Abstract
Wireless technology relies on the conversion of alternating electromagnetic fields into direct currents, a process known as rectification. Although rectifiers are normally based on semiconductor diodes, quantum mechanical non-reciprocal transport effects that enable a highly controllable rectification were recently discovered1,2,3,4,5,6,7,8,9. One such effect is magnetochiral anisotropy (MCA)6,7,8,9, in which the resistance of a material or a device depends on both the direction of the current flow and an applied magnetic field. However, the size of rectification possible due to MCA is usually extremely small because MCA relies on inversion symmetry breaking that leads to the manifestation of spin–orbit coupling, which is a relativistic effect6,7,8. In typical materials, the rectification coefficient γ due to MCA is usually ∣γ∣ ≲ 1 A−1 T−1 (refs. 8,9,10,11,12) and the maximum values reported so far are ∣γ∣ ≈ 100 A−1 T−1 in carbon nanotubes13 and ZrTe5 (ref. 14). Here, to overcome this limitation, we artificially break the inversion symmetry via an applied gate voltage in thin topological insulator (TI) nanowire heterostructures and theoretically predict that such a symmetry breaking can lead to a giant MCA effect. Our prediction is confirmed via experiments on thin bulk-insulating (Bi1−xSbx)2Te3 (BST) TI nanowires, in which we observe an MCA consistent with theory and ∣γ∣ ≈ 100,000 A−1 T−1, a very large MCA rectification coefficient in a normal conductor.
Similar content being viewed by others
Main
In most materials transport is well described by Ohm’s law, V = IR0, dictating that for small currents I the voltage drop across a material is proportional to a constant resistance R0. Junctions that explicitly break inversion symmetry, for instance semiconductor pn junctions, can produce a difference in resistance R as a current flows in one or the opposite direction through the junction, R( + I) ≠ R( − I); this difference in resistance is the key ingredient required to build a rectifier. A much greater degree of control over the rectification effect can be achieved when a similar non-reciprocity of resistance exists as a property of a material rather than a junction. However, to achieve such a non-reciprocity necessitates that the inversion symmetry of the material is itself broken. Previously, large non-reciprocal effects were observed in materials where inversion symmetry breaking resulted in strong spin–orbit coupling (SOC)6,7,8,9,10,11,12,14. However, as SOC is always a very small energy scale, this limits the possible size of any rectification effect.
The non-reciprocal transport effect considered here is magnetochiral anisotropy (MCA), which occurs when both inversion and time-reversal symmetry are broken6,7,8,9,10,11,12,14. When allowed, the leading order correction of Ohm’s law due to MCA is a term that is second order in current and manifests itself as a resistance of the form R = R0(1 + γBI), with B the magnitude of an external magnetic field and the rectification coefficient γ determines the size of the possible rectification effect. MCA may also be called bilinear magnetoelectric resistance9,15. We note that non-reciprocal transport in ferromagnets3,4 does not allow the coefficient γ to be calculated and rectification of light into d.c. current due to bulk photovoltaic effects16,17,18 concerns much higher energy scales than those of MCA.
In heterostructures of topological materials it is possible to artificially break the inversion symmetry of a material19; such an approach provides an unexplored playground to substantially enhance the size of non-reciprocal transport effects. In this context, quasi-one-dimensional (1D) bulk-insulating 3D TI nanowires19,20,21,22,23 are the perfect platform to investigate large possible MCAs due to artificial inversion symmetry breaking. In the absence of symmetry breaking, for an idealized cylindrical topological insulator (TI) nanowire—although generalizable to an arbitrary cross-section19,22—the surface states form energy subbands of momentum k along the nanowire and half-integer angular momentum \(l =\pm \frac{1}{2},\frac{3}{2},\ldots \,\) around the nanowire, where the half-integer values are due to spin-momentum locking. The presence of inversion symmetry along a TI nanowire requires the subbands with angular momenta ±l to be degenerate. It is possible to artificially break the inversion symmetry along the wire, for instance, by the application of a gate voltage from the top of the TI nanowire19,21,23. Such a gate voltage induces a non-uniformity of charge density across the nanowire cross-section, which breaks the subband degeneracy and results in a splitting of the subband at finite momenta19 (Fig. 1c). An additional consequence is that the subband states develop a finite spin polarization in the plane perpendicular to the nanowire axis (that is, the yz plane) with the states with opposite momenta being polarized in the opposite directions, such that the time-reversal symmetry is respected. When a magnetic field is applied, the subbands can be shifted in energy via the Zeeman effect, which suggests that an MCA can be present in this set-up. Indeed, using the Boltzmann equation10,11,14 (Supplementary Note 4), we found an MCA of the vector-product type \(\gamma \propto {{{{{\mathbf{P}}}}}}\cdot (\hat{{{{{{\mathbf{B}}}}}}}\times \hat{{{{{{\mathbf{I}}}}}}})\) with the characteristic vector P in the yz plane. For the rectification effect γl(μ) of a given subband pair η = ± labelled by l > 0, we found:
where e is the elementary charge, h is the Planck constant, σ(1) is the conductivity in linear response, τ is the scattering time, \({{{V}}}_l^{\eta }(k)=\frac{1}{{\hslash }^{2}}{\partial }_{k}^{2}{\varepsilon }_l^{\eta }(k)\) in which \({\varepsilon }_l^{\eta }(k)\) describes the energy spectrum as a function of momentum k in the presence of symmetry breaking terms and the finite magnetic field B (Fig. 1c and Supplementary Note 4) and \({k}_{l,{\rm{R}}({\rm{L}})}^{\eta }\) is the right (left) Fermi momentum of a given subband (Fig. 1c). Owing to the non-parabolic spectrum of the subbands, differences in \({{{V}}}_{l }^{\eta }(k)\) are large for a TI nanowire, which results in the giant MCA. The quantities \({\gamma }_{l }^{+}\) and \({\gamma }_{l }^{-}\) are the contributions of the individual subbands. The behaviour of γl as a function of the chemical potential μ is shown in Fig. 1d. We found that, as the chemical potential is tuned through the subband pair, γl changes sign depending on the chemical potential. This makes the rectification effect due to the MCA highly controllable by both the magnetic field direction and the chemical potential μ within a given subband pair, which can be experimentally adjusted by a small change in gate voltage Vg. For reasonable experimental parameters, we predict that the theoretical size of the rectification can easily reach giant values of γ ≈ 5 × 105 T−1 A−1 (Supplementary Note 5).
To experimentally investigate the predicted non-reciprocal transport behaviour, we fabricated nanowire devices24 of the bulk-insulating TI material BST, as shown in Fig. 1a by etching high-quality thin films grown by molecular beam epitaxy (MBE). The nanowires have a rectangular cross-section of thickness d ≈ 16 nm and width w ≈ 200 nm, with channel lengths up to several micrometres. The long channel lengths suppress coherent transport effects, such as universal conductance fluctuations, and the cross-sectional perimeter allows for the formation of well-defined subbands (Supplementary Note 8). An electrostatic gate electrode is placed on top of the transport channel for the dual purpose of breaking inversion symmetry and tuning the chemical potential. The resistance R of the nanowire shows a broad maximum as a function of Vg (Fig. 2a inset), which indicates that the chemical potential can be tuned across the charge neutrality point (of the surface-state Dirac cone; the dominant surface transport in these nanowires is further documented in Supplementary Note 7). Near the broad maximum (that is, around the charge neutrality point), the Vg dependence of R shows reproducible peaks and dips (Fig. 2a), which is a manifestation of the quantum-confined quasi-1D subbands realized in TI nanowires23—each peak corresponds to the crossing of a subband minima, although the feature can be smeared by disorder23. To measure the non-reciprocal transport, we used a low-frequency a.c. excitation current I = I0sinωt and probed the second-harmonic resistance R2ω; here, I0 is the amplitude of the excitation current, ω is the angular frequency, and t is time. The MCA causes a second-harmonic signal that is antisymmetric with the magnetic field B and therefore we calculated the antisymmetric component \({R}_{2\omega }^{{\rm{A}}}\equiv \frac{{R}_{2\omega }({{{{{B}}}}})-{R}_{2\omega }(-{{{{{B}}}}})}{2}\), which is proportional to γ via \({R}_{2\omega }^{{\rm{A}}}=\frac{1}{2}\gamma {R}_{0}B{I}_{0}\approx \frac{1}{2}\gamma RB{I}_{0}\), where R0 is the reciprocal resistance (see Methods for details).
In our experiment, we observed a large \({R}_{2\omega }^{{\rm{A}}}\) for Vg ≳ 2 V with a magnetic field along the z axis. The \({R}_{2\omega }^{{\rm{A}}}({B}_{z})\) behaviour was linear for small Bz values (Fig. 2b) and \({R}_{2\omega }^{A}\) increased linearly with I0 up to ~250 nA (Fig. 2c), both of which are the defining characteristics of the MCA. The deviation from the linear behaviour at higher B fields is probably due to orbital effects (Supplementary Note 3). The magnetic-field-orientation dependence of γ, shown in Fig. 2d for the rotation in the zx plane, agrees well with γ ≈ γ0cosα, with α the angle from the z direction and γ0 the value at α = 0; the rotation in the yz plane gave similar results, whereas MCA remained essentially zero for the rotation in the xy plane (Supplementary Note 10). This points to the vector-product type MCA, \({R}_{2\omega }^{{\rm{A}}}\propto {{{{{\mathbf{P}}}}}}\cdot ({{{{{\mathbf{B}}}}}}\times {{{{{\mathbf{I}}}}}})\), with the characteristic vector P essentially parallel to y, which is probably dictated by the large g-factor anisotropy25 (Supplementary Note 2). The maximum size of the ∣γ∣ in Fig. 2d reaches a giant value of ∣γ∣ ≈ 6 × 104 A−1 T−1. In addition, one may notice in Fig. 2b,d that the relative sign of γ changes for different Vg values, which is very unusual. We observed a giant MCA with a similarly large rectification γ in all the measured devices, some of which reached ~1 × 105 A−1 T−1 (Supplementary Note 13). Note that in the MCA literature, γ is often multiplied by the cross-sectional area A of the sample to give γ′ (= γA), which is useful to compare the MCA in different materials as a bulk property. However, in nanodevices, such as our TI nanowires, the large MCA owes partly to mesoscopic effects and γ′ is not very meaningful. In fact, the large MCA rectification of ∣γ∣ ≈ 100 A−1 T−1 observed in chiral carbon nanotubes13 was largely due to the fact that a nanotube can be considered a quasi-1D system. In Supplementary Note 13, we present extensive comparisons of the non-reciprocal transport reported for various systems.
A unique feature of the predicted MCA is the controllability of its sign with a small change of Vg. To confirm this prediction, we measured detailed Vg dependences of \({R}_{2\omega }^{{\rm{A}}}\) in the Vg range of 5.1–5.5 V, in which the chemical potential appears to pass through two subband minima, because R(Vg) presents two peaks (Fig. 3a). We, indeed, observed the slope of \({R}_{2\omega }^{{\rm{A}}}({B}_{z})\) to change sign with Vg (Fig. 3b), and its zero-crossing roughly coincides with the peak or dip in the R(Vg) curve (compare Fig. 3a,b). A change in sign of the slope of \({R}_{2\omega }^{A}({B}_{z})\) on either side of the R(Vg) peaks was also observed in other devices (Supplementary Note 11). To obtain confidence in this striking observation, the evolution of the \({R}_{2\omega }^{{\rm{A}}}({B}_{z})\) behaviour on changing Vg is shown in Fig. 3c for many Vg values. This sign change on a small change of Vg also endows the giant MCA in TI nanowires with an unprecedented level of control. In addition, this Vg-dependent sign change of MCA gives a unique proof that the origin of the peak-and-dip feature in R(Vg) is, indeed, subband crossings.
The giant MCA observed here due to an artificial breaking of inversion symmetry in the TI nanowires not only results in a maximum rectification coefficient γ that is extremely high, but it is also highly controllable by small changes of chemical potential. Although rather different to the MCA of a normal conductor discussed here, we note that large rectification effects of a similar magnitude were recently discovered in non-centrosymmetric superconductor devices1,5 and in quantum anomalous Hall edge states4, for which the controllability is comparatively limited. It is prudent to mention that the MCA reported here was measured below 0.1 K and it diminishes at around 10 K (Supplementary Note 12), which is consistent with the sub-bandgap of ~1 meV. As TI nanowire devices are still in their infancy24, the magnitude and temperature dependence of the MCA could be improved with future improvements in nanowire quality and geometry; for example, in a 20-nm-diameter nanowire, the sub-bandgap would be ~10 meV, which enables MCAs up to ~100 K. The presence of the giant MCA provides compelling evidence for a large spin splitting of the subbands in TI nanowires with a broken inversion symmetry, which can be used for spin filters26,27. Moreover, it has been suggested that the helical spin polarization and large energy scales possible in such TI nanowires with a broken inversion symmetry can be used as a platform for robust Majorana bound states19, which are an integral building block for future topological quantum computers.
Methods
Theory
Transport coefficients were calculated using the Boltzmann equation11,14 to attain the current density due to an electric field E up to the second order such that j = j(1) + j(2) = σ(1)E + σ(2)E2. As discussed in ref. 11, experimentally the voltage drop V = EL as a function of current I is measured in the form V = R0I(1 + γBI). Using R0 = L/σ(1) for a nanowire of length L, a comparison with the experimental behaviour can then be achieved via the relation \({\gamma }_{0}=-\frac{{\sigma }^{(2)}}{B{({\sigma }^{(1)})}^{2}}\). Although the linear response conductivity σ(1) contains small peaks and dips due to an increased scattering rate close to the bottom of a subband, such fluctuations occur on top of a large constant conductivity and we therefore approximate \({\gamma }_{0}\approx \frac{A}{B}{\sigma }^{(2)}\), with \(A=-1/{({\sigma }^{(1)})}^{2}\) approximately constant.
Material growth and device fabrication
A 2 × 2 cm2 thin film of BST was grown on a sapphire (0001) substrate by co-evaporation of high-purity Bi, Sb and Te in an ultrahigh vacuum MBE chamber. The flux of Bi and Sb was optimized to obtain the most bulk-insulating film, which was achieved with a ratio of 1:6.8. The thickness varied in the range 14–19 nm in the whole film. Immediately after taking the film out of the MBE chamber, it was capped with a 3-nm-thick Al2O3 capping layer grown by atomic-layer deposition at 80 °C using an Ultratec Savannah S200. The carrier density and the mobility of the film were extracted from Hall measurements performed at 2 K using a Quantum Design PPMS. Gate-tunable multiterminal nanowire devices were fabricated using the following top-down approach: after defining the nanowire pattern with electron-beam lithography, the film was first dry etched using a low-power Ar plasma and then wet etched with a H2SO4/H2O2/H2O aqueous solution. To prepare the contact leads, the Al2O3 capping layer was removed in a heated aluminium etchant (Type-D, Transene) and 5/45 nm Pt/Au contacts were deposited by ultrahigh vacuum sputtering. Then, the whole device was capped with a 40-nm-thick Al2O3 dielectric grown by atomic-layer deposition at 80 °C, after which the 5/40 nm Pt/Au top gate was sputter deposited. Scanning electron microscopy was used to determine the nanowire size. Devices 1–4 reported in this Letter were fabricated on the same film in one batch, whereas device 5 (Supplementary Notes 7 and 8) was fabricated on a similar film.
Second-harmonic resistance measurement
Transport measurements were performed in a dry dilution refrigerator (Oxford Instruments TRITON 200, base temperature ~20 mK) equipped with a 6/1/1-T superconducting vector magnet. The first- and second-harmonic voltages were measured in a standard four-terminal configuration with a low-frequency lock-in technique at 13.37 Hz using NF Corporation LI5645 lock-ins. In the presence of the vector-product-type MCA with \({{{\bf{P}}}}\parallel \hat{{{{\boldsymbol{y}}}}}\), the voltage is given by V = R0I(1 + γBI) for \({{{\bf{I}}}}\parallel \hat{{{{\boldsymbol{x}}}}}\) and \({{{\bf{B}}}}\parallel \hat{{{{\boldsymbol{z}}}}}\), where a hat indicates a unit vector in the given direction. For an a.c. current I = I0sinωt this becomes \(V={R}_{0}{I}_{0}\sin \omega t+\frac{1}{2}\gamma {R}_{0}B{I}_{0}^{2}[1+\sin (2\omega t-\frac{\uppi }{2})]\), which allows us to identify \({R}_{2\omega }=\frac{1}{2}\gamma {R}_{0}B{I}_{0}\) by measuring the out-of-phase component of the a.c. voltage at a frequency of 2ω. The d.c. gate voltage was applied using a Keithley 2450.
Error bars
In the plots of \({R}_{2\omega }^{A}\) versus I shown in Fig. 2c (and in Supplementary Figs. 9b, 10b, 11b and 12b), the data points for each current value were calculated by obtaining slopes from linear fits to the \({R}_{2\omega }^{{\rm{A}}}(B)\) data at that current in the indicated B range (done individually for each measured B sweep); the standard deviation was calculated for the set of obtained slopes at each current and used as the error bar. In the plots of γ versus the angle shown in Fig. 2d (and in Supplementary Figs. 6 and 7) as well as the plot of γ versus T shown in Supplementary Fig. 13, the data points for each angle were calculated by obtaining slopes from linear fits to the \({R}_{2\omega }^{{\rm{A}}}(B)\) data at that angle in the indicated B range (done individually for each measured B sweep); from the set of obtained slopes at each angle, the error was calculated by using a minimum–maximum approach, in which we calculate the error to be half of the difference between the maximum and the minimum (calculating the standard deviation gives very similar results). In the plots of \({R}_{2\omega }^{{\rm{A}}}\) versus Vg shown Fig. 3b, the data points for each Vg value were calculated by obtaining slopes from the linear fits to the \({R}_{2\omega }^{{\rm{A}}}(B)\) data (shown in Fig. 3c) at that Vg in the indicated B range (done individually for each measured B sweep); from the set of obtained slopes per Vg, the standard deviation was calculated and used as the error bar.
Data availability
The data that support the findings of this study are available at the online depository figshare with the identifier https://doi.org/10.6084/m9.figshare.1933657128 and Supplementary Information. Additional data are available from the corresponding authors upon reasonable request.
References
Ando, F. et al. Observation of superconducting diode effect. Nature 584, 373–376 (2020).
Isobe, H., Xu, S.-Y. & Fu, L. High-frequency rectification via chiral Bloch electrons. Sci. Adv. 6, eaay2497 (2020).
Yasuda, K. et al. Large unidirectional magnetoresistance in a magnetic topological insulator. Phys. Rev. Lett. 117, 127202 (2016).
Yasuda, K. et al. Large non-reciprocal charge transport mediated by quantum anomalous Hall edge states. Nat. Nanotechnol. 15, 831–835 (2020).
Baumgartner, C. et al. Supercurrent rectification and magnetochiral effects in symmetric Josephson junctions. Nat. Nanotechnol. 17, 39–44 (2022).
Rikken, G. L. J. A., Fölling, J. & Wyder, P. Electrical magnetochiral anisotropy. Phys. Rev. Lett. 87, 236602 (2001).
Rikken, G. L. J. A. & Wyder, P. Magnetoelectric anisotropy in diffusive transport. Phys. Rev. Lett. 94, 016601 (2005).
Tokura, Y. & Nagaosa, N. Non-reciprocal responses from non-centrosymmetric quantum materials. Nat. Commun. 9, 3740 (2018).
He, P. et al. Bilinear magnetoelectric resistance as a probe of three-dimensional spin texture in topological surface states. Nat. Phys. 14, 495–499 (2018).
Morimoto, T. & Nagaosa, N. Chiral anomaly and giant magnetochiral anisotropy in noncentrosymmetric Weyl semimetals. Phys. Rev. Lett. 117, 146603 (2016).
Ideue, T. et al. Bulk rectification effect in a polar semiconductor. Nat. Phys. 13, 578–583 (2017).
Rikken, G. L. J. A. & Avarvari, N. Strong electrical magnetochiral anisotropy in tellurium. Phys. Rev. B 99, 245153 (2019).
Krstić, V., Roth, S., Burghard, M., Kern, K. & Rikken, G. Magneto-chiral anisotropy in charge transport through single-walled carbon nanotubes. J. Chem. Phys. 117, 11315–11319 (2002).
Wang, Y. et al. Gigantic magnetochiral anisotropy in the topological semimetal ZrTe5. Preprint at https://doi.org/10.48550/arXiv.2011.03329 (2020).
Zhang, S. S. L. & Vignale, G. Theory of bilinear magneto-electric resistance from topological-insulator surface states. Proc. SPIE 10732 1073215 (2018).
Inglot, M., Dugaev, V. K., Sherman, E. Y. & Barnaś, J. Enhanced photogalvanic effect in graphene due to Rashba spin–orbit coupling. Phys. Rev. B 91, 195428 (2015).
Zhang, Y. et al. Switchable magnetic bulk photovoltaic effect in the two-dimensional magnet CrI3. Nat. Commun. 10, 3783 (2019).
Bhalla, P., MacDonald, A. H. & Culcer, D. Resonant photovoltaic effect in doped magnetic semiconductors. Phys. Rev. Lett. 124, 087402 (2020).
Legg, H. F., Loss, D. & Klinovaja, J. Majorana bound states in topological insulators without a vortex. Phys. Rev. B 104, 165405 (2021).
Zhang, Y. & Vishwanath, A. Anomalous Aharonov–Bohm conductance oscillations from topological insulator surface states. Phys. Rev. Lett. 105, 206601 (2010).
Ziegler, J. et al. Probing spin helical surface states in topological HgTe nanowires. Phys. Rev. B 97, 035157 (2018).
de Juan, F., Bardarson, J. H. & Ilan, R. Conditions for fully gapped topological superconductivity in topological insulator nanowires. SciPost Phys. 6, 060 (2019).
Münning, F. et al. Quantum confinement of the Dirac surface states in topological-insulator nanowires. Nat. Commun. 12, 1038 (2021).
Breunig, O. & Ando, Y. Opportunities in topological insulator devices. Nat. Rev. Phys 4, 184–193 (2022).
Liu, C.-X. et al. Model Hamiltonian for topological insulators. Phys. Rev. B 82, 045122 (2010).
Středa, P. & Šeba, P. Antisymmetric spin filtering in one-dimensional electron systems with uniform spin–orbit coupling. Phys. Rev. Lett. 90, 256601 (2003).
Braunecker, B., Japaridze, G. I., Klinovaja, J. & Loss, D. Spin-selective Peierls transition in interacting one-dimensional conductors with spin–orbit interaction. Phys. Rev. B 82, 045127 (2010).
Rößler, M. et al. Giant magnetochiral anisotropy from quantum confined surface states of topological insulator nanowires. figshare https://doi.org/10.6084/m9.figshare.19336571.v1 (2022).
Acknowledgements
We acknowledge useful discussions with A. Rosch and B. Shklovskii. This work was supported by the Georg H. Endress Foundation (H.F.L.) and NCCR QSIT, a National Centre of Excellence in Research, funded by the Swiss National Science Foundation (grant no. 51NF40-185902) (H.F.L., D.L. and J.K.). This project has received funding from the European Research Council (ERC) under the European Union’s Horizon 2020 research and innovation programme (grant agreement no. 741121 (Y.A.) and grant agreement no. 757725 (J.K.)). It was also funded by the Deutsche Forschungsgemeinschaft (DFG, German Research Foundation) under CRC 1238-277146847 (Subprojects A04 and B01) (Y.A., O.B. and A.A.T.) as well as under Germany’s Excellence Strategy—Cluster of Excellence Matter and Light for Quantum Computing (ML4Q) EXC 2004/1-390534769 (Y.A.). G.L. acknowledges support from the KU Leuven BOF and Research Foundation Flanders (FWO, Belgium), file no. 27531 and no. 52751.
Funding
Open access funding provided by Universität zu Köln
Author information
Authors and Affiliations
Contributions
H.F.L., with help from J.K., D.L. and Y.A., conceived the project. H.F.L., with help from J.K. and D.L., performed the theoretical calculations. M.R. fabricated the devices, performed the experiments and analysed the data with help from H.F.L., F.M., D.F., O.B. and Y.A. A.B., G.L., A.U. and A.A.T. provided the material. H.F.L., M.R., D.L., J.K. and Y.A. wrote the manuscript with inputs from all the authors.
Corresponding authors
Ethics declarations
Competing interests
The authors declare no competing interests.
Peer review
Peer review information
Nature Nanotechnology thanks Zhao-Hua Cheng, Dimitrie Culcer and the other, anonymous, reviewer(s) for their contribution to the peer review of this work.
Additional information
Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Supplementary information
Supplementary Information
Supplementary Figs. 1–14, Notes 1–13 and Tables 1 and 2.
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Legg, H.F., Rößler, M., Münning, F. et al. Giant magnetochiral anisotropy from quantum-confined surface states of topological insulator nanowires. Nat. Nanotechnol. 17, 696–700 (2022). https://doi.org/10.1038/s41565-022-01124-1
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1038/s41565-022-01124-1
This article is cited by
-
Light-induced giant enhancement of nonreciprocal transport at KTaO3-based interfaces
Nature Communications (2024)
-
Signatures of a surface spin–orbital chiral metal
Nature (2024)