Ultrahigh damping capacity achieved by modulating R phase in Ti49.2Ni50.8 shape memory alloy wires
Scripta Materialia ( IF 5.3 ) Pub Date : 2020-07-01 , DOI: 10.1016/j.scriptamat.2020.03.017 Mingjiang Jin , Yuanwei Song , Xiaodong Wang , Peng Chen , Guobo Pang , Xuejun Jin
Scripta Materialia ( IF 5.3 ) Pub Date : 2020-07-01 , DOI: 10.1016/j.scriptamat.2020.03.017 Mingjiang Jin , Yuanwei Song , Xiaodong Wang , Peng Chen , Guobo Pang , Xuejun Jin
Abstract An ultrahigh damping capacity with internal friction close to 0.35 was detected over a large temperature range of 75 °C (from -40 to 35 °C) in Ti49.2Ni50.8 shape memory wires by adjusting the B2→R phase transformation through a low-temperature aging treatment. Microstructural analysis showed that the excellent damping performance is attributed to high-density nanodomains in the R phase, which are induced by short-range Ni segregation. These results are expected to further expand capacity for designing damping microstructure.
中文翻译:
通过调制 Ti49.2Ni50.8 形状记忆合金线材中的 R 相实现超高阻尼能力
摘要 通过调节 B2→R 相变,在 Ti49.2Ni50.8 形状记忆丝中在 75 °C(-40 至 35 °C)的大温度范围内检测到内摩擦接近 0.35 的超高阻尼能力。低温时效处理。微观结构分析表明,优异的阻尼性能归因于 R 相中的高密度纳米域,这是由短程 Ni 偏析引起的。这些结果有望进一步扩大设计阻尼微结构的能力。