Aligned Droplet Patterns by Dewetting of Polymer Bilayers
Macromolecules ( IF 5.1 ) Pub Date : 2018-07-05 00:00:00 , DOI: 10.1021/acs.macromol.8b00620 Ming Chiu 1 , Jared A. Wood 1 , Asaph Widmer-Cooper 1 , Chiara Neto 1
Macromolecules ( IF 5.1 ) Pub Date : 2018-07-05 00:00:00 , DOI: 10.1021/acs.macromol.8b00620 Ming Chiu 1 , Jared A. Wood 1 , Asaph Widmer-Cooper 1 , Chiara Neto 1
Affiliation
|
Dewetting of polymer thin films has been extensively studied in the past two decades as an approach to produce patterned surfaces. Here we report a novel phenomenon where dewetted polymer droplets spontaneously align on a substrate, and the alignment extends over a large scale (millimeters). The patterns are formed by dewetting a bilayer system formed by poly(4-vinylpyridine) (P4VP) thin film (80 nm) on a polystyrene (PS) thin film (100 nm) prepared by spin-coating. We investigated the mechanism of the spontaneous droplet alignment and concluded that the final aligned pattern results from series of aligned defects on the P4VP, which are formed during spin-coating. We identified experimental parameters that control the appearance and the order of the resulting aligned droplets.
中文翻译：
通过聚合物双层去湿排列的液滴模式
在过去的二十年中，已经对聚合物薄膜的去湿进行了广泛的研究，作为产生图案化表面的一种方法。在这里，我们报告了一种新颖的现象，其中经过润湿处理的聚合物液滴自发地在基板上对齐，并且对齐范围扩大了（毫米）。通过将由聚（4-乙烯基吡啶）（P4VP）薄膜（80 nm）形成的双层体系去湿在旋涂制备的聚苯乙烯（PS）薄膜（100 nm）上形成双层图案，从而形成图案。我们研究了自发液滴对准的机制，并得出结论，最终对准的图案是由P4VP上一系列对准的缺陷产生的，这些缺陷在旋涂过程中形成。我们确定了控制外观和排列的液滴顺序的实验参数。
更新日期：2018-07-05
中文翻译：
通过聚合物双层去湿排列的液滴模式
在过去的二十年中，已经对聚合物薄膜的去湿进行了广泛的研究，作为产生图案化表面的一种方法。在这里，我们报告了一种新颖的现象，其中经过润湿处理的聚合物液滴自发地在基板上对齐，并且对齐范围扩大了（毫米）。通过将由聚（4-乙烯基吡啶）（P4VP）薄膜（80 nm）形成的双层体系去湿在旋涂制备的聚苯乙烯（PS）薄膜（100 nm）上形成双层图案，从而形成图案。我们研究了自发液滴对准的机制，并得出结论，最终对准的图案是由P4VP上一系列对准的缺陷产生的，这些缺陷在旋涂过程中形成。我们确定了控制外观和排列的液滴顺序的实验参数。