Abstract
To investigate the impact of radiotherapy on surface properties of restorative dental materials. A conventional resin composite—CRC (Aura Enamel), a bulk-fill resin composite—BFRC (Aura Bulk-fill), a conventional glass ionomer cement—CGIC (Riva self cure), and a resin-modified glass ionomer cement—RMGIC (Riva light cure) were tested. Forty disc-shaped samples from each material (8 mm diameter × 2 mm thickness) (n = 10) were produced according to manufacturer directions and then stored in water distilled for 24 h. Surface wettability (water contact angle), Vickers microhardness, and micromorphology through scanning electron microscopy (SEM) before and after exposition to ionizing radiation (60 Gy) were obtained. The data were statistically evaluated using the two-way ANOVA and Tukey posthoc test (p < 0.05). Baseline and post-radiation values of contact angles were statistically similar for CRC, BFRC, and RMGIC, whilst post-radiation values of contact angles were statistically lower than baseline ones for CGIC. Exposition to ionizing radiation statistically increased the microhardness of CRC, and statistically decreased the microhardness of CGIC. The surface micromorphology of all materials was changed post-radiation. Exposure to ionizing radiation negatively affected the conventional glass ionomer tested, while did not alter or improved surface properties testing of the resin composites and the resin-modified glass ionomer cement tested.
Similar content being viewed by others
1 Introduction
The head and neck region is a prevalent site for the occurrence of malignant neoplasms which mainly affect several oral tissues [1, 2]. The treatment of cancer in the head and neck region is generally based on clinical staging, tumor location, histological differentiation, and the patient’s clinical conditions [3, 4]. Treatment is performed in most situations employing surgery or radiotherapy, and there may be cases that require both association therapy. Radiotherapy uses a beam of ionizing radiation and aims to destroy tumor cells, minimizing damage to normal cells [5, 6].
The management of patients submitted to cervicofacial radiotherapy requires a multidisciplinary approach, making the restoration of caries lesions highly challenging for dentists [7, 8]. The restorative treatment of caries lesions before radiation therapy is necessary to prevent disease progression and reduce the burden of microorganisms [9]. This approach is important because adhesion between restorative materials and dental tissues is compromised by ionizing radiation so that a post-radiotherapy tooth restoration might provide an unsuccessful treatment [10].
Regarding the restorative materials available for dentists, resin composites, and glass ionomer cement are frequently used to restore caries lesions and esthetic restorative treatments [11]. Resin-based restorative dental materials are versatile and have shown constant progress concerning types of filler particles [12]. However, resin composites still present unfavorable aspects such as polymerization shrinkage stress, marginal infiltration, biocompatibility, and the presence of unreacted monomers [13]. Bulk-fill resins emerged to optimize restorative procedures with more advantages, such as the single-step incremental insertion proposal, saving clinical time, demonstrating a better degree of conversion, and polymerization stress in deeper layers [14].
In restorative dentistry, glass ionomer cement is available in two formulations: conventional glass-ionomer and resin-modified glass-ionomer [15]. Conventional glass-ionomers set via an acid-basic reaction and present anti-cariogenic activity, good adhesion to dental tissues, and long-term fluoride release [16]. However, the low tensile strength, susceptibility to dehydration, and low fracture toughness may limit the use [17]. In an attempt to improve the physical properties and minimize risk to moisture, resin-modified ionomer cement has been market, increasing work-time, control over material prey, and improving the hardening process [18, 19].
In this context, studies report that gamma radiation therapy affects the glass ionomers and the resin composite properties [20,21,22]. It has been demonstrated that gamma radiation increased the microhardness of a glass ionomer cement [23] and can produce free radicals that may improve the microhardness of resin-based materials such as conventional resin composites [24]. However, bulk-fill resin composites were recently introduced in the market so that it is necessary to investigate how the gamma radiation would affect their surface properties in an attempt to provide a safe clinical use in individuals undergoing radiotherapy. Moreover, changes in the wettability of dental restorative materials might increase their susceptibility to microbial adhesion and biofilm formation [25], so that there is the need to investigate if the exposition to gamma radiation would become conventional and bulk-fill resin composites and conventional and resin-modified glass ionomer cements more wettable.
This study aimed to evaluate the influence of ionizing radiation on surface wettability, microhardness, and micromorphology of conventional and bulk-fill resin composites, and conventional and resin-modified glass ionomer cement. The null hypothesis was that ionizing radiation would not alter the surface properties of materials tested.
2 Materials and methods
2.1 Experimental design
A factorial design 4 × 2 was developed in this laboratory investigation. The factors under study were: restorative dental materials (conventional resin composite—CRC; bulk-fill resin composite—BFRC; conventional glass ionomer cement—CGIC; and resin-modified glass ionomer cement—RMGIC); and timepoint of analysis (before and after exposition to ionizing radiation). Surface microhardness, wettability, and surface morphology were the response variables. The materials used in this study are shown in Table 1.
2.2 Preparation of the specimens
A schematic representation of the methods is shown in Fig. 1. Forty disc-shaped specimens (n = 10) were produced (8 mm diameter × 2 mm thickness) according to the materials used in this study. Resin composites were inserted in a single increment into the mold and covered with a mylar strip and a 1-mm thick glass slide before photoactivation for 20 s using a light-emitting diode (Radii-Cal, SDI, Victoria, Australia—1200 mW/cm2, 440–480 nm). Glass ionomer cement encapsulated were prepared according to the manufacturer’s instructions. The plunger was placed on a hard surface and a mechanical mixer (Ultramat S, SDI, Victoria, Australia, 4600 rpm) was used to mix the capsules for 10 s. The capsule was then placed into the Riva applicator (SDI Limited, Bayswater, VIC, Australia). Then, a single portion of materials was inserted into the mold and covered with a mylar strip and a 1-mm thick glass slide. The resin-modified glass ionomer cement was photoactivated for 20 s. The self-cure glass ionomer cement was kept undisturbed for 6 min until the entire curing, and the coating agent (Riva Coast, SDI Limited, Victoria, Australia) was applied and photoactivated for 20 s. Specimens were stored in water at 37 °C for 24 h before further analysis.
2.3 Baseline analyses
Micromorphology, wettability, and microhardness were evaluated in all specimens. Photomicrographs were obtained through Scanning Electron Microscopy (SEM) (TM-3000, Hitachi Tabletop, Tokyo, Japan) with 100X magnification on the center of each specimen to observe how the surfaces of the glass ionomers and resin composites behaved before and after exposition to ionizing radiation. The specimens did not need any surface treatment because an Environmental SEM was used.
Wettability was evaluated by measuring the contact angle between all materials’ surfaces and distilled water through the sessile drop method at room temperature [26] with a drop shape analysis system (Surftens 4.7 Software, Frankfurt, Germany). A drop of 10 µl of distilled water was dispensed on the center of each specimen and the contact angle was measured at three different locations for each specimen and the average value was reported.
Microhardness was measured using a digital microhardness tester (MV2000A, Pantec, São Paulo, SP, Brazil). Five indentations were made on the center of specimens randomly under 50 g load for 15 s. The diagonals of Vickers indentations were measured through the eyepiece of the optical microscope immediately after indentation. The means of the diagonals of each indentation were measured and the mean of five indentations for each surface was calculated for each specimen.
2.4 Irradiation
During radiation therapy, oral cancer patients are exposed to a total radiation dose ranged from 50 to 70.4 Gy [27]. Cobalt-60 or linear accelerator units can be used as a source of radiation [28]. To simulate the clinical parameters and radiation doses used during radiotherapy, this in vitro study used a linear accelerator to apply the radiation dose of 60 Gy on forty disc-shaped specimens in a single session [29], with a gamma beam of cobalt-60 teletherapy unit (Theratron 760) simulating a radiotherapy procedure applied to patients with head and neck cancer. Radiation was performed in a hospital environment. The specimens were stored in distilled water and irradiated aiming at the homogeneity of irradiation.
2.5 Post-radiation analyses
Forty-eight hours after irradiation, micromorphology, wettability, and microhardness were evaluated using the previously described protocol.
2.6 Statistical analysis
Wettability (contact angles) and microhardness were evaluated using two-way ANOVA and Tukey posthoc tests (p < 0.05) since a parametric data distribution was obtained (Kolmogorov–Smirnov). The software ASSISTAT Beta (7.7 version) (Campina Grande, PB, Brazil) was used to perform statistic tests. Micromorphology was descriptively analyzed.
3 Results
3.1 Vickers microhardness
Two-way ANOVA revealed statistically significant differences among restorative dental materials (p < 0.001) and timepoints of analysis (p < 0.001). The interaction between “restorative dental material” versus “timepoint of analysis” was statistically significant (p < 0.001). Multiple comparisons among the groups are shown in Table 2. Bulk fill resin composite and resin-modified glass ionomer cement maintained statistically similar values before and after radiation. In contrast, conventional resin composite showed increased values, and conventional glass ionomer cement decreased values at post-radiation. At pre-radiation timepoint, resin composites showed statistically similar and lower values than glass ionomer cement. On the other hand, conventional resin composite showed statistically highest values at post-radiation timepoint, and conventional glass ionomer cement statistically the lowest values.
3.2 Wettability
Two-way ANOVA revealed no statistically significant differences in time points of analysis (p = 0.3262). However, there were statistically significant differences among restorative dental materials (p = 0.0251) and the interaction between “restorative dental material” versus “timepoint of analysis” was statistically significant (p = 0.0194). Multiple comparisons among the groups are shown in Table 3. Conventional glass ionomer cement showed statistically lower values post-radiation than at pre-radiation timepoint, whilst other restorative dental materials maintained statistically similar values between different time points. At pre-radiation, resin composites showed similar values and statistically lower than those of glass ionomer cement. On the other hand, restorative dental materials showed statistically similar values post-radiation.
3.3 SEM analysis
Figure 2 presents images of the materials before and after ionizing radiation. In the CGIC, ionizing radiation removed the resin coating that was applied to the material surface. On the other hand, ionizing radiation did not alter the morphology of RMGIV, which showed similar visual characteristics at baseline and post-radiation. In the CRC, specimens after ionizing radiation presented more filler particles exposed on the material surface, which were covered by the organic matrix at baseline. Specimens of BFRC after ionizing radiation presented fewer large filler particles exposed and smaller filler particles exposed than at baseline.
4 Discussion
The null hypothesis—that ionizing radiation would not alter the surface properties of materials—was rejected. In general, ionizing radiation promoted changes in the microhardness, wettability, and surface morphology of resin composites and glass ionomer cements tested.
In this study, a conventional and a resin-modified GIC, and a conventional and a bulk-fill resin composite were tested as they are the most commonly used dental materials to perform direct tooth restorations [11] and can be subjected to ionizing radiation in individuals undergoing head and neck radiotherapy. CGIC’s are produced by an acid-base reaction from a powder–liquid mixture [30]. Whilst the liquid contains mainly water and polyacrylic acid, the powder contains non silanized fluoro-alumino-silicate fillers (FASF) and other inorganic components such as strontium, phosphate, zinc, calcium, or sodium which react with [31]. RMGIC contains the same components as CGIC, but the FASF are silanized and the liquid includes methacrylate monomers, typically 2-hydroxyethyl methacrylate (HEMA), and camphorquinone as photoinitiator [32]. On the other hand, resin composites are composed of methacrylate monomers, photoinitiators, typically camphorquinone, and silanized filler particles [33].
When dental materials are subjected to ionizing radiation, they can interact with their surface and cause structural changes, which will occur distinctly depending on the surface chemical components of the material. The CGIC tested was the only one that presented microhardness decreasing after being exposed to ionizing radiation. Ionizing radiation likely caused the dissolution of resin coating applied on the CGIC’s surface and detachment of their non silanized FASF, exposing a softer material with decreased microhardness. Silane coupling agents are mainly organic silicides (X3SiY) where X may be chlorine, alkoxy or acetoxy groups and Y may be vinyl, epoxy, amino or mercapto groups. X groups convert to the alkoxy group via hydrolysis and make hydrogen bonding or covalent bonding with the alkoxy group present on the surface of inorganic filler particles while Y is reactive groups that bind with organic monomers and hence improve adhesion of interface [34]. Since FASF are not silanized and CGIC has not methacrylate monomers, probably, they were numerously detached from the material surface, which would have led to a microhardness decreasing. Conversely, as the RMGIC tested contains silanized FASF and methacrylate monomers, a more stable bond between monomers and fillers can be obtained [33] so that they were less detached, and post-radiation morphology microhardness was maintained.
Concerning CRC and BFRC tested, SEM images showed that a slight dissolution of materials’ surfaces occurred in consequence of exposition to ionizing radiation, which promoted the appearance of subsurface filler particles that were distributed below the resin-rich surface layer [35, 36]. As it was seen at baseline, the CRC Aura Enamel contains only microfillers of similar size, which were exposed after the dissolution of the resin matrix occurred after the specimens were subjected to ionizing radiation. On the other hand, the BFRC aura bulk fill presented filler particles with different sizes even at baseline. Ionizing radiation likely weakened the bond between larger fillers and resin matrix due to a larger peripherical area exposed than in smaller particles. In this way, larger particles would have been detached from the polymerized resin matrix, appearing smaller particles that were maintained entrapped into the polymerized resin matrix.
In summary, the hardness of restorative materials depends on the number of exposed filler particles [37]. Thus, the higher exposition of filler particles provided increased surface hardness values in the conventional resin composite tested. Also, a glass ionomer cement is softer than other restorative materials [38]. In this way, the resin coat remotion in the conventional glass ionomer cement post-radiation exposed a softer and more hydrophilic material with a decreased hardness and increased wettability. Also, conventional glass ionomer cement is softer and more hydrophilic than other restorative materials [39].
At the moment that ionizing radiation can cause a dissolution of the resin matrix, it can improve linking among polymerized chains after photoactivation through molecular excitation and continuous polymerization of the non-polymerized surface layer [25, 40]. Polymerized chains can form crosslinks through hydrogen bonds between OH or NH groups and ether or carbonyl groups, as well as among themselves, especially for hydroxyl-hydroxyl groups of monomers [41, 42]. In this way, resin composites containing a higher percentage of dimethacrylate monomers that present these groups, such as bisphenol A diglycidyl methacrylate (Bis-GMA), diurethane dimethacrylate (UDMA), and ethoxylated bisphenol A dimethacrylate (Bis-EMA). Since only the CRC showed increased microhardness at post-radiation, Aura Enamel probably contains an increased percentage of monomers that can form post-polymerization crosslinks than the BFRC aura bulk fill. It is reasonable to assume that the decreased microhardness of resin composites at post-radiation obtained previously [20], different from the present investigation, may be attributed to the lower percentage of crosslinker monomers in the materials tested. From a clinical point of view, it is supposed that Eura Enamel may provide increased clinical longevity of tooth restorations in individuals undergoing head and neck radiotherapy, once microhardness is related to the material’s strength [43].
Another important parameter that influences the longevity of resin composite restorations is how distilled water interacts with the material surface. High contact angle values imply lesser staining, biofilm accumulation, and pathogen adhesion/proliferation and, ultimately, lower the risk of caries in the restoration margins and progression [44]. Conversely, increased wettability (low contact angle values) of the restorative material can favor continuous penetration of water or oral solvents, chemical degradation, and pore formation [45]. The fact that CFIC presented lower contact angles after exposition to ionizing radiation indicates that the material became more wettable. As resin composites and resin-modified glass ionomer cement contain organic monomers, they can have maintained the wettability of these materials at post-radiation. In this way, one can presume that the use of this CGIC to restore decayed teeth of individuals undergoing head and neck radiotherapy would not guarantee clinical longevity for dental restoration.
In a general way, the CRC showed the best behavior for all properties tested, although BFRC and CGIC were not negatively affected by ionizing radiation. Since individuals undergoing head and neck radiotherapy are more prone to have caries in the restoration margins [46], the ideal material to restore their decayed teeth should present mechanical strength, resistance to erosion, and inhibit the formation of caries lesions. Thus, although glass ionomer cement can release fluoride which contributes to inhibiting the formation of caries lesion [46], further in vivo studies should be performed to evaluate the behavior of the materials tested in this study. In clinical conditions, dental materials and tooth restorations are exposed to radiotherapy in the presence of saliva. However, the specimens were stored in distilled water in this study following previous investigations [24, 29, 47, 48]. Clinical variables associated with individual biology or oral hygiene such as hyposalivation, caries appearance, and longevity of restorative materials were not evaluated and, therefore, need to be evaluated in further clinical trials.
5 Conclusion
The conventional glass ionomer tested was the only material tested which was negatively affected by exposition to ionizing radiation. Exposition to ionizing radiation positively affected the microhardness of the conventional resin composite tested, while did not alter its wettability, and maintained microhardness and wettability of the resin-modified glass ionomer cement and the bulk-fill resin composite tested.
References
Ferlay J, Steliarova-Foucher E, Lortet-Tieulent J, Rosso S, Coebergh JW, Comber H, et al. Cancer incidence and mortality patterns in Europe: estimates for 40 countries in 2012. Eur J Cancer. 2013;49:1374–403. https://doi.org/10.1016/j.ejca.2012.12.027
Ferlay J, Soerjomataram I, Dikshit R, Eser S, Mathers C, Rebelo M, et al. Cancer incidence and mortality worldwide: sources, methods and major patterns in GLOBOCAN 2012. Int J Cancer. 2015;136:E359–86. https://doi.org/10.1002/ijc.29210
Funk CS, Warmling CM, Baldisserotto J. A randomized clinical trial to evaluate the impact of a dental care program in the quality of life of head and neck cancer patients. Clin Oral Investig. 2014;18:1213–9. https://doi.org/10.1007/s00784-013-1068-2
Farquhar DR, Divaris K, Mazul AL, Weissler MC, Zevallos JP, Olshan AF. Poor oral health affects survival in head and neck cancer. Oral Oncol. 2017;73:111–7. https://doi.org/10.1016/j.oraloncology.2017.08.009
Baskar R, Dai J, Wenlong N, Yeo R, Yeoh KW. Biological response of cancer cells to radiation treatment. Front Mol Biosci. 2014;1:24. https://doi.org/10.3389/fmolb.2014.00024
Kawashita Y, Soutome S, Umeda M, Saito T. Oral management strategies for radiotherapy of head and neck cancer. Jpn Dent Sci Rev. 2020;56:62–67. https://doi.org/10.1016/j.jdsr.2020.02.001
Beech N, Robinson S, Porceddu S, Batstone M. Dental management of patients irradiated for head and neck cancer. Aust Dent J. 2014;59:20–8. https://doi.org/10.1111/adj.12134
Cho H, Kumar N. Dental management of a patient with head and neck cancer: a case report. Br Dent J. 2019;227:25–29. https://doi.org/10.1038/s41415-019-0464-7
Murdoch-Kinch CA, Zwetchkenbaum S. Dental management of the head and neck cancer patient treated with radiation therapy. J Mich Dent Assoc. 2011;93:28–37.
Naves LZ, Novais VR, Armstrong SR, Correr-Sobrinho L, Soares CJ. Effect of gamma radiation on bonding to human enamel and dentin. Support Care Cancer. 2012;20:2873–8. https://doi.org/10.1007/s00520-012-1414-y
Francois P, Fouquet V, Attal JP, Dursun E. Commercially available fluoride-releasing restorative materials: a review and a proposal for classification. Materials 2020;13:2313. https://doi.org/10.3390/ma13102313
Jasse FF, Barud HG, Boaventura JM, Alencar CD, Gatti A, Campos EA. Bulk-fill versus conventional composite: a comparative analysis on degree of conversion. Eur J Gen Dent. 2019;8:36–40.
Soares CJ, Faria-e-Silva AL, Rodrigues MP, Vilela ABF, Pfeifer CS, Tantbirojn D, et al. Polymerization skrinkage stress of composite resins and resin cements—what do we need to know? Braz Oral Res. 2017;31:e62. https://doi.org/10.1590/1807-3107bor-2017.vol31.0062
Orłowski M, Tarczydło B, Chałas R. Evaluation of marginal integrity of four bulk-fill dental composite materials: in vitro study. ScientificWorldJournal. 2015;2015:701262. https://doi.org/10.1155/2015/701262
Muñoz-Viveros CA. Glass ionomer restoratives. In: Freedman G editors, Contemporary esthetic dentistry, 3rd ed. St. Louis: Mosby; 2012, pp 337–40. https://doi.org/10.1016/C2009-0-39360-5
Menezes-Silva R, Cabral RN, Pascotto RC, Borges AFS, Martins CC, Navarro MFL, et al. Mechanical and optical properties of conventional restorative glass-ionomer cements—a systematic review. J Appl Oral Sci. 2019;27:e2018357. https://doi.org/10.1590/1678-7757-2018-0357
Khoroushi M, Keshani F. A review of glass-ionomers: from conventional glass-ionomer to bioactive glass-ionomer. Dent Res J. 2013;10:411–20.
Sidhu SK, Nicholson JW. A review of glass-ionomer cements for clinical dentistry. J Funct Biomater. 2016;7:16. https://doi.org/10.3390/jfb7030016
Knight GM. The benefits and limitations of glass-ionomer cements and their use in contemporary dentistry. In: Sidhu S editors, Glass-ionomers in dentistry. Cham: Springer; 2026, pp 57–79. https://doi.org/10.1007/978-3-319-22626-2_3
Vieiro FL, Boscolo FN, Demarco FF, Faot F. Effect of radiotherapy on the hardness and surface roughness of two composite resins. Gen Dent. 2011;59:168–72.
Aziz AAA. Effect of different gamma radiation doses on the mechanical properties of esthetic restorations. Egypt Dent J. 2017;63:3955–64. https://doi.org/10.21608/edj.2017.76462
Lima RBW, Meireles SS, Pontual ML, Andrade AKM, Duarte RM. The impact of radiotherapy in the in vitro remineralization of demineralized enamel. APESB. 2019;19:e4073. https://doi.org/10.4034/pboci.2019.191.18
Novais VR, Simamoto Júnior PC, Rodrigues RB, Roscoe MG, Valdívia ADCM, Soares CJ. Effect of irradiation on the mechanical behavior of restorative materials. Rev Odontol Bras Cent. 2015;24:44–48.
Brandeburski SBN, Della Bona A. Effect of ionizing radiation on properties of restorative materials. Dent Mater. 2018;34:221–7. https://doi.org/10.1016/j.dental.2017.10.006
Cazzaniga G, Ottobelli M, Ionescu A, Garcia-Godoy F, Brambilla E. Surface properties of resin-based composite materials and biofilm formation: a review of the current literature. Am J Dent. 2015;28:311–20.
Kasraei S, Azarsina M. Addition of silver nanoparticles reduces the wettability of methacrylate and silorane-based composites. Braz Oral Res. 2012;26:505–510. https://doi.org/10.1590/s1806-83242012000600004
Silva AR, Alves FA, Berger SB, Giannini M, Goes MF, Lopes MA. Radiation-related caries and early restoration failure in head and neck cancer patients. A polarized light microscopy and scanning electron microscopy study. Support Care Cancer. 2010;18:83–7. https://doi.org/10.1007/s00520-009-0633-3
Kielbassa AM, Hinkelbein W, Hellwig E, Meyer-Lückel H. Radiation-related damage to dentition. Lancet Oncol. 2006;7:326–35. https://doi.org/10.1016/S1470-2045(06)70658-1
Lima RBWE, Vasconcelos LC, Pontual ML, Meireles SS, Andrade AKM, Duarte RM. Effect of ionizing radiation on the properties of restorative materials. Indian J Dent Res. 2019;30:408–13.
Wilson DA, Kent BE. The glass-ionomer cement, a new translucent dental filling material. J Appl Chem Biotechnol. 2007;21(11):313–42. https://doi.org/10.1002/jctb.5020211101
Najeeb S, Khurshid Z, Zafar MS, Khan AS, Zohaib S, Martí JMN, et al. Modifications in glass ionomer cements: nano-sized fillers and bioactive nanoceramics. Int J Mol Sci. 2016;17:1134. https://doi.org/10.3390/ijms17071134
Moberg M, Brewster J, Nicholson J, Roberts H. Physical property investigation of contemporary glass ionomer and resin-modified glass ionomer restorative materials. Clin Oral Investig. 2019;23:1295–308. https://doi.org/10.1007/s00784-018-2554-3
Pratap B, Gupta RK, Bhardwaj B, Nag M. Resin based restorative dental materials: characteristics and future perspectives. Jpn Dent Sci Rev. 2019;55:126–38. https://doi.org/10.1016/j.jdsr.2019.09.004
Nihei T. Dental applications for silane coupling agents. J Oral Sci. 2016;58:151–5. https://doi.org/10.2334/josnusd.16-0035
Costa GFAD, Fernandes ACBCJ, Carvalho LAO, de Andrade AC, de Assunção IV, Borges BCD. Effect of additional polishing methods on the physical surface properties of different nanocomposites: SEM and AFM study. Microsc Res Technol. 2018;81:1467–73. https://doi.org/10.1002/jemt.23147
Costa GFAD, Melo AMDS, de Assunção IV, Borges BCD. Impact of additional polishing method on physical, micromorphological, and microtopographical properties of conventional composites and bulk fill. Microsc Res Technol. 2020;83:211–22. https://doi.org/10.1002/jemt.23404
Kundie F, Azhari CH, Muchtar A, Ahmad ZA. Effects of filler size on the mechanical properties of polymer-filled dental composites: a review of recent developments. J Phys Sci. 2018;29:141–65. https://doi.org/10.21315/jps2018.29.1.10
Nassar HM, Platt JA. Fluoride release from two high-viscosity glass ionomers after exposure to fluoride slurry and varnish. Materials. 2019;12:3760. https://doi.org/10.3390/ma12223760. Nov 15
Spajić J, Prskalo K, Šariri K, Par M, Pandurić V, Demoli N. Dimensional changes of glass ionomers and a giomer during the setting time. Acta Stomatol Croat Dec. 2018;52:298–306. https://doi.org/10.15644/asc52/4/3
Cruz A, Sinhoreti M, Ambrosano G, Rastelli A, Bagnato V, Bóscolo F. Effect of therapeutic dose Xrays on mechanical and chemical properties of esthetic dental materials. Mater Res. 2008;11:313–8. https://doi.org/10.1590/S1516-14392008000300014
Ren Z, Ma D, Yang X. H-bond and conformations of donors and acceptors in model polyether based polyurethanes. Polymer. 2003;44:6419–25. https://doi.org/10.1016/S0032-3861(03)00726-2
Lemon MT, Jones MS, Stansbury JW. Hydrogen bonding interactions in methacrylate monomers and polymers. J Biomed Mater Res A. 2007;83:734–46. https://doi.org/10.1002/jbm.a.31448
Elkaffas AA, Eltoukhy RI, Elnegoly SA, Mahmoud SH. The effect of preheating resin composites on surface hardness: a systematic review and meta-analysis. Restor Dent Endod. 2019;44:e41. https://doi.org/10.5395/rde.2019.44.e41
Fu J, Liu W, Hao Z, Wu X, Yin J, Panjiyar A, et al. Characterization of a low shrinkage dental composite containing bismethylene spiroorthocarbonate expanding monomer. Int J Mol Sci. 2011;15:2400–12. https://doi.org/10.3390/ijms15022400
Borges MA, Matos IC, Mendes LC, Gomes AS, Miranda MS. Degradation of polymeric restorative materials subjected to a high caries challenge. Dent Mater. 2011;27:244–52. https://doi.org/10.1016/j.dental.2010.10.009
De Moor RJ, Stassen IG, van ‘t Veldt Y, Torbeyns D, Hommez GM. Two-year clinical performance of glass ionomer and resin composite restorations in xerostomic head- and neck-irradiated cancer patients. Clin Oral Investig. 2011;15:31–8. https://doi.org/10.1007/s00784-009-0355-4
Yamin PA, Pereira RD, Lopes FC, Queiroz AM, Oliveira HF, Saquy PC, et al. Longevity of bond strength of resin cements to root dentine after radiation therapy. Int Endod J Nov. 2018;51:1301–12. https://doi.org/10.1111/iej.12945
Ugurlu M, Ozkan EE, Ozseven A. The effect of ionizing radiation on properties of fluoride-releasing restorative materials. Braz Oral Res. 2020;34:e005. https://doi.org/10.1590/1807-3107bor-2020.vol34.0005
Author information
Authors and Affiliations
Contributions
DMGdA (hypothesis, execution of the experimental part, interpretation of qualitative analyzes and wrote manuscript), AHV (hypothesis, execution of the experimental part, execution and interpretation of qualitative analyzes and wrote manuscript), AKCR (interpretation of qualitative analyzes and wrote manuscript), ROdAS, IVdA, BCDB and MRGRC (idea, consulted, evaluated the results and proofread the manuscript).
Corresponding author
Ethics declarations
Conflict of interest
The authors declare no competing interests.
Additional information
Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
de Amorim, D.M.G., Veríssimo, A.H., Ribeiro, A.K.C. et al. Effects of ionizing radiation on surface properties of current restorative dental materials. J Mater Sci: Mater Med 32, 69 (2021). https://doi.org/10.1007/s10856-021-06543-5
Received:
Accepted:
Published:
DOI: https://doi.org/10.1007/s10856-021-06543-5