Abstract This research aimed to prepare smart cotton fabrics with multi functions for antibacterial activity, UV protection and electrical conductivity via in situ coating with conductive polymer and conductive hydrogel. Therefore, 3-(furan-2-carboamido) propionic acid was synthesized followed by polymerization using ceric ammonium nitrate. In addition, cotton fabrics coated with 3-(furan-2-carboamido) propionic acid via in situ polymerization and by the hydrogel that based on poly (3-(furan-2-carboamido) propionic acid) and gelatin which have been performed via in situ gelation process. The chemical structure and morphology of the 3-(furan-2-carboamido) propionic acid (monomer) and the synthesized polymer (PFu) were investigated by H1NMR, IR, SEM, TGA and DSC. Where, the treated fabrics (PFu-T and PFu-G-T) are characterized by SEM, FTIR and contact angle. Furthermore, the AC electrical conductivity and dielectric properties of PFu, PFu-T, PFu-G-T and blank were investigated over the frequency range of 20 Hz–10 MHz at room temperature using impedance spectroscopy where the electric conductivity values are 1.74 × 10-5, 7.5 × 10-8, 4 × 10-7, 8.24 × 10-11 (S·cm)-1, respectively. In addition, the anti-bacterial activity of PFu-T, PFu-G-T and blank was assessed versus gram-positive and gram-negative bacteria where, PFu-G-T shows activity against Escherichia coli and Staphylococcus aureus. Moreover, PFu-T, PFu-G-T showed high UV protection especially for PFu-G-T.

中文翻译：

---

含有聚（3-（呋喃-2-碳酰氨基）丙酸）和聚（3-（呋喃-2-碳酰氨基）丙酸）/明胶水凝胶的改性棉织物，具有紫外线防护、抗菌和电气特性

摘要 本研究旨在通过原位涂覆导电聚合物和导电水凝胶制备具有抗菌活性、紫外线防护和导电性的多功能智能棉织物。因此，合成了 3-(furan-2-carboamido) 丙酸，然后使用硝酸铈铵进行聚合。此外，通过原位聚合和基于聚（3-（呋喃-2-碳酰氨基）丙酸）和明胶的水凝胶涂覆了 3-（呋喃-2-碳酰氨基）丙酸的棉织物已经通过原位凝胶化过程。通过H1NMR、IR、SEM、TGA和DSC研究了3-(呋喃-2-碳酰氨基)丙酸(单体)和合成聚合物(PFu)的化学结构和形态。其中，处理后的织物（PFu-T 和 PFu-GT）通过 SEM 表征，FTIR 和接触角。此外，使用阻抗谱研究了 PFu、PFu-T、PFu-GT 和空白在室温下 20 Hz–10 MHz 频率范围内的交流电导率和介电性能，其中电导率值为 1.74 × 10-5 , 7.5 × 10-8, 4 × 10-7, 8.24 × 10-11 (S·cm)-1。此外，PFu-T、PFu-GT 和空白对革兰氏阳性和革兰氏阴性细菌的抗菌活性进行了评估，其中 PFu-GT 显示出抗大肠杆菌和金黄色葡萄球菌的活性。此外，PFu-T、PFu-GT 尤其对 PFu-GT 显示出高紫外线防护。在室温下使用阻抗谱在 20 Hz–10 MHz 的频率范围内研究 PFu-GT 和空白，其中电导率值为 1.74 × 10-5、7.5 × 10-8、4 × 10-7、8.24 × 10分别为-11 (S·cm)-1。此外，PFu-T、PFu-GT 和空白对革兰氏阳性和革兰氏阴性细菌的抗菌活性进行了评估，其中 PFu-GT 显示出抗大肠杆菌和金黄色葡萄球菌的活性。此外，PFu-T、PFu-GT 尤其对 PFu-GT 显示出高紫外线防护。在室温下使用阻抗谱在 20 Hz–10 MHz 的频率范围内研究 PFu-GT 和空白，其中电导率值为 1.74 × 10-5、7.5 × 10-8、4 × 10-7、8.24 × 10分别为-11 (S·cm)-1。此外，PFu-T、PFu-GT 和空白对革兰氏阳性和革兰氏阴性细菌的抗菌活性进行了评估，其中 PFu-GT 显示出抗大肠杆菌和金黄色葡萄球菌的活性。此外，PFu-T、PFu-GT 尤其对 PFu-GT 显示出高紫外线防护。