Efficient Pt–FeOx/TiO2@SBA-15 catalysts for selective hydrogenation of cinnamaldehyde to cinnamyl alcohol
Catalysis Science & Technology ( IF 4.4 ) Pub Date : 2017-11-13 00:00:00 , DOI: 10.1039/c7cy02008b
Yujie Xue 1, 2, 3, 4, 5 , Ruihua Yao 1, 2, 3, 4, 5 , Junrui Li 1, 2, 3, 4, 5 , Guimei Wang 1, 2, 3, 4, 5 , Peng Wu 1, 2, 3, 4, 5 , Xiaohong Li 1, 2, 3, 4, 5
Affiliation  

TiO2 was coated onto mesoporous silica SBA-15 by hydrolysis of tetrabutyl titanate to prepare 15 wt% TiO2@SBA-15 composites (15TS). The 15TS composites retain the mesostructure of the SBA-15 host, and TiO2 was highly dispersed and uniformly coated. 5 wt% Pt nanoparticles supported on 15TS were employed for liquid-phase selective hydrogenation of cinnamaldehyde (CAL) to cinnamyl alcohol (COL). Compared with the Pt catalyst supported on pristine SBA-15, the Pt/15TS catalyst afforded higher activity and selectivity to COL. Furthermore, the modification of the Pt/15TS catalyst by FeOx can greatly improve the activity and selectivity to COL. As a result, the Pt–FeOx/15TS catalyst displayed excellent selectivity to COL (around 84.5%) at nearly complete CAL conversion. Of particular note is that further calcination of the Pt–FeOx/15TS catalyst precursor in air at 773 K before reduction would greatly enhance the catalytic performance. Consequently, the TOF reached 3.06 s−1 with a selectivity to COL of 86.4% over the Pt–FeOx/15TS-773 catalyst. Moreover, the Pt–FeOx/15TS-773 catalyst can also be reused about eight times without distinct loss in activity or selectivity. Based on characterization by XPS and H2-TPR, the important promotion effect of FeOx and strong metal–support interaction played key roles in preferential adsorption and activation of C[double bond, length as m-dash]O bonds in CAL.

中文翻译:

高效的Pt–FeO x / TiO 2 @ SBA-15催化剂,用于将肉桂醛选择性加氢为肉桂醇

通过钛酸四丁酯的水解将TiO 2涂覆到中孔二氧化硅SBA-15上以制备15wt%的TiO 2 SBA-15复合材料(15TS)。15TS复合材料保留了SBA-15主体的介孔结构,并且TiO 2高度分散且被均匀涂覆。将负载在15TS上的5 wt%的Pt纳米颗粒用于肉桂醛(CAL)的液相选择性加氢为肉桂醇(COL)。与负载在原始SBA-15上的Pt催化剂相比,Pt / 15TS催化剂具有更高的活性和对COL的选择性。此外,FeO x对Pt / 15TS催化剂的改性可以大大提高活性和对COL的选择性。结果,Pt–FeO x/ 15TS催化剂在几乎完全的CAL转化率下显示出出色的COL选择性(约84.5%)。特别值得注意的是,还原前在空气中于773 K下进一步煅烧Pt–FeO x / 15TS催化剂前体会大大提高催化性能。因此,在Pt-FeO x / 15TS-773催化剂上,TOF达到3.06 s -1,对COL的选择性为86.4%。此外,Pt-FeO x / 15TS-773催化剂也可以重复使用约八次,而不会明显降低活性或选择性。基于XPS和H 2 -TPR的表征,FeO x的重要促进作用金属与载体之间的强相互作用[双键,长度为m-破折号]在CAL中优先吸附和活化C O键起着关键作用。