Synthesis of non-ionic poly(ester-sulfone) via low-temperature polycondensation for anode-selective electrophoretic deposition and subsequent photo cross-linking
Polymer Journal ( IF 2.3 ) Pub Date : 2017-12-22 , DOI: 10.1038/s41428-017-0001-y
Yoshifumi Matsumoto , Akinori Takasu

AbstractNon-ionic aliphatic polymers containing ester and sulfonyl moieties, poly(ester-sulfones) were found to show anode-selective electrophoresis under electrophoretic deposition (EPD) conditions. Various polyesters containing a sulfide linkage were prepared via low-temperature polycondensation using scandium trifluoromethanesulfonate [Sc(OTf)3] as a catalyst in order to clarify the relationship between the chemical structure and the electrophoresis. Subsequently, oxone oxidation was carried out in order to obtain the expected saturated and unsaturated poly(ester-sulfone)s, and electrophoretic deposition (EPD) of the poly(ester-sulfone) onto stainless steel was performed. For unsaturated poly(ester-sulfone) onto stainless steel, subsequent UV irradiation cured the deposited film, improving the peeling strength of the coating.Graphical AbstractVarious polyesters containing a sulfide linkage were prepared via low-temperature polycondensation using scandium trifluoromethanesulfonate [Sc(OTf)3] as a catalyst in order to clarify the relationship between the chemical structure and the electrophoresis. Subsequently, oxone oxidation was carried out in order to obtain the expected saturated and unsaturated poly(ester-sulfone)s, and electrophoretic deposition (EPD) of the poly(ester-sulfone) onto stainless steel was performed. For unsaturated poly(ester-sulfone) onto stainless steel, subsequent UV irradiation cured the deposited film, improving the peeling strength of the coating.

中文翻译:

通过低温缩聚反应合成非离子聚(酯-砜)用于阳极选择性电泳沉积和随后的光交联

摘要发现含有酯和磺酰基部分的非离子脂肪族聚合物聚(酯-砜)在电泳沉积 (EPD) 条件下显示出阳极选择性电泳。为了阐明化学结构与电泳之间的关系,使用三氟甲磺酸钪[Sc(OTf)3]作为催化剂,通过低温缩聚反应制备了各种含硫键的聚酯。随后,进行oxone氧化以获得预期的饱和和不饱和聚(酯-砜),并进行聚(酯-砜)在不锈钢上的电泳沉积(EPD)。对于不锈钢上的不饱和聚(酯-砜),随后的紫外线照射固化了沉积的薄膜,提高了涂层的剥离强度。图解摘要为了阐明化学结构与电泳之间的关系,以三氟甲磺酸钪[Sc(OTf)3]为催化剂,通过低温缩聚反应制备了各种含硫键的聚酯。随后,进行oxone氧化以获得预期的饱和和不饱和聚(酯-砜),并进行聚(酯-砜)在不锈钢上的电泳沉积(EPD)。对于不锈钢上的不饱和聚(酯-砜),随后的紫外线照射固化了沉积的薄膜,提高了涂层的剥离强度。并在不锈钢上进行聚(酯-砜)的电泳沉积(EPD)。对于不锈钢上的不饱和聚(酯-砜),随后的紫外线照射固化了沉积的薄膜,提高了涂层的剥离强度。并在不锈钢上进行聚(酯-砜)的电泳沉积(EPD)。对于不锈钢上的不饱和聚(酯-砜),随后的紫外线照射固化了沉积的薄膜,提高了涂层的剥离强度。