Optimal Pore Size of Honeycomb Polylactic Acid Films for In Vitro Cartilage Formation by Synovial Mesenchymal Stem Cells

Yagi, Misaki; Mizuno, Mitsuru; Fujisawa, Ryota; Katano, Hisako; Endo, Kentaro; Ozeki, Nobutake; Sakamaki, Yuriko; Koga, Hideyuki; Sekiya, Ichiro

doi:https://doi.org/10.1155/2021/9239728

Stem Cells International

On this page

Abstract Background Methods Results Discussion Abbreviations Data Availability Ethical Approval Consent Conflicts of Interest Authors’ Contributions Acknowledgments References Copyright Related Articles

Special Issue

Molecules and Biomaterial Technologies Affecting Stem Cell Differentiation

View this Special Issue

Research Article | Open Access

Volume 2021 | Article ID 9239728 | https://doi.org/10.1155/2021/9239728

Optimal Pore Size of Honeycomb Polylactic Acid Films for In Vitro Cartilage Formation by Synovial Mesenchymal Stem Cells

Misaki Yagi,¹Mitsuru Mizuno,¹Ryota Fujisawa,¹Hisako Katano,¹Kentaro Endo,¹Nobutake Ozeki,¹Yuriko Sakamaki,²Hideyuki Koga,³and Ichiro Sekiya¹

Academic Editor: Marco Mascitti

Received06 Apr 2021

Revised24 Jun 2021

Accepted16 Jul 2021

Published03 Aug 2021

Abstract

Background. Tissue engineering of cartilage requires the selection of an appropriate artificial scaffold. Polylactic acid (PLA) honeycomb films are expected to be highly biodegradable and cell adhesive due to their high porosity. The purpose of this study was to determine the optimal pore size of honeycomb PLA films for in vitro cartilage formation using synovial mesenchymal stem cells (MSCs). Methods. Suspensions of human synovial MSCs were plated on PLA films with different pore sizes (no pores, or with 5 μm or 20 μm pores) and then observed by scanning electron microscopy. The numbers of cells remaining in the film and passing through the film were quantified. One day after plating, the medium was switched to chondrogenic induction medium, and the films were time-lapse imaged and observed histologically. Results. The 5 μm pore film showed MSCs with pseudopodia that extended between several pores, while the 20 μm pore film showed MSC bodies submerged into the pores. The number of adhered MSCs was significantly lower for the film without pores, while the number of MSCs that passed through the film was significantly higher for the 20 μm pore film. MSCs that were induced to form cartilage peeled off as a sheet from the poreless film after one day. MSCs formed thicker cartilage at two weeks when growing on the 5 μm pore films than on the 20 μm pore films. Conclusions. Honeycomb PLA films with 5 μm pores were suitable for in vitro cartilage formation by synovial MSCs.

1. Background

Tissue engineering of cartilage requires the appropriate selection of cells [1]. Several cell candidates are currently available, including chondrocytes, induced pluripotent stem (iPS) cells, and mesenchymal stem cells (MSCs). The use of chondrocytes is invasive, as cell collection requires that normal cartilage be sacrificed [2]; however, iPS cells require more time and effort than other cell types for cartilage differentiation [3]. MSCs are therefore more useful, as their cell sources are easy to harvest, the cells proliferate well, and they can be induced to differentiate into cartilage. Synovial MSCs are particularly attractive as a cell source for tissue engineering of cartilage because of their high chondrogenic differentiation potential [4, 5].

The appropriate selection of artificial material is also important for cartilage engineering [6] in addition to the selection of synovial MSCs. Several artificial scaffold materials are already in clinical use [7]. In the field of orthopedics, one of the most popular scaffold materials is polylactic acid (PLA) because of its biodegradability; however, cells can have difficulty adhering to it. For this reason, PLA is not yet in common use as a scaffold for cells used clinically for cartilage regeneration. Efforts made to overcome this adhesion problem have included spinning of PLA nanofibers and arranging PLA fibers in lattice patterns [8, 9], but the types of PLA scaffolds that are most suitable for tissue formation have not yet been identified.

PLA can be prepared in the form of honeycomb-like sheets, and these are expected to show highly biodegradability and improved cell adhesion due to their high porosity [10]. Porous films can be formed from water droplet templates by the breath figure method, and this method has attracted considerable interest because of its simplicity and wide applicability to a variety of materials. Recently, honeycomb films have been prepared by the breath figure technique [11, 12]; however, the best pore size for efficient cell adhesion and cartilage formation has not been established. The purpose of the present study was to determine the optimal pore size of honeycomb PLA films for in vitro cartilage formation by synovial MSCs.

2. Methods

2.1. Preparation of Synovial MSCs

All methods were carried out in accordance with relevant guidelines and regulations. All procedures performed in the study involving human participants were in accordance with the Declaration of Helsinki [13]. This study was approved by the Medical Research Ethics Committee of Tokyo Medical and Dental University (M2017-142), and informed consent was obtained from all study subjects.

Human synovium was harvested from the knees of patients with osteoarthritis who underwent total knee arthroplasty operations, and cell culture was performed according to the method established in our previous reports [4, 14, 15]. Briefly, the synovium was minced and digested at 37°C for 3 h in a solution of 3 mg/mL collagenase (Sigma Aldrich, MO, USA), and the digested cells were filtered through a 70 μm cell strainer (Greiner Bio-one GmbH, Kremsmuenster, Austria). The obtained nucleated cells were cultured in 150 cm² culture dishes (Nalge Nunc International, Thermo Fisher Scientific, MA, USA) in 18 mL alpha minimum essential medium (αMEM, Thermo Fisher Scientific) containing 10% fetal bovine serum (FBS, Thermo Fisher Scientific). The cells were treated with 0.25% trypsin-EDTA (Thermo Fisher Scientific) at 37°C for 5 min, harvested, and cryopreserved as passage 0. For cell culture, the frozen cells were slowly thawed, plated, and incubated for 4 days as passage 1. These passage 1 cells were then replated at 50 cells/cm², cultured for 14 days, and the resulting passage 2 cells were used for analyses.

2.2. Differentiation Assays

The differentiation potential of the MSCs was evaluated as in previous studies [15–17]. Chondrogenesis was examined by suspending synovial MSCs in 0.5 mL chondrogenic induction medium consisting of Dulbecco’s modified Eagle’s medium (DMEM, Thermo Fisher Scientific) containing 10 ng/mL transforming growth factor-β3 (TGF-β3, Miltenyi Biotec, Bergisch Gladbach, Germany), 500 ng/mL bone morphogenetic protein 2 (BMP-2, Medtronic, MN, USA), 40 μg/mL proline (Sigma-Aldrich), 100 nM dexamethasone (Fujifilm Wako Pure Chemical Corporation, Osaka, Japan), 100 μg/mL pyruvate (Sigma-Aldrich), 50 μg/mL ascorbate-2-phosphate (Fujifilm Wako Pure Chemical Corporation), and 50 mg/mL 1% ITS Premix (BD: Becton, Dickinson and Company, NZ, USA). The cells were pelleted by centrifugation at 500 × g for 10 min and then cultured for 21 days. After centrifugation, the pellets were sectioned and stained with toluidine blue (Fujifilm Wako Pure Chemical Corporation) for morphological analysis. Adipogenesis was determined by suspending 100 synovial MSCs in a 60 cm² dish and culturing in culture medium for 14 days to produce cell colonies. The adherent cells were cultured for a further 21 days in adipogenic induction medium consisting of α-MEM supplemented with 100 nM dexamethasone, 0.5 mM isobutylmethylxanthine (Sigma-Aldrich), and 50 mM indomethacin (Fujifilm Wako Pure Chemical Corporation). Adipocytes were stained with oil red O (Muto Pure Chemicals, Tokyo, Japan).

Calcification was studied by plating 100 synovial MSCs in a 60 cm² dish and culturing for 14 days in culture medium to allow formation of cell colonies. The adherent cells were further cultured in a calcification induction medium consisting of α-MEM supplemented with 50 μg/mL ascorbic acid 2-phosphate, 10 nM dexamethasone, and 10 mM β-glycerophosphate (Sigma-Aldrich). After 21 days, calcification was assessed by alizarin red staining (Merck Millipore, MA, USA).

2.3. PLA Honeycomb Films

Circular PLA films with a diameter of 6 mm and thickness of 5 μm were prepared as three types: a PLA film without any pores (0 μm), one with 5 μm pores, and one with 20 μm pores. Before cell plating, the films were immersed in 70% ethanol, washed with phosphate-buffered saline (PBS, Thermo Fisher Scientific) for hydrophilization, and incubated with FBS overnight at 4°C.

2.4. Scanning Electron Microscopy (SEM)

Synovial MSCs () were suspended in 500 μL αMEM with 10% FBS and plated on PLA films in a 24-well plate. After 2 h, the films were fixed in 2.5% glutaraldehyde (TAAB Laboratories and Equipment Ltd., Berks, England) for 2 h and washed overnight in 0.1 M PBS at 4°C. Each film specimen was then postfixed with 1% osmium tetroxide (TAAB Laboratories and Equipment Ltd.) for 2 h at 4°C and dehydrated in graded ethanol solutions (Fujifilm Wako Pure Chemical Corporation). After exchanging with 3-methyl butyl acetate (Fujifilm Wako Pure Chemical Corporation) and critical point drying, the specimen was coated with platinum and the surface was observed by SEM (S-4500, Hitachi Ltd., Tokyo, Japan) [18].

2.5. Surface Markers

Synovial MSCs () at passage 3 in 500 μL αMEM containing 10% FBS were dropped onto films in the wells of a 24-well plate. A 1 mL volume of αMEM containing 10% FBS was added, and the cells were incubated for 24 h at 37°C and 5% CO₂. Adherent cells were then detached by treating with 0.25% trypsin-EDTA for 5 min. The cells were suspended in Hank’s balanced salt solution (HBSS, Thermo Fisher Scientific) at a density of and treated for 30 minutes on ice with antibodies for CD14, CD29 (integrin β1), CD31, CD44, CD45, CD49c (integrin α3), CD49f (integrin α6), CD51/CD61 (integrin αvβ3), CD61, CD73, CD106, and CD146 (all from BD). The data were analyzed by FACS Verse (BD) and FlowJo software (Tree Star Inc., OR, USA). Cells positively stained with Ghost Dye Violet 510 (Tonbo Biosciences, CA, USA) were removed as dead cells. Isotype controls were prepared as negative controls (BD). The expressions of CD29, CD49c, CD49f, and CD51/CD61 by cells seeded on plastic dishes (just before seeding on the film) were examined in the same manner.

2.6. Quantitative Evaluation of Adherent Cells

Synovial MSCs were stained with DiI (Thermo Fisher Scientific) and synovial MSCs suspended in 500 μL αMEM with 10% FBS were plated on the PLA films in a 24-well plate. After 24 h, the films and plates were fixed with 10% neutral formalin (Fujifilm Wako Pure Chemical Corporation). The MSCs remaining on the PLA films and the MSCs passing through the film to the bottom of the plates were observed, and the numbers of the cells were counted from the images obtained with a microscope analysis system (BZ-X810, KEYENCE, Osaka, Japan). Partial images of area of film and a area of bottom were taken at 4x magnification of the objective lens and automatically combined using software (BZ-X analyzer, KEYENCE). The regions with a fluorescence intensity above a fixed value within the film or on the bottom were defined as cells, and the number of regions was counted using imaging software (BZ-X analyzer). The numbers of nonadherent cells were calculated from the numbers of adherent cells on film and bottoms.

2.7. In Vitro Cartilage Formation of MSCs Plated on PLA Films

A 500 μL volume of αMEM with 10% FBS containing synovial MSCs was dropped onto films in the wells of a 24-well plate. A further 1 mL αMEM with 10% FBS was added, and the cells were incubated for 24 h. The medium was then switched to chondrogenic induction medium (this was considered time 0). The medium was exchanged every 1–3days.

2.8. Time-Lapse Images

Synovial MSCs seeded on PLA films were observed with a microscope (EVOS XL Core Cell Imaging System, Thermo Fisher Scientific) at time 0, 1, 3, and 5 days. The film and cell sheet areas at each time point were defined manually using ImageJ software (National Institutes of Health, MD, USA), and the area ratio was calculated.

2.9. Histology

Synovial MSCs seeded on PLA films were washed with PBS, fixed in 4% paraformaldehyde (PFA, Fujifilm Wako Pure Chemical Corporation) at 4°C for 1 h, and embedded in 2% agarose gel (Fujifilm Wako Pure Chemical Corporation). The framework of the PLA film was then removed, and the cylindrical agarose gel holding the PLA film was embedded in paraffin, sliced, stained with safranin-o/fast green (Fujifilm Wako Pure Chemical Corporation), and observed with a microscope (BZ-X810).

The cartilage thickness was measured by drawing a single line along the long axis of the cartilage, determining the midpoint of both ends of the cartilage on that line, and then drawing seven perpendicular lines 500 μm on both sides of that midpoint. The midpoints of both ends of the cartilage were determined on each vertical line, and the minimum width through these points was determined. Finally, an average thickness of the cartilage and the coefficient of variance for cartilage thickness at 7 points were calculated using ImageJ.

2.10. Statistical Analysis

The Shapiro-Wilk test was used to confirm the normality of the data (). The analysis between the two groups were calculated by a paired Student’s test. Cell counts and time courses were statistically analyzed by two-way analysis of variance (ANOVA) with Tukey’s multiple comparisons test using GraphPad Prism 8 software (GraphPad Software, CA, USA). All statistical analysis methods are described in the figure legends. Two-tailed values of <0.05 were considered statistically significant.

3. Results

3.1. SEM Images of Honeycomb PLA Films after Plating MSCs

Synovial MSCs showed multipotency for chondrogenesis, adipogenesis, and calcification (Figure 1). At 2 h after plating onto the film without pores (0 μm), MSCs showed extended pseudopodia and attachment to the film (Figure 2(a)). MSCs on the 5 μm pore film also showed pseudopodia that extended and adhered to several pores. MSCs on the 20 μm pore film showed submergence of the cell body into the pore and pseudopodia extending around the pore.

(a)

(b)

(c)

Figure 2

SEM images and surface markers of synovial MSCs plated onto honeycomb films. (a) SEM images of honeycomb PLA films after plating synovial MSCs. Synovial MSCs ( in 500 μL medium) were plated on PLA films without pores (0 μm) or with 5 μm and 20 μm pores and observed from above after 2 h. Representative pseudopodia are indicated with yellow arrows. (b) Surface markers of synovial MSCs one day after seeding onto the film. Means and standard deviations are shown (). (c) Surface markers of synovial MSCs before and one day after seeding onto 0 μm film. . values were determined by paired Student’s test.

3.2. Surface Markers of Synovial MSCs Plated onto Honeycomb Films

One day after seeding onto films with pore sizes of 0, 5, and 20 μm, the MSCs in each film expressed 100% of the positive MSC markers CD44, CD73, and CD90, and less than 5% of the negative MSC markers CD14, CD45, CD106, and CD146 (Figure 2(b)). The expression of the four different integrins in MSCs did not differ among the films, but the expression of integrin α6 was significantly lower in MSCs on films than in MSCs cultured in plastic dishes (Figure 2(c)).

3.3. MSC Numbers Remaining in and Passing through Films

One day after seeding the MSCs (Figure 3(a)), fewer cells were observed in the film without pores than in the films with pores, and more cells were observed in the bottom of the dish containing the film with 20 μm pores than dishes containing the other film types (Figure 3(b)). The number of cells on the film with no pores was , which was significantly lower than the cell number of for the 5 μm pore film or cells for the 20 μm pore film (Figure 3(c)). The number of cells on the bottom was essentially 0 cells for both the film with no pores and the 5 μm pore film, which was significantly lower than cells noted for the 20 μm pore film. The number of cells not adhered to the film or the bottom of the dish was cells for the film with no pores and was significantly higher than the cells obtained with the 5 μm pore film. The value was also significantly higher than cells obtained with the 20 μm pore film.

Figure 3

Analysis of numbers of synovial MSCs remaining in and passing through PLA films. (a) Experimental setting. (b) Images of MSCs remaining on PLA films and MSCs passing to the bottoms of the plates. DiI-stained cells were observed from above and image processed and are shown in blue. (c) Quantitative evaluation of cell numbers on the films, on the bottoms of the dishes, and nonadherent cells. Means and standard deviations are shown (). . values were determined by one-way ANOVA with Tukey’s multiple comparisons test.

3.4. The Early Phase of Cartilage Formation

During in vitro cartilage formation by MSCs, the cell sheet formed by the plated MSCs peeled off the film without pores at one day, assumed a round shape at three days, and was maintained as a cartilage mass at five days (Figure 4(a)). By contrast, the cell sheets formed by MSCs plated on the 5 and 20 μm pore films remained sheet-like and did not peel off the film. Quantitative evaluation showed that the area of the sheet of MSCs plated on the film without pores significantly decreased to at 1 day, while the area of the sheet of MSCs plated on the film with 5 and 20 μm pores was maintained at 100% for 5 days (Figure 4(b)).

(a)

(b)

3.5. Effect of Pore Size of the PLA Film on Cartilage Formation

Synovial MSCs were plated on the three types of PLA films, cultured in the chondrogenic induction medium for two weeks, and then observed histologically (Figure 5(a)). MSCs plated on all three PLA films produced extracellular matrix, as confirmed by red staining with safranin O and they formed cartilage. The MSCs plated on the films without pores were spherical in shape, whereas the MSCs plated on the films with pores were sheet-like. The thickness of the sheet-like cartilage formed by MSCs plated on 5 μm pore film (Figure 5(b)) was and was significantly thicker than the thick sheet-like cartilage formed by plating MSCs on the 20 μm pore film (Figure 5(c)). The coefficient of variance for thickness of sheet-like cartilage measured at seven different points was for MSCs seeded on 5 μm pore film and was significantly lower than the thickness measured for MSCs seeded on the 20 μm pore film. This suggests the formation of a more even cartilage by MSCs seeded on 5 μm pore film than on 20 μm pore film.

(a)

(b)

(c)

Figure 5

Histological images and thickness of cartilage derived from synovial MSCs plated on PLA films. (a) Histological images. MSCs ( in 500 μL medium) were plated, cultured in chondrogenic induction medium for 14 days, and stained with safranin O. The results of three different samples are shown. (b) Method for measuring the cartilage thickness. A single line was drawn along the long axis of the cartilage, the midpoint of both ends of the cartilage was determined on this line (point A), and seven perpendicular lines were drawn every 500 μm on both sides from “point A.” The midpoints of both ends of the cartilage were determined on each vertical line (M1-M7), and the minimum width through these points was determined. (c) Average thickness of the cartilage and the coefficient of variance for cartilage thickness at 7 points. Means and standard deviations are shown (). . values were determined by a paired Student’s test.

3.6. Cartilage Formation of MSCs Plated on 5 μm Pore PLA Films

Synovial MSCs plated on 5 μm pore PLA films and cultured in the chondrogenic induction medium for three weeks showed multilayered cells above the film and a small number of cells below the film (Figure 6). A few layers of cells were observed above and below the film and a slight cartilage matrix was produced at one week, and the thickness of the cartilage increased at two weeks and further increased to 300–500 μm at 3 weeks. The thickness ratio of the cartilage above and below the film was approximately 3 : 1.

4. Discussion

Synovial MSCs seeded on PLA films without pores exhibited extended pseudopodia. Some reports have indicated that the pseudopodia perform the function of cell adhesion [18, 19]; however, in the present study, the number of adherent cells was on the film without pores was only about one third of the number on the PLA films with pores. This finding does not mean that the pseudopodia of synovial MSCs have no ability to adhere to films without pores; rather, it means that the pseudopodia of synovial MSCs are not sufficiently adhesive to withstand removal of the film from the dish, fixation of the cells with formalin, and microscopy observation. In other words, pores of a suitable size are useful to ensure efficient functioning of the pseudopodia.

The expression of surface markers by the synovial MSCs that adhered to the film did not differ with the presence or size of the pores, but the expression of integrin α6 was reduced compared to cells cultured on plastic dishes. The PLA film we used is a thin sheet of less than 10 μm thickness and has softer physical properties than a plastic dish. The expression level of integrin α6 might be altered when MSCs adhere to soft PLA materials, since the expression levels of other integrins depend on mechanosensing of the rigidity of the materials by the adhering cells [20–24].

Chondrogenic induction was observed in MSCs plated on the PLA films without pores, but the cell sheet peeled off from the films after one day and formed a spherical cartilage mass after two weeks. The ascorbate-2-phosphate contained in the chondrogenic induction medium promotes the production of extracellular matrix and the aggregation of MSCs [25]. The observation of peeling of the cell sheets from the films during the process of cartilage formation indicates that the strength of aggregation of the MSCs is greater than the strength of adhesion of the MSCs to the PLA films without pores.

MSCs plated on 5 μm pore films formed the thickest cartilage among the three types of films used in this study. This is because the MSCs did not fall through the pores after plating; instead, they firmly adhered to the pores via their pseudopodia. This firm adhesion prevented the cells from peeling off after chondrogenic differentiation. The chondrogenic differentiation of MSCs using scaffolds is affected by the size of the scaffold pores [26, 27]. In the current study, the film with the 5 μm pore size was the best of the three tested films for cartilage formation by synovial MSCs under the conditions used here. MSCs seeded on 20 μm pore films formed thinner and more uneven cartilage compared to MSCs seeded on 5 μm pore films. The number of cells that adhered to the film one day after seeding was the same, but the number of cells that passed through the film and fell to the bottom was higher for the 20 μm pore films.

Although the MSCs extended their pseudopodia and were caught in the pores, some of the cells passed through the 20 μm pores, probably because the MSC body is less than 20 μm in diameter [28] and therefore smaller than the pores. One possibility why the thickness and smoothness of the cartilage formed at 2 weeks differed between the films with 5 μm and 20 μm pores, even though the number of cells remaining in the film at 1 day was the same, might be that cells fell through the 20 μm pores from 1 day to 2 weeks after seeding, especially in the early period before the cartilage matrix was fully formed.

The pore size in honeycomb films can be adjusted in a range from several tens of nanometers to tens of micrometers by controlling the template water droplets by the breath figure method. The honeycomb films have the added advantage of forming uniformly sized pores when compared to conventional porous scaffolds with size-distributed pores [11]. The pore sizes reported for honeycomb films have been found suitable for proliferation and function of endothelial cells [29], myocytes [30], and hepatocytes [31]. Kawano et al. compared PLA honeycomb films with 1.6 μm, 3.2 μm, and 4.7 μm pores and reported that the number of adherent bone marrow MSCs increased as the pore size increased [32]. This finding concurred with our results and suggests that a suitable pore size for MSC adhesion to a PLA honeycomb film is approximately 5 μm.

One limitation of our study is that we did not conduct in vivo investigations of the effectiveness of implanting honeycomb PLA films plated with MSCs into cartilage defects. Therefore, we cannot say at this time whether cartilage defects will be repaired when transplanted with undifferentiated MSCs adhering to 5 μm pore honeycomb PLA films or whether the MSCs will require further ex vivo differentiation into cartilage sheets. We also do not know whether the PLA film will be absorbed after implantation, or when this will occur. Another point that requires clarification is whether a PLA film will be recognized as a foreign substance in the joint and cause inflammation.

We compared in vitro cartilage sheet formation by synovial MSCs using honeycomb PLA films with 0, 5, and 20 μm pores. MSCs on the 5 μm pore film showed pseudopodia that extended out to several pores. MSCs on the 20 μm pore film showed cell bodies submerged in the pores. MSCs plated on 5 μm pore films formed the thickest and most even cartilage layer among the three types of films. Honeycomb PLA films with 5 μm pores were therefore considered suitable for in vitro cartilage formation by synovial MSCs.

Abbreviations

PLA:	Polylactic acid
MSCs:	Mesenchymal stem cells.

Data Availability

The datasets used and/or analyzed during the current study are available from the corresponding author on reasonable request.

Ethical Approval

All methods were carried out in accordance with relevant guidelines and regulations. All procedures performed in the study involving human participants were in accordance with the Declaration of Helsinki. This study was approved by the Medical Research Ethics Committee of Tokyo Medical and Dental University (M2017-142).

Informed consent was obtained from all study subjects.

Conflicts of Interest

The authors declare that they have no competing interests.

Authors’ Contributions

MY performed the experiments, data collection, and rough draft writing; MM performed the experiments, data collection, and draft writing; RF performed the experiments and data collection; HKa, KE, NO, and HKo are responsible for the project administration; YS is responsible for the scanning electron microscopy; IS is responsible for the conceptualization, supervision, and final writing. All authors reviewed and approved the manuscript.

Acknowledgments

Honeycomb PLA films were provided by Fujifilm. We thank Takahiro Oba, Kenichi Yasuda, and Fumikazu Sato at Fujifilm for providing the honeycomb film production. We also thank Ms. Ellen Roider for proofreading the manuscript. This study was supported by the JSPS KAKENHI grant number JP18K09095 to HKa.

References

J. C. Bernhard and G. Vunjak-Novakovic, “Should we use cells, biomaterials, or tissue engineering for cartilage regeneration?” Stem Cell Research & Therapy, vol. 7, no. 1, p. 56, 2016.
View at: Publisher Site | Google Scholar
P. Niemeyer, D. Albrecht, S. Andereya et al., “Autologous chondrocyte implantation (ACI) for cartilage defects of the knee: A guideline by the working group "Clinical Tissue Regeneration" of the German Society of Orthopaedics and Trauma (DGOU),” The Knee, vol. 23, no. 3, pp. 426–435, 2016.
View at: Publisher Site | Google Scholar
A. Yamashita, M. Morioka, Y. Yahara et al., “Generation of scaffoldless hyaline cartilaginous tissue from human iPSCs,” Stem Cell Reports, vol. 4, no. 3, pp. 404–418, 2015.
View at: Publisher Site | Google Scholar
Y. Sakaguchi, I. Sekiya, K. Yagishita, and T. Muneta, “Comparison of human stem cells derived from various mesenchymal tissues: superiority of synovium as a cell source,” Arthritis & Rheumatism, vol. 52, no. 8, pp. 2521–2529, 2005.
View at: Publisher Site | Google Scholar
C. De Bari and A. J. Roelofs, “Stem cell-based therapeutic strategies for cartilage defects and osteoarthritis,” Current Opinion in Pharmacology, vol. 40, pp. 74–80, 2018.
View at: Publisher Site | Google Scholar
A. R. Armiento, M. J. Stoddart, M. Alini, and D. Eglin, “Biomaterials for articular cartilage tissue engineering: learning from biology,” Acta Biomaterialia, vol. 65, pp. 1–20, 2018.
View at: Publisher Site | Google Scholar
D. da Silva, M. Kaduri, M. Poley et al., “Biocompatibility, biodegradation and excretion of polylactic acid (PLA) in medical implants and theranostic systems,” Chemical Engineering Journal, vol. 340, pp. 9–14, 2018.
View at: Publisher Site | Google Scholar
A. Grémare, V. Guduric, R. Bareille et al., “Characterization of printed PLA scaffolds for bone tissue engineering,” Journal of Biomedical Materials Research Part A, vol. 106, no. 4, pp. 887–894, 2018.
View at: Publisher Site | Google Scholar
K. Kim, M. Yu, X. Zong et al., “Control of degradation rate and hydrophilicity in electrospun non-woven poly(d,l-lactide) nanofiber scaffolds for biomedical applications,” Biomaterials, vol. 24, no. 27, pp. 4977–4985, 2003.
View at: Publisher Site | Google Scholar
Y. Fukuhira, E. Kitazono, T. Hayashi et al., “Biodegradable honeycomb-patterned film composed of poly(lactic acid) and dioleoylphosphatidylethanolamine,” Biomaterials, vol. 27, no. 9, pp. 1797–1802, 2006.
View at: Publisher Site | Google Scholar
H. Yabu, “Fabrication of honeycomb films by the breath figure technique and their applications,” Science and Technology of Advanced Materials, vol. 19, no. 1, pp. 802–822, 2018.
View at: Publisher Site | Google Scholar
H. Yamazaki, K. Ito, H. Yabu, and M. Shimomura, “Formation and control of line defects caused by tectonics of water droplet arrays during self-organized honeycomb-patterned polymer film formation,” Soft Matter, vol. 10, no. 16, p. 2741, 2014.
View at: Publisher Site | Google Scholar
W H Organization, “World Medical Association Declaration of Helsinki,” Jama, vol. 310, no. 20, 2013.
View at: Publisher Site | Google Scholar
M. Mizuno, H. Katano, Y. Shimozaki et al., “Time-lapse image analysis for whole colony growth curves and daily distribution of the cell number per colony during the expansion of mesenchymal stem cells,” Scientific Reports, vol. 9, no. 1, p. 16835, 2019.
View at: Publisher Site | Google Scholar
M. Mizuno, H. Katano, Y. Mabuchi et al., “Specific markers and properties of synovial mesenchymal stem cells in the surface, stromal, and perivascular regions,” Stem Cell Research & Therapy, vol. 9, no. 1, p. 123, 2018.
View at: Publisher Site | Google Scholar
R. Fujisawa, M. Mizuno, H. Katano et al., “Cryopreservation in 95% serum with 5% DMSO maintains colony formation and chondrogenic abilities in human synovial mesenchymal stem cells,” BMC Musculoskeletal Disorders, vol. 20, no. 1, p. 316, 2019.
View at: Publisher Site | Google Scholar
Y. Kohno, M. Mizuno, N. Ozeki et al., “Comparison of mesenchymal stem cells obtained by suspended culture of synovium from patients with rheumatoid arthritis and osteoarthritis,” BMC Musculoskeletal Disorders, vol. 19, no. 1, p. 78, 2018.
View at: Publisher Site | Google Scholar
S. Suzuki, M. Mizuno, Y. Sakamaki et al., “Morphological changes in synovial mesenchymal stem cells during their adhesion to the meniscus,” Laboratory Investigation, vol. 100, no. 7, pp. 916–927, 2020.
View at: Publisher Site | Google Scholar
J. C. Adams, “Cell-matrix contact structures,” Cellular and Molecular Life Sciences, vol. 58, no. 3, pp. 371–392, 2001.
View at: Publisher Site | Google Scholar
A. Elosegui-Artola, E. Bazellières, M. D. Allen et al., “Rigidity sensing and adaptation through regulation of integrin types,” Nature Materials, vol. 13, no. 6, pp. 631–637, 2014.
View at: Publisher Site | Google Scholar
P. H. Krebsbach and L. G. Villa-Diaz, “The role of integrin α6 (CD49f) in stem cells: more than a conserved biomarker,” Stem Cells and Development, vol. 26, no. 15, pp. 1090–1099, 2017.
View at: Publisher Site | Google Scholar
H. Lv, L. Li, M. Sun et al., “Mechanism of regulation of stem cell differentiation by matrix stiffness,” Stem Cell Research & Therapy, vol. 6, no. 1, 2015.
View at: Publisher Site | Google Scholar
N. Strohmeyer, M. Bharadwaj, M. Costell, R. Fässler, and D. J. Müller, “Fibronectin-bound α5β1 integrins sense load and signal to reinforce adhesion in less than a second,” Nature Materials, vol. 16, no. 12, pp. 1262–1270, 2017.
View at: Publisher Site | Google Scholar
A. van Wijnen, R. Olivares-Navarrete, E. M. Lee et al., “Substrate stiffness controls osteoblastic and chondrocytic differentiation of mesenchymal stem cells without exogenous stimuli,” Plos One, vol. 12, no. 1, 2017.
View at: Publisher Site | Google Scholar
W. Ando, K. Tateishi, D. Katakai et al., “In vitro generation of a scaffold-free tissue-engineered construct (TEC) derived from human synovial mesenchymal stem cells: biological and mechanical properties and further chondrogenic potential,” Tissue Engineering Part A, vol. 14, no. 12, pp. 2041–2049, 2008.
View at: Publisher Site | Google Scholar
A. Matsiko, J. P. Gleeson, and F. J. O'Brien, “Scaffold mean pore size influences mesenchymal stem cell chondrogenic differentiation and matrix deposition,” Tissue Engineering Part A, vol. 21, article 3-4, pp. 486–497, 2015.
View at: Publisher Site | Google Scholar
C. M. Murphy, M. G. Haugh, and F. J. O'Brien, “The effect of mean pore size on cell attachment, proliferation and migration in collagen-glycosaminoglycan scaffolds for bone tissue engineering,” Biomaterials, vol. 31, no. 3, pp. 461–466, 2010.
View at: Publisher Site | Google Scholar
M. Mizuno, H. Katano, K. Otabe et al., “Complete human serum maintains viability and chondrogenic potential of human synovial stem cells: suitable conditions for transplantation,” Stem Cell Research & Therapy, vol. 8, no. 1, p. 144, 2017.
View at: Publisher Site | Google Scholar
S. Yamamoto, M. Tanaka, H. Sunami et al., “Effect of honeycomb-patterned surface topography on the adhesion and signal transduction of porcine aortic endothelial cells,” Langmuir, vol. 23, no. 15, pp. 8114–8120, 2007.
View at: Publisher Site | Google Scholar
K. Arai, M. Tanaka, S. Yamamoto, and M. Shimomura, “Effect of pore size of honeycomb films on the morphology, adhesion and cytoskeletal organization of cardiac myocytes,” Colloids and Surfaces A: Physicochemical and Engineering Aspects, vol. 313-314, pp. 530–535, 2008.
View at: Publisher Site | Google Scholar
M. Tanaka, K. Nishikawa, H. Okubo et al., “Control of hepatocyte adhesion and function on self-organized honeycomb- patterned polymer film,” Colloids and Surfaces A: Physicochemical and Engineering Aspects, vol. 284-285, pp. 464–469, 2006.
View at: Publisher Site | Google Scholar
T. Kawano, M. Sato, H. Yabu, and M. Shimomura, “Honeycomb-shaped surface topography induces differentiation of human mesenchymal stem cells (hMSCs): uniform porous polymer scaffolds prepared by the breath figure technique,” Biomater. Sci., vol. 2, no. 1, pp. 52–56, 2014.
View at: Publisher Site | Google Scholar

Copyright

Copyright © 2021 Misaki Yagi et al. This is an open access article distributed under the Creative Commons Attribution License, which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.

PDF Download Citation

Download other formats

Order printed copies

Views

616

Downloads

593

Citations