Pure Yttrium silicate (Y2SiO5) crystal was synthesized by solid-state reaction method. The structural behavior of the sample was determined by X-ray diffraction analysis. The particle size of the sample was found around 35 nm. The particle size was further confirmed by transmission electron microscopy (TEM) analysis. The TEM images are well matched with the XRD analysis. The band gap of the Y2SiO5 was determined by Tauc’s plot. The band gap of the sample was obtained 5.44 eV
Similar content being viewed by others
References
L.E. Muresan, Y. Karabulut, A.I. Cadis, I. Perhaita, A. Canimoglu, J. Garcia Guinea, L. BarbuTudoran, D. Silipasf, M. Ayvacikli, N. Can, J. Alloy. Compd. 658, 356 (2016)
N.L. Jobbitt, J.-P.R. Wells, M.F. Reid, J. Lumin. 224, 117302 (2020)
Yu. Ma, Z.-Q. Zhou, C. Liu, Y.-J. Han, T.-S. Yang, Tu. Tao, Y.-X. Xiao, P.-J. Liang, P.-Y. Li, Y.-L. Hua, X. Liu, Z.-F. Li, Hu. Jun, X. Li, C.-F. Li, G.-C. Guo, J. Lumin. 202, 32 (2018)
S.B. Altner, S. Bernet, A. Renn, E.S. Maniloff, F.R. Graf, U.P. Wild, Opt. Commun. 120, 103 (1995)
R. Gaume, P.H. Haumesser, B. Viana, D. Vivien, B. Ferrand, G. Aka, Opt. Mater. 19, 81 (2002)
Wu. Xiao-Xuan, Z. Wen-Chen, T. Sheng, Zi. Jian, Solid State Commun. 131, 93 (2004)
L.E. Muresan, A.I. Cadis, I. Perhaita, D.T. Silipas, L Barbu Tudoran, Mater. Res. Bull. 68, 295–301 (2015)
H.J. Lee, S.K. Hong, D.S. Jung, S.H. Ju, H.Y. Koo, Y.C. Kang, The characteristics of X1 type Y2SiO5: Tb phosphor particles prepared by high temperature spray pyrolysis. Ceram. Int. 32, 865–870 (2006)
X.J. Li, H. Jiao, X.M. Wang, Z.Z. Zeng, X.P. Jing, Y2SiO5:Ce3+ particle growth during sol–gel preparation. J. Rare Earth 28, 504–508 (2010)
H. Jiao, L.Q. Wei, N. Zhang, M. Zhong, X.P. Jing, Melting salt assisted sol–gel synthesis of blue phosphor Y2SiO5:Ce. J. Eur. Ceram. Soc. 27, 185–189 (2007)
D.W. Cooke, J.K. Lee, B.L. Bennett, J.R. Groves, L.G. Jacobsohn, E.A. McKigney, R.E. Muenchausen, M. Nastasi, K.E. Sickafus, M. Tang, J.A. Valdez, J.Y. Kim, K.S. Hong, Luminescent properties and reduced dimensional behavior of hydrothermally prepared Y2SiO5:Ce nanophosphors. Appl. Phys. 88(1–3), 103108 (2006)
G. Ramakrishna, H. Nagabhushana, D.V. Sunitha, S.C. Prashantha, S.C. Sharma, B.M. Nagabhushana, Effect of different fuels on structural, photo and thermo luminescence properties of solution combustion prepared Y2SiO5nanopowders. Spectrochim. Acta Part A 127, 177–184 (2014)
R.K. Tamrakara, D.P. Bisen, N. Brahme, I.P. Sahu, K. Upadhyay, Structural and luminescence behavior of Gd2O3:Er3+phosphorsynthesized by solid state reaction method. Optik 126, 2654–2658 (2015)
C. Michel, G. Buisson, E.F. Bertaut, Structure de Y2SiO5. ComptesRendusHebdomadaires des Seances de l’Academie des Sciences, Serie B 264, 397–399 (1967)
R.K. Tamrakar, D.P. Bisen, Optical and kinetic studies of CdS: Cu nanoparticles. Res. Chem. Intermed. 39(7), 3043–3048 (2013)
A.J. Deotale, R.V. Nandedkar, Materials Today: Proceedings 3, 2069–2076 (2016)
P. Dewangan, D.P. Bisen, N. Brahme et al., Opt. Quant. Electron. 50, 367 (2018). https://doi.org/10.1007/s11082-018-1634-6
Acknowledgments
The authors thank the Bhilai Institute of Technology for providing lab facility for synthesis process.
This study is financially supported by the DST-SERB, Government of India (PDF/2017/000095) under the national post-doctoral fellowship scheme.
Author information
Authors and Affiliations
Corresponding author
Additional information
Publisher’s Note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
About this article
Cite this article
Upadhyay, K., Thomas, S., Kalarikkal, N. et al. Particle Size and Band Gap Calculation of Pure Y2SiO5 Crystal Synthesized by Solid-State Reaction Method. Braz J Phys 51, 599–604 (2021). https://doi.org/10.1007/s13538-021-00859-x
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s13538-021-00859-x