-39 (AEI), -SSZ-13 (CHA) and Ultra stable-Y (US–Y, FAU) at temperatures between 279 K and 304 K are investigated. The gravimetric hydrogen storage capacity values reaching 83 μmol H g (at 279 K and 1 bar) are found to be comparable with the highest adsorption capacity values reported on metal-organic frameworks. The volumetric hydrogen storage capacity values; on the other hand, are found to be more than three times of those reported on metal-organic frameworks (0.57 g/L on Cu(I)-SSZ-39 at 1 bar and 296 K vs. ca. 0.18 g/L on Co(-dobdc) at 1 bar and 298 K (Kapelewski MT, Runčevski T, Tarver JD, Jiang HZH, Hurst KE, Parilla PA et al. Record High Hydrogen Storage Capacity in the Metal-Organic Framework Ni(-dobdc) at Near-Ambient Temperatures. Chem Mater 2018; 30:8179–89)). The isosteric heat of adsorption values are calculated to be between 80 kJ mol and 49 kJ mol on Cu(I)-SSZ-39 and between 22 kJ mol and 15 kJ mol on Cu(I)-US-Y indicating H adsorption mainly at Cu(I) cations located at the eight-membered rings on Cu(I)-SSZ-39 and at six-membered rings on Cu(I)-US-Y. Hydrogen adsorption experiments performed at 77 K showed higher adsorption capacity values for Cu(I)-SSZ-39 at 1 bar, but Cu(I)-US-Y showed potential for hydrogen storage at higher pressure values.

中文翻译:


Cu(I) 交换的 SSZ-39 具有显着的氢吸附等量热



研究了 Cu(I) 交换的 SSZ-39 (AEI)、-SSZ-13 (CHA) 和超稳定-Y (US-Y、FAU) 在 279 K 至 304 K 温度之间的储氢能力。重量储氢容量值达到 83 μmol H g(在 279 K 和 1 bar 下),与金属有机框架报道的最高吸附容量值相当。体积储氢容量值;另一方面,发现是金属有机框架报道的三倍多(Cu(I)-SSZ-39 在 1 bar 和 296 K 下为 0.57 g/L,而在 Cu(I)-SSZ-39 上为 0.18 g/L Co(-dobdc) 在 1 bar 和 298 K 下(Kapelewski MT、Runčevski T、Tarver JD、Jiang HZH、Hurst KE、Parilla PA 等人。在接近金属有机框架 Ni(-dobdc) 中记录高储氢容量- 环境温度。2018 年;30:8179–89))。 Cu(I)-SSZ-39 上的等量吸附热值计算在 80 kJ mol 和 49 kJ mol 之间,Cu(I)-US-Y 上的等量吸附热值在 22 kJ mol 和 15 kJ mol 之间,表明 H 吸附主要在Cu(I) 阳离子位于 Cu(I)-SSZ-39 上的八元环和 Cu(I)-US-Y 上的六元环上。在 77 K 下进行的氢吸附实验显示,Cu(I)-SSZ-39 在 1 bar 下具有较高的吸附容量值,但 Cu(I)-US-Y 在较高压力值下显示出储氢潜力。