Journal of the European Ceramic Society ( IF 5.8 ) Pub Date : 2020-01-07 , DOI: 10.1016/j.jeurceramsoc.2020.01.009 Shiv Singh , Jie Yin , Lun Feng , Dehi Pada Mondal , Daejong Kim , Sea-Hoon Lee
Several intermediate steps were applied before the precursor infiltration and pyrolysis process to improve the infiltration of SiC slurry for promoting the infiltration of SiC slurry into fiber voids. These steps include sonication, popping, electrophoretic deposition, vacuum infiltration and cold isostatic pressing (CIP). The intermediate processes, especially popping and CIP, had a beneficial effect on green density enhancement and improving the homogeneous infiltration of the slurry into fiber fabrics. The density of the SiCfiber/SiCfiller green body was 2.20 g/cm3, which corresponded to 68 % of relative density. The SiCf/SiC composite has a high density of 2.65 g/cm3 after seven PIP cycles.
中文翻译:
浆料浸渗工艺的改进对SiC f / SiC复合材料前驱体浸渍和热解过程的意义
在前体渗透和热解过程之前应用了几个中间步骤,以改善SiC浆料的渗透性,以促进SiC浆料向纤维空隙中的渗透。这些步骤包括超声处理,爆裂,电泳沉积,真空渗透和冷等静压(CIP)。中间过程,特别是膨化和CIP,对提高生坯密度和改善浆料向纤维织物的均匀渗透具有有益的作用。SiC纤维/ SiC填料生坯的密度为2.20g / cm 3,相当于相对密度的68%。在七个PIP循环后,SiC f / SiC复合材料具有2.65 g / cm 3的高密度。