This paper focus on the nature of a high-damping soft elastic material based on Eucommia ulmoides gum (EUG) obtained by epoxidation of EUG first and then in situ reaction between epoxy group and sodium bisulfite. The influence of degree of modification (M mol%) and degree of sulfonation (S mol%) of the product sulfonated E. ulmoides gum (SEUG) on the melting–crystallization behavior, tensile properties and dynamic mechanical properties is analyzed mainly. The results show that M mol% is the key factor in controlling the aggregation structure and static or dynamic mechanical behavior of SEUG, while the introduced sodium bisulfite groups show strengthening and toughening effect to some extent. Besides, the SEUG with high M mol% shows dramatically high tanδ value. With M mol% increasing, the tensile strength and Shore A hardness of SEUG decrease sequentially, while the elongation at break increases visibly. SEUGs with M mol% above 20.3 display soft and elastic stress–strain behavior. At similar M mol% level, SEUG with higher S mol% shows higher tensile strength and lower elongation at break than the one with lower S mol% value. These are attributed to the transformation of the aggregate structure and the introduction of ion interaction. The maximum tanδ value of SEUG reaches up to 2.19. The removal of the restriction effect of crystal region on the molecular motion of amorphous and the increased intermolecular interaction are thought to be main causes.

中文翻译：

---

杜仲胶基高阻尼软弹性体的制备

本文重点研究了一种基于杜仲胶 (EUG) 的高阻尼软弹性材料的性质，该材料通过 EUG 的环氧化，然后环氧基与亚硫酸氢钠的原位反应获得。主要分析了磺化杜仲胶(SEUG)的改性度(M mol%)和磺化度(S mol%)对熔融结晶行为、拉伸性能和动态力学性能的影响。结果表明，M mol%是控制SEUG的聚集结构和静态或动态力学行为的关键因素，而引入的亚硫酸氢钠基团在一定程度上显示出强化和增韧作用。此外，具有高 M mol% 的 SEUG 显示出非常高的 tanδ 值。随着 M mol% 的增加，SEUG的拉伸强度和肖氏A硬度依次降低，而断裂伸长率明显增加。M mol% 高于 20.3 的 SEUG 显示出柔软和弹性的应力-应变行为。在类似的 M mol% 水平下，具有较高 S mol% 的 SEUG 比具有较低 S mol% 值的 SEUG 显示出更高的拉伸强度和更低的断裂伸长率。这些归因于聚集体结构的转变和离子相互作用的引入。SEUG的最大tanδ值达到2.19。晶体区域对非晶分子运动的限制作用的消除和分子间相互作用的增加被认为是主要原因。与具有较低 S mol% 值的 SEUG 相比，具有较高 S mol% 的 SEUG 显示出更高的拉伸强度和更低的断裂伸长率。这些归因于聚集体结构的转变和离子相互作用的引入。SEUG的最大tanδ值达到2.19。晶体区域对非晶分子运动的限制作用的消除和分子间相互作用的增加被认为是主要原因。与具有较低 S mol% 值的 SEUG 相比，具有较高 S mol% 的 SEUG 显示出更高的拉伸强度和更低的断裂伸长率。这些归因于聚集体结构的转变和离子相互作用的引入。SEUG的最大tanδ值达到2.19。晶体区域对非晶分子运动的限制作用的消除和分子间相互作用的增加被认为是主要原因。