Results of studying the rheotechnological properties of moldable refractory mixes based on bauxite suspensions plasticized with refractory clay are presented. Features of the effect of filler diameter and binder content in a mix on structural-mechanical and operating properties of specimens based upon it are established. Specimens from the developed mixes intended for molding at low pressure (up to 10 MPa) are characterized by high compressive strength (100 – 110 MPa) and relatively low porosity (up to 20 – 21%) after heat treatment at 1300°C.

中文翻译：

---

基于模制铝土矿悬浮液的高铝混合物

给出了研究基于耐火粘土增塑的铝土矿悬浮液的可塑耐火混合物流变技术特性的结果。建立了混合物中填料直径和粘结剂含量对样品的结构力学和操作性能影响的特征。用于低压成型（最高10 MPa）的已开发混合物的样品具有在1300°C热处理后具有较高的抗压强度（100 – 110 MPa）和较低的孔隙率（最高20 – 21％）的特点。