Effect of Sodium Silicate on the Sintering and Properties of Zirconia Ceramics
Doklady Chemistry ( IF 0.8 ) Pub Date : 2019-09-01 , DOI: 10.1134/s0012500819090015
V. V. Smirnov , S. V. Smirnov , T. O. Obolkina , O. S. Antonova , M. A. Gol’dberg , D. R. Khairutdinova , O. A. Ovchinnikova , S. M. Barinov

Dependences of the formation of the microstructure and phase composition of partially stabilized zirconia ceramics on the sintering temperature and the content of the sintering additive have been studied. It has been shown that introduction of an additive forming a low-temperature melt based on sodium silicate Na2SiO3 reduces the sintering temperature by 200°C. Dense nanocrystalline materials with a crystal size of 100–200 nm, a flexural strength to 600 MPa, and a sintering temperature of 1200–1250°C were obtained.

中文翻译:

硅酸钠对氧化锆陶瓷烧结及性能的影响

研究了部分稳定的氧化锆陶瓷的微观结构和相组成的形成对烧结温度和烧结添加剂含量的依赖性。已经表明,引入基于硅酸钠 Na2SiO3 形成低温熔体的添加剂可使烧结温度降低 200°C。获得了晶体尺寸为 100-200 nm、弯曲强度为 600 MPa、烧结温度为 1200-1250°C 的致密纳米晶材料。