Facile Synthesis of Hollow MgO Spheres and Their Fluoride Adsorption Properties

Zhang, Yong; Jin, Zhen; Min-He, Liao; Guang-Song, Xu; Min-Da, Xu; Cheng, Hui; Huang, Jian

doi:https://doi.org/10.1155/2021/6655593

Advances in Condensed Matter Physics

On this page

Abstract Introduction Experimental Results and Discussion Conclusions Data Availability Conflicts of Interest Acknowledgments References Copyright Related Articles

Research Article | Open Access

Volume 2021 | Article ID 6655593 | https://doi.org/10.1155/2021/6655593

Facile Synthesis of Hollow MgO Spheres and Their Fluoride Adsorption Properties

Yong Zhang,¹Zhen Jin,²Liao Min-He,¹Xu Guang-Song,¹Xu Min-Da,²Hui Cheng,³and Jian Huang¹

Academic Editor: Markus R. Wagner

Received25 Dec 2020

Revised30 Mar 2021

Accepted09 May 2021

Published19 Jun 2021

Abstract

In the present work, the hollow MgO spheres were synthesized through a facile wet-chemistry method. X-ray diffraction, scanning electron microscopy, transmission electron microscopy, and energy dispersive spectrum are employed to characterize the as-prepared sample. Those results indicate that the average size of the as-prepared MgO hollow spheres is about 2 μm. Also, the MgO hollow spheres have the polycrystalline and porous structure, which would provide large specific surface area and plenty active sites for fluoride adsorption. The adsorption properties of the MgO hollow spheres towards fluoride are investigated. The fluoride adsorption kinetics of the MgO hollow spheres fits well the pseudo-second-order model. Also, the kinetic data revealed that the fluoride adsorption was rapid, more than 83% of fluoride could be removed within 40 min. The fluoride adsorption capacity of the hollow MgO spheres is larger than 182.4 mg/g at a pH of 7.0. The as-prepared products maintain excellent adsorption performance in the pH range of 3–11. In addition, the adsorption mechanism also has been discussed. From the FTIR results, a hydroxyl and carbonate coexchange mechanism is proposed. It is believed that the hollow MgO spheres are a potential candidate for fluoride removal.

1. Introduction

Excessive fluorine in drinking water is one of the world problems [1, 2]. Only in the concentration range of 0.5–1.0 mg/L, fluoride-contained water is good for human health [3]. However, when the concentration of fluorine goes beyond this range, long-term intake of the fluoride-excessive water would cause dental and skeletal fluorosis. Thus, the World Health Organization (WHO) classified fluoride as one of the contaminants in ground water [4]. Over 200 million people drink fluoride-excessive water every day [5]. Many methods have been developed to the remove the excessive fluoride from drinking water, such as precipitation [6], ion exchange [7, 8], nanofiltration [3, 9], reverse osmosis [10, 11], electrodialysis [12, 13], and adsorption [14,15]. Due to the low cost and simplicity of operation, adsorption seems to be the attractive one among those technologies [16, 17]. Various absorbents have been investigated for the fluoride removal [18–22]. For example, Zhang et al. applied bauxite in fluoride removal, the adsorption capacity of which is 1.775 mg/g [19]. Ku and Chiou studied the defluoride property of the alumina and found that the maximum fluoride removal capacity is 16.3 mg/g when pH = 5 [23]. However, the low adsorption capacity and narrow pH application range largely restrict the applications of those absorbents [24, 25]. Thus, developing novel fluoride adsorbents with high adsorption capacity, low price, and wide pH application range is very important.

Magnesium oxide (MgO), as a low-cost absorbent, is attractive in fluoride removal due to its strong affinity, high adsorption capacity, nontoxic nature, and limited solubility in water [22, 26, 27]. It is reported that the MgO absorbents can efficiently remove fluoride in wide pH range. Liu found that the fluoride adsorption capacity of pure MgO was 4.5 mg/g, and the adsorption performance remained stable in the pH range of 2–10 [28]. Maliyekkal also found that the MgO/Al₂O₃ composite can efficiently remove fluoride in the pH range of 3–10 [29]. However, the adsorption capacity of those absorbents is still limited. Many efforts have been taken to achieve high-performance MgO absorbents [30]. It is well accepted that the morphology can greatly affect the corresponding adsorption performance [31]. With the development of science and technology, nanostructures always exhibit better properties [32, 33]. Among various nanostructures, hollow and porous nanostructures always possess higher surface area, subsequently bringing more surface defects. Those defects can work as active sites and accordingly increase the adsorption property [34]. Thus, hollow and porous structures are favorable for absorbents. Many pioneer works reported that the hollow-structured MgO absorbents would exhibit better adsorption properties. Kuang et al. synthesized spherical-like MgO nanostructures by calcinate magnesium acetate, which exhibited high adsorption performance for metal ions [35]. Song prepared the hierarchical flower-like MgO hollow spheres extremely through a solvothermal method, which are the excellent arsenic absorbents [36]. However, those methods always require high temperature, high pressure, and complex operation. It is still a big challenge to obtain the MgO hollow absorbents through a simple method for high-performance fluoride removal. In the present work, the MgO hollow spheres were synthesized through a facile wet-chemical method. The operation temperature is as lower as 100°C, and high temperature, high pressure, and autoclave are no longer needed.

The as-prepared MgO hollow spheres are with the uniform sizes of 2 μm in average. Also, the MgO hollow spheres have the polycrystalline and porous structure, which would provide large specific surface area and plenty active sites for fluoride adsorption. The fluoride adsorption kinetics of the MgO hollow spheres fits well the pseudo-second-order model. Also, the kinetic data reveal that the fluoride adsorption was rapid, more than 83% of fluoride could be removed within 40 min. The MgO hollow spheres can efficiently remove fluoride at the condition of acid, neutral, and even weak alkaline. The adsorption capacity is over 182.4 mg/g at neutral condition. The fluoride adsorption mechanism of the absorbents is also investigated. It is found that, besides the hydroxyls, the surface carbonates formed during the synthesis process also can be exchanged with fluoride.

2. Experimental

2.1. Synthesis

All reagents were purchased from Sinopharm Chemical Reagent Co., Ltd. (China) with analytical grade. In the synthesis process, 1 g MgSO₄·7H₂O and 3 g urea were added into the mixed solution of 20 mL deionized water and vigorously stirred for 10 min. Then, the abovementioned solution was transferred into a 100 mL conical flask, sealed, and heated at 100°C for 720 min. After reaction, the white precipitate was collected by centrifugation. The resultant precipitate was washed and dried at 60°C. After annealing at 500°C for 4 h, the white MgO hollow spheres can be obtained.

2.2. Characterization

The morphologies of the samples were examined by field-emission scanning electron microscopy (FE-SEM; JEOL JSM-7500F) and high-resolution transmission electron microscopy (HRTEM; FEI Talos F200X). The crystal structure of the samples was determined by X-ray diffraction (XRD; Bruker D8) with Cu Kα radiation. The infrared spectrum of the samples was tested by Fourier-transform infrared spectrometer (FTIR; Thermo Scientific Nicolet 8700).

2.3. Adsorption Experiments

The fluoride stock solution with the concentration of 1000 ppm was prepared by dissolving NaF in deionized water and stored under dark conditions at 4°C. The fluoride standard solutions with different concentrations were prepared by rational dilution of the stock solution. The isotherm adsorption tests were carried out in a centrifuge tubes containing 10 mg absorbent and 10 mL fluoride solution. Then, the centrifuge tubes were shaked in a shaker at 25°C for 12 h. The pH value was not further adjusted. Then, the upper layer solution was carefully pipetted and filtered through a 0.45 μm filter for collection. The fluoride-ion-selective electrode PF-202-CF was applied to measure the residual fluoride concentration of the solution. The residual MgO hollow spheres were centrifuged, washed, and dried in an oven at 60°C.

In the kinetics test, the initial fluoride concentration was 10 mg/L, the dose of adsorbents was 1.0 g/L, and the volume of the fluoride solution was 100 mL. The samples were shaken at 150 rpm in the shaker at 25°C. At certain time, 6 mL of supernatant solutions was pipette and centrifuged for the remaining fluoride concentration determination.

In the experiment of pH effect on fluoride adsorption, the pH value was adjusted by HCl and NaOH solution. In the experiment of the coexisting anions’ effects on fluoride adsorption, the concentration of coexisting anions was set as 300 mg/g.

3. Results and Discussion

3.1. Characterization

Firstly, the morphology of the MgO hollow spheres was characterized by SEM. Figure 1(a) presents the SEM image of the MgO hollow spheres. It can be clearly seen that the MgO hollow spheres are with the uniform sizes of 2 μm in average. Figure 1(b) shows the high-resolution SEM images of the MgO hollow spheres. Obviously, the as-prepared MgO hollow spheres have rough external surface, which is probably due to the chaos accumulation of small nanoparticles. In the direction of the white arrow, the broken spheres can be clearly observed, and the hollow nature of MgO spheres is verified. During the experimental process, the precursors were firstly synthesized, and then, the MgO hollow spheres can be obtained after the heat treatment. Figure 1(c) presents the XRD patterns of the precursors and the final MgO hollow spheres. All peaks of the precursors can be indexed to Mg₅(CO₃)₄(OH)₂•(H₂O)₄ hydromagnesium (JCPDS 70-1177) [5]. After annealing at 600°C for 2 h in the air, the XRD pattern has totally changed, which can be indexed to (111), (200), and (220) planes of the hexagonal structure MgO (JCPDS card no. 89-4248). Also, no peak for precursor hydromagnesium can be identified, indicating that the precursor is fully decomposed to MgO. Figure 1(d) presents the representative EDS spectra of the MgO hollow spheres, and the molar ratio of Mg : O is 1 : 1.13, which is very close to the stoichiometry of MgO. The structure of the MgO hollow spheres is further investigated by TEM and SAED. Figure 2(a) is the typical TEM image of the MgO sphere. The contrast of the deep outside and shallow inside definitely confirmed the hollow structure of the product. The thickness of the shell is about 30 nm. Figure 2(b) is the high-magnification TEM image of the shell and reveals that the sphere is made up of huge number of nanoparticles. Moreover, there are many tiny mesopores on the shell, which is benefit to the adsorption performance of the product. From the HRTEM image presented in Figure 2(c), the fringe spacing of 0.24 nm can be ascribed to the (111) planes of the MgO. Figure 2(d) is the SAED pattern of the MgO spheres. A series of concentric rings with different radii can be seen, indicating the polycrystalline nature of the MgO hollow spheres.

(a)

(b)

(c)

(d)

(a)

(b)

(c)

(d)

3.2. Adsorption Properties

The fluoride adsorption performances of the MgO hollow spheres were systematically studied. Due to the hollow structure and porous surface, the as-prepared samples are expected with good adsorption properties. Figure 3(a) presents the fluoride adsorption kinetics of the MgO hollow spheres. It can be seen that the adsorption happens rapidly in the first 40 min, where over 83% of the fluoride ions can be adsorbed. Then, the adsorption capacity increases gradually until it reaches the equilibrium, where more than 95% of the fluoride ions can be removed by the MgO hollow spheres. To further quantify the changes of fluoride adsorption with time on the MgO hollow spheres, the Lagergren pseudo-first-order Model (1) [37] and Ho’s pseudo-second-order Model (2) [38] were used to simulate the kinetics.where q_e and q_t are the amounts of adsorbed fluoride at equilibrium and at any time t; k₁ and k₂ are the equilibrium rate constants for pseudo-first-order and pseudo-second-order sorption.

(a)

(b)

The adsorption kinetic experimental data fitted into the pseudo-second-order model are presented in Figure 3(b). Also, Table 1 shows the summarized results fitted by the pseudo-first-order and pseudo-second-order models. The higher correlation coefficient value of the pseudo-second-order model (R² = 0.998) indicates that the fluoride adsorption kinetics of the MgO hollow spheres fit well with the pseudo-second-order kinetics model. When the initial fluoride concentration is 10 mg/L, the equilibrium adsorption capacities (qe, cal) can be calculated as 9.54 mg/g, which is in agreement with experimental equilibrium adsorption capacities.

To further reveal the adsorption performance of the MgO hollow spheres, the fluoride adsorption isotherm is employed. The fluoride adsorption isotherm of the MgO hollow spheres is carried out at pH = 7.0, and the result is depicted in Figure 4(a). Obviously, when the concentration of the fluoride solution increases, the adsorption capacity of the MgO hollow spheres increases. The adsorption capacity of the spheres is 119.3 mg/g when the equilibrium concentration is 80.7 mg/g. As the equilibrium concentration increases, the adsorption capacity of the MgO hollow spheres is larger than 182.4 mg/g. Langmuir and Freundlich models are applied for data fitting, and the results are presented in Figures 4(b) and 4(c). Table 2 summarizes the isotherm parameters computed from the Langmuir and Freundlich models. The R² value of the Langmuir and Freundlich fitting model is 0.962 and 0.996, respectively. The higher value of R² suggests that the fluoride adsorption isotherm of the MgO hollow spheres follows the Freundlich models. The results are similar with the previous reported MgO fluoride adsorbent [26]. A adsorption capacity comparison of different adsorbents is listed in Table 3. It can be seen that the MgO hollow spheres have a much higher adsorption capacity than other adsorbents. The excellent fluoride adsorption performance can be attributed to the hollow structure and porous surface. The hollow structure would bring relatively large surface area and more active sites for fluoride adsorption. Commonly, the adsorbents work when its surfaces contact with the fluoride solution, indicating that only the outer surface of normal sphere works during the adsorption process. However, the MgO hollow spheres have two surfaces, an inner and outer surface. They both can work during the fluoride adsorption process, which largely improve the utilization of the adsorbents. Furthermore, the porous structure can provide abundant channels for fluoride ion diffusion, which would efficiently improve the adsorption performance of the absorbent.

(a)

(b)

(c)

It is well accepted that the pH value of the fluoride solution can largely affect the performance of the adsorbents. Thus, the fluoride adsorption property of the MgO hollow spheres were studied under different pH values. It can be seen from Figure 4 that, within 2–10, the pH value has little influence on the fluoride removal efficiency of the MgO hollow spheres. However, when the pH value is beyond 11, the fluoride removal efficiency of the absorbent dramatically decreases. The quick reduction of fluoride removal efficiency of the MgO hollow spheres in the alkaline condition could be attributed to competition of hydroxyl ions with fluoride for adsorption sites [46].

In practical application, various anions exist in the actual groundwater; thus, it is useful to investigate the interference of coexisting ions on the fluoride adsorption of MgO hollow spheres. As presented in Figure 6, these anions at different concentrations have different effects on the fluoride adsorption. Cl⁻, SO₄²⁻, and NO₃⁻ have shown a negligible effect on fluoride adsorption. However, the CO₃²⁻ and HCO₃⁻ ions can largely effect the adsorption performance of the MgO hollow spheres.

3.3. Adsorption Mechanism

To reveal the adsorption mechanism, zeta potential analysis was firstly employed. Figure 7 presents the zeta potential of the MgO hollow spheres at different pH values. When the pH = 2, the zeta potential of the sample is 13.8 eV. Under acidic conditions, as the pH value increases, the zeta potential of the MgO hollow spheres slightly decreases. However, when the pH value continuously increases to alkaline, the zeta potential of the MgO hollow spheres drops sharply. It can be seen that the zero point of potential of the MgO hollow spheres is close to pH 10. The higher zero point of the MgO hollow spheres is benefit to the fluoride adsorption via electrostatic attraction, subsequently resulting in the good fluoride adsorption performance in neutral and even weak alkaline conditions.

Obviously, only zeta potential is inadequate to illustrate the adsorption mechanism of the MgO hollow spheres; thus, the FTIR analysis was also employed. Figure 8 indicates the FTIR spectra of the MgO hollow spheres before and after fluoride adsorption. There are a broad-band peak located at 3466 cm⁻¹ and a relatively small peak located at 1641 cm⁻¹ existing in both the samples, which correspond to the stretching vibration modes of OH bands and the bending vibration of the H-O-H band of the adsorbed water, respectively [43]. After fluoride adsorption, the FTIR peak at 3695 cm⁻¹ become strong, suggesting the formation of Mg(OH)₂ on the surface of MgO hollow spheres during the adsorption process [47]. Furthermore, before fluoride adsorption, the peak at 429.7 cm⁻¹ can be obviously observed, which corresponds to the Mg-O stretching vibration. However, after adsorption, the peak at 429.7 cm⁻¹ vanishes, and a new peak at 492.7 cm⁻¹ appears. The new peak can be assigned to the Mg-F stretching vibration, indicating that MgF forms during the adsorption process. For the MgO hollow spheres, the peak at 1453 cm⁻¹ can be clearly observed, which corresponds to the asymmetric stretching vibration of carbonates [48]. MgO, as basic oxide, easily reacts with the CO₂ molecule in the air, forming a magnesium carbonate species on its surface [26]. It is noteworthy that, after adsorption, the intensity of the peak at 1453 cm⁻¹ largely decreases, indicating the great reduction of the surface carbonates during the fluoride adsorption process. The hydroxyl exchange adsorption mechanism is well accepted in fluoride adsorption. In our case, we also found that the surface carbonates also can be exchanged with F⁻ during the adsorption process.

As presented in Figure 9, the schematic fluoride adsorption mechanism is proposed on the MgO hollow spheres. It is well accepted that the MgO can react with H₂O, forming MgOH on the surface. By exchanging with the surface hydroxyls, fluoride ions can be adsorbed on the surface. In acidic condition, the large amount of H⁺ ions are conducive to the adsorption equilibrium; thus, the MgO hollow spheres exhibit higher adsorption property in acidic condition. When the pH value increase, the redundant hydroxyl ions are not in favor for the fluoride removal, which will result in the decrease of the removal capacity. Furthermore, due to the preparation environment, there is a considerable quantity of carbonates adsorbed on the surface of MgO hollow spheres. During the adsorption process, those surface carbonates also can exchange with the fluoride ions in the water, which is benefit to the adsorption property of the absorbents. The coexchange of the hydroxyls and surface carbonates would largely increase the adsorption performance of the MgO hollow spheres in neutral and alkaline conditions. In this way, the MgO hollow spheres the exhibit superior performance in fluoride adsorption over a wide pH range.

4. Conclusions

In conclusion, the MgO hollow spheres have been synthesized via a facile wet-chemistry method. The hollow and porous structure endorses the MgO hollow spheres the good fluoride adsorption property. The removal efficiency of the MgO hollow spheres to fluoride is very fast, and the result can be well fitted into the pseudo-second-order rate kinetic model. The adsorption capacity of the MgO hollow spheres is larger than 182.4 mg/g at pH 7.0. The MgO hollow spheres maintain excellent fluoride adsorption performance over a wide pH range. From the FTIR results, a hydroxyl and carbonate coexchange mechanism is proposed. It is believed that the as-prepared MgO hollow spheres can be a potential candidate for fluoride removal.

Data Availability

The raw data required to reproduce these findings cannot be shared at this time as the data also form part of an ongoing study.

Conflicts of Interest

The authors declare that they have no conflicts of interest.

Acknowledgments

The authors gratefully acknowledge the financial support provided by the National Key Research and Development Program (No. 2019YFC0408504), Natural Science Foundation of Anhui Province (No. 2008085MB44), Natural Science Research Project of Anhui Educational Committee (Nos. KJ2019A0772 and KJ2018ZD048), Initial Scientific Research Fund of Anhui Jianzhu University (No. 2017QD14), and Science and Technology Service Network Initiative of the Chinese Academy of Sciences (No. KFJ-STS-QYZD-173).

References

J. Jankausk, “Effects of fluoride on kidney review,” Fluoride, vol. 7, no. 2, pp. 93–105, 1974, in English.
View at: Google Scholar
X. L. Zhao, “Removal of fluoride from aqueous media by Fe₃O₄@AlOH₃ magnetic nanoparticles, in English,” Journal of Hazardous Materials, vol. 173, no. 1–3, pp. 102–109, 2010.
View at: Publisher Site | Google Scholar
K. Hu and J. M. Dickson, “Nanofiltration membrane performance on fluoride removal from water, in English,” Journal of Membrane Science, vol. 279, no. 1-2, pp. 529–538, 2006.
View at: Publisher Site | Google Scholar
WHO, Guidelines for drinking-water quality: incorporating first addendum, WHO, Geneva, Switzerland, 2006.
Z. Jin, T. Jia et al., “Efficient removal of fluoride by hierarchical MgO microspheres: performance and mechanism study,” Applied Surface Science, vol. 357, pp. 1080–1088, 2015.
View at: Publisher Site | Google Scholar
B. D. Turner, P. Binning, and S. L. S. Stipp, “Fluoride removal by calcite: evidence for fluorite precipitation and surface adsorption,” Environmental Science & Technology, vol. 39, no. 24, pp. 9561–9568, 2005.
View at: Publisher Site | Google Scholar
B. Pan, J. Xu, B. Wu, Z. Li, and X. Liu, “Enhanced removal of fluoride by polystyrene anion exchanger supported hydrous zirconium oxide nanoparticles,” Environmental Science & Technology, vol. 47, no. 16, pp. 9347–9354, 2013.
View at: Publisher Site | Google Scholar
C. S. Sundaram and S. Meenakshi, “Fluoride sorption using organic-inorganic hybrid type ion exchangers, in English,” Journal of Colloid and Interface Science, vol. 333, no. 1, pp. 58–62, 2009.
View at: Google Scholar
W. F. Ma, W. J. Liu, and G. W. Chen, “Factors influencing the removal of fluoride from groundwater by nanofiltration,” in Proceedings of the 2009 3rd International Conference on Bioinformatics and Biomedical Engineering, vol. 1-11, pp. 5771–5775, Beijing, China, June 2009.
View at: Google Scholar
L. A. Richards, M. Vuachère, and A. I. Schäfer, “Impact of pH on the removal of fluoride, nitrate and boron by nanofiltration/reverse osmosis,” Desalination, vol. 261, no. 3, pp. 331–337, 2010.
View at: Publisher Site | Google Scholar
I. Bejaoui, A. Mnif, and B. Hamrouni, “Performance of reverse osmosis and nanofiltration in the removal of fluoride from model water and metal packaging industrial effluent,” Separation Science and Technology, vol. 49, no. 8, pp. 1135–1145, 2014.
View at: Publisher Site | Google Scholar
L. J. Banasiak and A. I. Schafer, “Removal of boron, fluoride and nitrate by electrodialysis in the presence of organic matter, in English,” Journal of Membrane Science, vol. 334, no. 1-2, pp. 101–109, 2009.
View at: Publisher Site | Google Scholar
M. Arda, E. Orhan, O. Arar, M. Yuksel, and N. Kabay, “Removal of fluoride from geothermal water by electrodialysis ED,” Separation Science and Technology, vol. 44, no. 4, pp. 841–853, 2009.
View at: Publisher Site | Google Scholar
L. Chen, B.-Y. He, S. He, T.-J. Wang, C.-L. Su, and Y. Jin, “Fe―Ti oxide nano-adsorbent synthesized by co-precipitation for fluoride removal from drinking water and its adsorption mechanism,” Powder Technology, vol. 227, pp. 3–8, 2012.
View at: Publisher Site | Google Scholar
Y. Nie, C. Hu, and C. Kong, “Enhanced fluoride adsorption using Al III modified calcium hydroxyapatite,” Journal of Hazardous Materials, vol. 233-234, pp. 194–199, 2012.
View at: Publisher Site | Google Scholar
S. Mandal and S. Mayadevi, “Cellulose supported layered double hydroxides for the adsorption of fluoride from aqueous solution,” Chemosphere, vol. 72, no. 6, pp. 995–998, 2008.
View at: Publisher Site | Google Scholar
W.-X. Gong, J.-H. Qu, R.-P. Liu, and H.-C. Lan, “Adsorption of fluoride onto different types of aluminas,” Chemical Engineering Journal, vol. 190, pp. 126–133, 2012.
View at: Publisher Site | Google Scholar
S. Ghorai and K. K. Pant, “Investigations on the column performance of fluoride adsorption by activated alumina in a fixed-bed, in English,” Chemical Engineering Journal, vol. 98, no. 1-2, pp. 165–173, 2004.
View at: Publisher Site | Google Scholar
D. Zhang, H. Luo, L. Zheng et al., “Utilization of waste phosphogypsum to prepare hydroxyapatite nanoparticles and its application towards removal of fluoride from aqueous solution,” Journal of Hazardous Materials, vol. 241-242, pp. 418–426, 2012.
View at: Publisher Site | Google Scholar
M. G. Sujana and S. Anand, “Fluoride removal studies from contaminated ground water by using bauxite,” Desalination, vol. 267, no. 2-3, pp. 222–227, 2011.
View at: Publisher Site | Google Scholar
S. Meenakshi, C. S. Sundaram, and R. Sukumar, “Enhanced fluoride sorption by mechanochemically activated kaolinites, in English,” Journal of Hazardous Materials, vol. 153, no. 1-2, pp. 164–172, 2008.
View at: Publisher Site | Google Scholar
A. Bhatnagar, E. Kumar, and M. Sillanpää, “Fluoride removal from water by adsorption-A review,” Chemical Engineering Journal, vol. 171, no. 3, pp. 811–840, 2011.
View at: Publisher Site | Google Scholar
Y. Ku and H. M. Chiou, “The adsorption of fluoride ion from aqueous solution by activated alumina,” Water Air and Soil Pollution, vol. 133, no. 1-4, pp. 349–360, 2002.
View at: Publisher Site | Google Scholar
Y. H. Li et al., “Adsorption of fluoride from water by amorphous alumina supported on carbon nanotubes, in English,” Chemical Physics Letters, vol. 350, no. 5-6, pp. 412–416, 2001.
View at: Publisher Site | Google Scholar
J. Wang, W. Xu, L. Chen et al., “Excellent fluoride removal performance by CeO2-ZrO2 nanocages in water environment,” Chemical Engineering Journal, vol. 231, pp. 198–205, 2013.
View at: Publisher Site | Google Scholar
K. Sasaki, N. Fukumoto, S. Moriyama, Q. Yu, and T. Hirajima, “Chemical regeneration of magnesium oxide used as a sorbent for fluoride,” Separation and Purification Technology, vol. 98, pp. 24–30, 2012.
View at: Publisher Site | Google Scholar
Z. Jin, Y. Jia, K.-S. Zhang et al., “Effective removal of fluoride by porous MgO nanoplates and its adsorption mechanism,” Journal of Alloys and Compounds, vol. 675, pp. 292–300, 2016.
View at: Publisher Site | Google Scholar
J. Kang, B. Li, J. Song et al., “Defluoridation of water using calcined magnesia/pullulan composite,” Chemical Engineering Journal, vol. 166, no. 2, pp. 765–771, 2011.
View at: Publisher Site | Google Scholar
S. M. Maliyekkal, S. Shukla, L. Philip, and I. M. Nambi, “Enhanced fluoride removal from drinking water by magnesia-amended activated alumina granules, in English,” Chemical Engineering Journal, vol. 140, no. 1-3, pp. 183–192, 2008.
View at: Publisher Site | Google Scholar
K. Zhang, S. Wu, X. Wang et al., “Wide pH range for fluoride removal from water by MHS-MgO/MgCO₃ adsorbent: kinetic, thermodynamic and mechanism studies,” Journal of Colloid and Interface Science, vol. 446, pp. 194–202, 2015.
View at: Publisher Site | Google Scholar
S. Lan, L. Liu, R. Li, Z. Leng, and S. Gan, “Hierarchical hollow structure ZnO: synthesis, characterization, and highly efficient adsorption/photocatalysis toward Congo red,” Industrial & Engineering Chemistry Research, vol. 53, no. 8, pp. 3131–3139, 2014.
View at: Publisher Site | Google Scholar
M. Huang, R. Zhang, Z. Yang et al., “Synthesis of Co₃S₄-SnO₂/polyvinylpyrrolidone-cellulose heterojunction as highly performance catalyst for photocatalytic and antimicrobial properties under ultra-violet irradiation,” International Journal of Biological Macromolecules, vol. 162, pp. 220–228, 2020.
View at: Publisher Site | Google Scholar
Y. F. Yang, M. A. Ashraf, A. Fakhri, V. K. Gupta, and D. Q. Zhang, “Facile synthesis of gold-silver/copper sulfide nanoparticles for the selective/sensitive detection of chromium, photochemical and bactericidal application,” Spectrochimica Acta Part A-Molecular and Biomolecular Spectroscopy, vol. 249, Article ID 119324, 2021.
View at: Google Scholar
S. Lan, N. Guo, L. Liu, X. Wu, L. Li, and S. Gan, “Facile preparation of hierarchical hollow structure gamma alumina and a study of its adsorption capacity,” Applied Surface Science, vol. 283, pp. 1032–1040, 2013.
View at: Publisher Site | Google Scholar
M. Kuang, Y. Shang, G. Yang, B. Liu, and B. Yang, “Facile synthesis of hollow mesoporous MgO spheres via spray-drying with improved adsorption capacity for PbII and CdII,” Environmental Science and Pollution Research, vol. 26, no. 18, pp. 18825–18833, 2019.
View at: Publisher Site | Google Scholar
S. Yang, P. Huang, L. Peng et al., “Hierarchical flowerlike magnesium oxide hollow spheres with extremely high surface area for adsorption and catalysis,” Journal of Materials Chemistry A, vol. 4, no. 2, pp. 400–406, 2016.
View at: Publisher Site | Google Scholar
S. Lagergren, “About the theory of so-called adsorption of soluble substances, K,” Svenska VetenskapsakadHandl, vol. 24, pp. 1–39, 1898.
View at: Google Scholar
Y.-S. Ho, “Second-order kinetic model for the sorption of cadmium onto tree fern: a comparison of linear and non-linear methods,” Water Research, vol. 40, no. 1, pp. 119–125, 2006.
View at: Publisher Site | Google Scholar
S. Moriyama, K. Sasaki, and T. Hirajima, “Effect of calcination temperature on Mg-Al bimetallic oxides as sorbents for the removal of F− in aqueous solutions,” Chemosphere, vol. 95, pp. 597–603, 2014.
View at: Publisher Site | Google Scholar
J. A. Blackwell and P. W. Carr, “Study of the fluoride adsorption characteristics of porous microparticulate zirconium oxide,” Journal of Chromatography A, vol. 549, no. 1-2, pp. 43–57, 1991.
View at: Publisher Site | Google Scholar
K. Biswas, D. Bandhoyapadhyay, and U. C. Ghosh, “Adsorption kinetics of fluoride on ironIII-zirconiumIV hybrid oxide,” Adsorption, vol. 13, no. 1, pp. 83–94, 2007.
View at: Publisher Site | Google Scholar
X. Wu, Y. Zhang, X. Dou, and M. Yang, “Fluoride removal performance of a novel Fe-Al-Ce trimetal oxide adsorbent,” Chemosphere, vol. 69, no. 11, pp. 1758–1764, 2007.
View at: Publisher Site | Google Scholar
H. Liu, S. B. Deng, Z. J. Li, G. Yu, and J. Huang, “Preparation of Al-Ce hybrid adsorbent and its application for defluoridation of drinking water,” Journal of Hazardous Materials, vol. 179, no. 1-3, pp. 424–430, 2010.
View at: Publisher Site | Google Scholar
N. I. Chubar, V. F. Samanidou, V. S. Kouts et al., “Adsorption of fluoride, chloride, bromide, and bromate ions on a novel ion exchanger,” Journal of Colloid and Interface Science, vol. 291, no. 1, pp. 67–74, 2005.
View at: Publisher Site | Google Scholar
C. S. Sundaram, N. Viswanathan, and S. Meenakshi, “Defluoridation of water using magnesia/chitosan composite, in English,” Journal of Hazardous Materials, vol. 163, no. 2-3, pp. 618–624, 2009.
View at: Google Scholar
D. Dayananda, V. R. Sarva, S. V. Prasad, J. Arunachalam, P. Parameswaran, and N. N. Ghosh, “Synthesis of MgO nanoparticle loaded mesoporous Al₂O₃ and its defluoridation study,” Applied Surface Science, vol. 329, pp. 1–10, 2015.
View at: Publisher Site | Google Scholar
H. Niu, Q. Yang, K. Tang, and Y. Xie, “Large-scale synthesis of single-crystalline MgO with bone-like nanostructures,” Journal of Nanoparticle Research, vol. 8, no. 6, pp. 881–888, 2006.
View at: Publisher Site | Google Scholar
R. Xu and H. C. Zeng, “Dimensional control of cobalt-hydroxide-carbonate nanorods and their thermal conversion to one-dimensional arrays of Co₃O₄ Nanoparticles,” The Journal of Physical Chemistry B, vol. 107, no. 46, pp. 12643–12649, 2003.
View at: Publisher Site | Google Scholar

Copyright

Copyright © 2021 Yong Zhang et al. This is an open access article distributed under the Creative Commons Attribution License, which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.

PDF Download Citation

Download other formats

Order printed copies

Views

676

Downloads

930

Citations