In this study, gradual and sudden reduction methods were combined to simulate a progressive failure in notched composite plates using a macro mechanics approach. Using the presented method, a progressive failure is simulated based on a linear softening law prior to a catastrophic failure, and thereafter, sudden reduction methods are employed for modeling a progressive failure. This combination method significantly reduces the computational cost and is also capable of simultaneously predicting the first and last ply failures (LPFs) in composite plates. The proposed method is intended to predict the first ply failure (FPF), LPF, and dominant failure modes of carbon/epoxy and glass/epoxy notched composite plates. In addition, the effects of mechanical properties and different stacking sequences on the propagation of damage in notched composite plates were studied. The results of the presented method were compared with experimental data previously reported in the literature. By comparing the numerical and experimental data, it is revealed that the proposed method can accurately simulate the failure propagation in notched composite plates at a low computational cost.
Similar content being viewed by others
References
Cárdenas D, Elizalde H, Marzocca P, Abdi F, Minnetyan L, Probst O. Progressive failure analysis of thin-walled composite structures. Composite Structures, 2013, 95: 53–62
Rafiee R, Torabi M A. Stochastic prediction of burst pressure in composite pressure vessels. Composite Structures, 2018, 185: 573–583
Irisarri F X, Laurin F, Carrere N, Maire J F. Progressive damage and failure of mechanically fastened joints in CFRP laminates—Part II: Failure prediction of an industrial junction. Composite Structures, 2012, 94(8): 2278–2284
Jordan J B, Naito C J, Haque B Z. Progressive damage modeling of plain weave E-glass/phenolic composites. Composites. Part B, Engineering, 2014, 61: 315–323
Lee C S, Kim J H, Kim S, Ryu D M, Lee J M. Initial and progressive failure analyses for composite laminates using Puck failure criterion and damage-coupled finite element method. Composite Structures, 2015, 121: 406–419
Fakoor M, Mohammad Navid Ghoreishi S. Experimental and numerical investigation of progressive damage in composite laminates based on continuum damage mechanics. Polymer Testing, 2018, 70: 533–543
Vo-Duy T, Nguyen-Minh N, Dang-Trung H, Tran-Viet A, Nguyen-Thoi T. Damage assessment of laminated composite beam structures using damage locating vector (DLV) method. Frontiers of Structural and Civil Engineering, 2015, 9(4): 457–465
Fakoor M, Ghoreishi S M N, Khansari N M. Investigation of composite coating effectiveness on stress intensity factors of cracked composite pressure vessels. Journal of Mechanical Science and Technology, 2016, 30(7): 3119–3126
Fakoor M, Ghoreishi S M N. Verification of a micro-mechanical approach for the investigation of progressive damage in composite laminates. Acta Mechanica, 2019, 230(1): 225–241
Matzenmiller A, Lubliner J, Taylor R. A constitutive model for anisotropic damage in fiber-composites. Mechanics of Materials, 1995, 20(2): 125–152
Hamdia K M, Silani M, Zhuang X, He P, Rabczuk T. Stochastic analysis of the fracture toughness of polymeric nanoparticle composites using polynomial chaos expansions. International Journal of Fracture, 2017, 206(2): 215–227
Vu-Bac N, Lahmer T, Zhuang X, Nguyen-Thoi T, Rabczuk T. A software framework for probabilistic sensitivity analysis for computationally expensive models. Advances in Engineering Software, 2016, 100: 19–31
Lapczyk I, Hurtado J A. Progressive damage modeling in fiber-reinforced materials. Composites. Part A, Applied Science and Manufacturing, 2007, 38(11): 2333–2341
Voyiadjis G Z, Taqieddin Z N, Kattan P I. Micromechanical approach to damage mechanics of composite materials with fabric tensors. Composites. Part B, Engineering, 2007, 38(7–8): 862–877
Nobeen N S, Zhong Y, Francis B A P, Ji X, Chia E S M, Joshi S C, Chen Z. Constituent materials micro-damage modeling in predicting progressive failure of braided fiber composites. Composite Structures, 2016, 145: 194–202
Praud F, Chatzigeorgiou G, Chemisky Y, Meraghni F. Hybrid micromechanical-phenomenological modelling of anisotropic damage and anelasticity induced by micro-cracks in unidirectional composites. Composite Structures, 2017, 182: 223–236
Barbero E, Cosso F, Roman R, Weadon T. Determination of material parameters for Abaqus progressive damage analysis of E-glass epoxy laminates. Composites. Part B, Engineering, 2013, 46: 211–220
Wang L, Zheng C, Luo H, Wei S, Wei Z. Continuum damage modeling and progressive failure analysis of carbon fiber/epoxy composite pressure vessel. Composite Structures, 2015, 134: 475–482
Papanikos P, Tserpes K, Labeas G, Pantelakis S. Progressive damage modelling of bonded composite repairs. Theoretical and Applied Fracture Mechanics, 2005, 43(2): 189–198
Areias P, Msekh M, Rabczuk T. Damage and fracture algorithm using the screened Poisson equation and local remeshing. Engineering Fracture Mechanics, 2016, 158: 116–143
Areias P, Reinoso J, Camanho P, César de Sá J C, Rabczuk T. Effective 2D and 3D crack propagation with local mesh refinement and the screened Poisson equation. Engineering Fracture Mechanics, 2018, 189: 339–360
Areias P, Rabczuk T, Msekh M. Phase-field analysis of finite-strain plates and shells including element subdivision. Computer Methods in Applied Mechanics and Engineering, 2016, 312: 322–350
Areias P, Rabczuk T, Camanho P. Finite strain fracture of 2D problems with injected anisotropic softening elements. Theoretical and Applied Fracture Mechanics, 2014, 72: 50–63
Areias P, Rabczuk T, Dias-da-Costa D. Element-wise fracture algorithm based on rotation of edges. Engineering Fracture Mechanics, 2013, 110: 113–137
Areias P, Rabczuk T. Steiner-point free edge cutting of tetrahedral meshes with applications in fracture. Finite Elements in Analysis and Design, 2017, 132: 27–41
Rabczuk T, Belytschko T. Cracking particles: A simplified meshfree method for arbitrary evolving cracks. International Journal for Numerical Methods in Engineering, 2004, 61(13): 2316–2343
Rabczuk T, Belytschko T. A three-dimensional large deformation meshfree method for arbitrary evolving cracks. Computer Methods in Applied Mechanics and Engineering, 2007, 196(29–30): 2777–2799
Rabczuk T, Zi G, Bordas S, Nguyen-Xuan H. A simple and robust three-dimensional cracking-particle method without enrichment. Computer Methods in Applied Mechanics and Engineering, 2010, 199(37–40): 2437–2455
Moure M, Otero F, García-Castillo S, Sánchez-Sáez S, Barbero E, Barbero E. Damage evolution in open-hole laminated composite plates subjected to in-plane loads. Composite Structures, 2015, 133: 1048–1057
Su Z, Tay T, Ridha M, Chen B. Progressive damage modeling of open-hole composite laminates under compression. Composite Structures, 2015, 122: 507–517
Chang F K, Lessard L B. Damage tolerance of laminated composites containing an open hole and subjected to compressive loadings: Part I—Analysis. Journal of Composite Materials, 1991, 25(1): 2–43
Hashin Z, Rotem A. A fatigue failure criterion for fiber reinforced materials. Journal of Composite Materials, 1973, 7(4): 448–464
Tsai S W, Wu E M. A general theory of strength for anisotropic materials. Journal of Composite Materials, 1971, 5(1): 58–80
Sun C, Tao J. Prediction of failure envelopes and stress/strain behaviour of composite laminates1. Composites Science and Technology, 1998, 58(7): 1125–1136
Puck A, Kopp J, Knops M. Guidelines for the determination of the parameters in Puck’s action plane strength criterion. Composites Science and Technology, 2002, 62(3): 371–378
Cuntze R, Freund A. The predictive capability of failure mode concept-based strength criteria for multidirectional laminates. Composites Science and Technology, 2004, 64(3–4): 343–377
He P, Shen Y, Gu Y, Shen P. 3D fracture modelling and limit state analysis of prestressed composite concrete pipes. Frontiers of Structural and Civil Engineering, 2019, 13(1): 165–175
Nali P, Carrera E. A numerical assessment on two-dimensional failure criteria for composite layered structures. Composites. Part B, Engineering, 2012, 43(2): 280–289
Yang B, Yue Z, Geng X, Wang P, Gan J, Liao B. Effects of space environment temperature on the mechanical properties of carbon fiber/bismaleimide composites laminates. Proceedings of the Institution of Mechanical Engineers. Part G, Journal of Aerospace Engineering, 2018, 232(1): 3–16
Liu P, Zheng J. Recent developments on damage modeling and finite element analysis for composite laminates: A review. Materials & Design, 2010, 31(8): 3825–3834
Catalanotti G, Camanho P, Marques A. Three-dimensional failure criteria for fiber-reinforced laminates. Composite Structures, 2013, 95: 63–79
Weng J, Wen W, Zhang H. Study on low-velocity impact and residual strength at high temperatures of composite laminates. Proceedings of the Institution of Mechanical Engineers, Part G: Journal of Aerospace Engineering. 2017, 233(3): 1106–1123
Maimí P, Camanho P P, Mayugo J, Dávila C. A continuum damage model for composite laminates: Part I—Constitutive model. Mechanics of Materials, 2007, 39(10): 897–908
Baaran J, Kärger L, Wetzel A. Efficient prediction of damage resistance and tolerance of composite aerospace structures. Proceedings of the Institution of Mechanical Engineers, Part G, Journal of Aerospace Engineering, 2008, 222(2): 179–188
Zhang B, Zhao L. Progressive damage and failure modeling in fiber-reinforced laminated composites containing a hole. International Journal of Damage Mechanics, 2012, 21(6): 893–911
Zhang X. Impact damage in composite aircraft structures-experimental testing and numerical simulation. Proceedings of the Institution of Mechanical Engineers. Part G, Journal of Aerospace Engineering, 1998, 212(4): 245–259
Liu P F, Zheng J. Progressive failure analysis of carbon fiber/epoxy composite laminates using continuum damage mechanics. Materials Science and Engineering A, 2008, 485(1–2): 711–717
Mills A, Jones J. Investigation, manufacture, and testing of damage-resistant airframe structures using low-cost carbon fibre composite materials and manufacturing technology. Proceedings of the Institution of Mechanical Engineers. Part G, Journal of Aerospace Engineering, 2010, 224(4): 489–497
Liu P F, Chu J, Hou S, Xu P, Zheng J. Numerical simulation and optimal design for composite high-pressure hydrogen storage vessel: A review. Renewable & Sustainable Energy Reviews, 2012, 16(4): 1817–1827
Bažant Z P, Pfeiffer P A. Determination of fracture energy from size effect and brittleness number. ACI Materials Journal, 1987, 84(6): 463–480
Lange F, Radford K. Fracture energy of an epoxy composite system. Journal of Materials Science, 1971, 6(9): 1197–1203
Bažant Z P, Kazemi M T. Determination of fracture energy, process zone longth and brittleness number from size effect, with application to rock and conerete. International Journal of Fracture, 1990, 44(2): 111–131
Guide AMUs. Engineering Data User’s Guide. Material Data, Mechanical Material Curve Fitting. Los Angeles: ANSYS, Inc., 2017
Hibbitt H, Karlsson B, Sorensen P. Abaqus Analysis User’s Manual Version 6.10. Providence, RI: Dassault Systèmes Simulia Corp, 2011
Duvant G, Lions J L. Inequalities in Mechanics and Physics. Berlin: Springer Science & Business Media, 2012
Wisnom M, Hallett S, Soutis C. Scaling effects in notched composites. Journal of Composite Materials, 2010, 44(2): 195–210
Acknowledgements
The authors would like to acknowledge the financial support of Iran’s National Elites Foundation for this research under Grant number 15/19549.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Ghoreishi, S.M.N., Fakoor, M. & Azizi, A. Progressive failure analysis of notched composite plate by utilizing macro mechanics approach. Front. Struct. Civ. Eng. 15, 623–642 (2021). https://doi.org/10.1007/s11709-021-0726-8
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11709-021-0726-8