Phase transition, dielectric switching property of an in (III)-Based organic-inorganic hybrid compound: (C5H16N2)InBr5
Journal of Solid State Chemistry ( IF 3.2 ) Pub Date : 2020-03-22 , DOI: 10.1016/j.jssc.2020.121329
Min Li , Guan-Cheng Xu , Yin-Qiang Zhang , Wen-Bo Xin

An indium-based organic-inorganic phase transition material (C5H16N2)InBr5 (1) was synthesized by the reaction of In2O3 and 2, 2-dimethyl-1, 3-propanediamine in excess hydrobromic acid solution. Differential scanning calorimetry (DSC) measurement reveals that 1 experiences a first-order structural phase transition at Curie temperature Tc = 176 K. A step-like dielectric anomaly was recorded at around phase transition temperature. Further the variable-temperature single crystal X-ray diffraction indicates that the order-disorder transition of (C5H16N2)2+ cation is the main factor drove the phase transition, changing from the non-centrosymmetric (NCS) space group of P212121 to centrosymmetric (CS) space group Pnma upon heating. This finding paves the avenue to design and explore dielectric switching materials based on In-based organic-inorganic hybrid compounds.



中文翻译:

(III)-基有机-无机杂化化合物:(C 5 H 16 N 2)InBr 5的相变,介电转换性能

通过In 2 O 3与2,2-二甲基-1,3-丙二胺在过量的氢溴酸溶液中的反应合成了铟基有机-无机相变材料(C 5 H 16 N 2)InBr 51)。差示扫描量热法(DSC)测量表明1在居里温度Tc = 176 K处经历了一级结构相变。在相变温度附近记录了阶梯状介电异常。此外,温度可变的单晶X射线衍射表明(C 5 H 16 N 2)的有序转变。2+阳离子是驱动相变的主要因素,加热时从P 2 1 2 1 2 1 1的非中心对称(NCS)空间群变为P nma的中心对称(CS)空间群。该发现为基于In-基有机-无机杂化化合物的介电开关材料的设计和探索铺平了道路。