In this paper, 3D warp-knitted camouflage fabrics were fabricated with two kinds of bottom structure. Polyester and coating treated PE flat wire were used as raw materials. The samples were manufactured by the RD6N warp-knitting machine. The properties of camouflage fabrics were tested and analyzed. Results show that the lowest reflection loss of 2 cm height of 3D warp-knitted camouflage fabrics with mesh was -38.49 dB at 15.45 GHz. And the 3D warp-knitted camouflage fabric has excellent absorption performance, tensile breaking strength and flame retardant property. The findings have theoretical and practical significance for the applications of 3D warp-knitted camouflage fabrics.

在本文中，制造了具有两种底部结构的3D经编迷彩织物。聚酯和经过涂层处理的PE扁线被用作原材料。样品由RD6N经编机制造。对伪装织物的性能进行了测试和分析。结果表明，在15.45 GHz下，具有网眼的3D经编迷彩织物的2 cm高度的最低反射损失为-38.49 dB。3D经编迷彩面料具有出色的吸收性能，拉伸断裂强度和阻燃性能。该发现对于3D经编迷彩织物的应用具有理论和实践意义。