Ceramics International ( IF 5.1 ) Pub Date : 2018-02-01 , DOI: 10.1016/j.ceramint.2017.10.180
Congcong Jiang , Shifeng Huang , Guozhong Li , Xiuzhi Zhang , Xin Cheng

Utilization of granite scraps and minor clay tailings to prepare closed-pore foam ceramic was investigated using SiC as foaming agent. The foam ceramic presented promising results with a bulk density of 237.4 kg/m 3 , compressive strength of 0.85 MPa, flexural strength of 0.42 MPa, porosity of 83.31%, water absorption of 2.21% and thermal conductivity of 0.051 W/(m k), which had good potential application in the field of building insulation.

中文翻译:

用花岗岩碎屑制备闭孔泡沫陶瓷

以碳化硅为发泡剂,研究了利用花岗岩碎屑和少量粘土尾矿制备闭孔泡沫陶瓷。泡沫陶瓷的堆积密度为 237.4 kg/m 3 ,抗压强度为 0.85 MPa,弯曲强度为 0.42 MPa,孔隙率为 83.31%,吸水率为 2.21%,热导率为 0.051 W/(mk),结果令人满意,在建筑保温领域具有良好的应用潜力。