Deciphering pitting behavior of lithium metal anodes in lithium sulfur batteries
Journal of Energy Chemistry ( IF 14.0 ) Pub Date : 2020-03-04 , DOI: 10.1016/j.jechem.2020.02.039
Fanyang Huang , Shuai Wang , Yulin Jie , Evan Hansen , Shiyang Wang , Zhanwu Lei , Jian Liu , Ruiguo Cao , Genqiang Zhang , Shuhong Jiao

Unambiguous understanding in lithium anode failure mechanism calls for a comprehensive methodology to investigate the coupled morphological, electrochemical and mechanical behaviors during the stripping process. In this work, a mechanistic investigation of the pitting behavior of lithium metal in an electrolyte containing lithium polysulfides in lithium sulfur batteries was developed. It is found that lithium polysulfides could aggravate the nonuniform stripping of lithium electrodes.



中文翻译:

锂硫电池中锂金属阳极的破损点蚀行为

对锂阳极失效机理的明确理解要求一种综合的方法,以研究汽提过程中耦合的形态,电化学和机械行为。在这项工作中,对锂硫电池中含有多硫化锂的电解质中锂金属的点蚀行为的机理进行了研究。发现多硫化锂可加剧锂电极的不均匀剥离。