Ultrastretchable, Tough, and Notch‐Insensitive Hydrogels Formed with Spherical Polymer Brush Crosslinker
Macromolecular Rapid Communications ( IF 4.2 ) Pub Date : 2017-09-29 , DOI: 10.1002/marc.201700455
Rui Zhang 1 , Lei Wang 1 , Zheqi Shen 1 , Min Li 1 , Xuhong Guo 1 , Yuan Yao 2
Affiliation  

Spherical polymer brushes, poly(acrylic acid) (PAA)‐grafted polystyrene nanoparticle (PAA@PS), are employed as the macro‐crosslinker to prepare PAA hydrogels. Benefitting from the innumerable hydrogen bonds between highly entangled PAA chains both in bulk and on the polymer brush, the PAA/PAA@PS hydrogels combine desirable stretchability, toughness, and notch‐insensitivity. The uniaxial tensile tests show a very high fracture elongation up to 9.1 × 103% while the fracture toughness reaches 3.0 MJ m−3 and the maximum swelling ratio of the hydrogel can be 2.0 × 103 as well. After being loaded with silver nanoparticles, the PAA/PAA@PS hydrogels are employed as a recyclable catalyst successfully.

中文翻译:

与球形聚合物刷交联剂形成的可超拉伸,坚韧且不刻痕的水凝胶

球形聚合物刷,聚丙烯酸(PAA)接枝的聚苯乙烯纳米颗粒(PAA @ PS)被用作大分子交联剂,以制备PAA水凝胶。得益于大量缠结的PAA链在本体和聚合物刷上无数的氢键,PAA / PAA @ PS水凝胶结合了理想的可拉伸性,韧性和缺口敏感性。单轴拉伸试验显示出非常高的断裂伸长率,高达9.1×10 3%,而断裂韧性达到3.0 MJ m -3,水凝胶的最大溶胀率也可以为2.0×10 3。负载银纳米颗粒后,PAA / PAA @ PS水凝胶被成功用作可循环利用的催化剂。