Comparing structure-property evolution for PM-HIP and forged alloy 625 irradiated with neutrons to 1 dpa

https://doi.org/10.1016/j.msea.2022.144058Get rights and content
Under a Creative Commons license
open access

Abstract

The nuclear power industry has growing interest in qualifying powder metallurgy with hot isostatic pressing (PM-HIP) to replace traditional alloy fabrication methods for reactor structural components. But there is little known about the response of PM-HIP alloys to reactor conditions. This study directly compares the response of PM-HIP to forged Ni-base Alloy 625 under neutron irradiation doses ∼0.5–1 displacements per atom (dpa) at temperatures ranging ∼321–385 °C. Post-irradiation examination involves microstructure characterization, ASTM E8 uniaxial tensile testing, and fractography. Up through 1 dpa, PM-HIP Alloy 625 appears more resistant to irradiation-induced cavity nucleation than its forged counterpart, and consequently experiences significantly less hardening. This observed difference in performance can be explained by the higher initial dislocation density of the forged material, which represents an interstitial-biased sink that leaves a vacancy supersaturation to nucleate cavities. These findings show promise for qualification of PM-HIP Alloy 625 for nuclear applications, although higher dose studies are needed to assess the steady-state irradiated microstructure.

Keywords

Powder metallurgy
Neutron irradiation
Tensile testing
Electron microscopy
Alloy 625
Ni alloy
Advanced manufacturing

Data availability

Data will be made available on request.

Cited by (0)