Abstract
Metal halide perovskites of the general formula ABX3—where A is a monovalent cation such as caesium, methylammonium or formamidinium; B is divalent lead, tin or germanium; and X is a halide anion—have shown great potential as light harvesters for thin-film photovoltaics1,2,3,4,5. Among a large number of compositions investigated, the cubic α-phase of formamidinium lead triiodide (FAPbI3) has emerged as the most promising semiconductor for highly efficient and stable perovskite solar cells6,7,8,9, and maximizing the performance of this material in such devices is of vital importance for the perovskite research community. Here we introduce an anion engineering concept that uses the pseudo-halide anion formate (HCOO−) to suppress anion-vacancy defects that are present at grain boundaries and at the surface of the perovskite films and to augment the crystallinity of the films. The resulting solar cell devices attain a power conversion efficiency of 25.6 per cent (certified 25.2 per cent), have long-term operational stability (450 hours) and show intense electroluminescence with external quantum efficiencies of more than 10 per cent. Our findings provide a direct route to eliminate the most abundant and deleterious lattice defects present in metal halide perovskites, providing a facile access to solution-processable films with improved optoelectronic performance.
This is a preview of subscription content, access via your institution
Access options
Access Nature and 54 other Nature Portfolio journals
Get Nature+, our best-value online-access subscription
$29.99 / 30 days
cancel any time
Subscribe to this journal
Receive 51 print issues and online access
$199.00 per year
only $3.90 per issue
Buy this article
- Purchase on Springer Link
- Instant access to full article PDF
Prices may be subject to local taxes which are calculated during checkout
Similar content being viewed by others
Data availability
The data that support the findings of this study are available from the corresponding author upon reasonable request.
Code availability
The code used for this study is available from the corresponding author upon reasonable request.
Change history
08 April 2021
This Article was amended to correct the Peer review information.
References
Kojima, A., Teshima, K., Shirai, Y. & Miyasaka, T. Organometal halide perovskites as visible-light sensitizers for photovoltaic cells. J. Am. Chem. Soc. 131, 6050–6051 (2009).
Grätzel, M. The light and shade of perovskite solar cells. Nat. Mater. 13, 838–842 (2014).
Park, N.-G. et al. Towards stable and commercially available perovskite solar cells. Nat. Energy 1, 16152 (2016).
Correa-Baena, J. P. et al. Promises and challenges of perovskite solar cells. Science 358, 739–744 (2017).
Lu, H., Krishna, A., Zakeeruddin, S. M., Grätzel, M. & Hagfeldt, A. Compositional and interface engineering of organic-inorganic lead halide perovskite solar cells. iScience 23, 101359 (2020).
Eperon, G. E. et al. Formamidinium lead trihalide: a broadly tunable perovskite for efficient planar heterojunction solar cells. Energy Environ. Sci. 7, 982–988 (2014).
Pellet, N. et al. Mixed-organic-cation perovskite photovoltaics for enhanced solar-light harvesting. Angew. Chem. Int. Ed. 53, 3151–3157 (2014).
Jeon, N. J. et al. Compositional engineering of perovskite materials for high-performance solar cells. Nature 517, 476–480 (2015).
Lu, H. et al. Vapor-assisted deposition of highly efficient, stable black-phase FAPbI3 perovskite solar cells. Science 370, eabb8985 (2020).
De Wolf, S. et al. Organometallic halide perovskites: sharp optical absorption edge and its relation to photovoltaic performance. J. Phys. Chem. Lett. 5, 1035–1039 (2014).
Stranks, S. D. et al. Electron-hole diffusion lengths exceeding 1 micrometer in an organometal trihalide perovskite absorber. Science 342, 341–344 (2013).
Herz, L. M. et al. Charge-carrier mobilities in metal halide perovskites: fundamental mechanisms and limits. ACS Energy Lett. 2, 1539–1548 (2017).
NREL. Best Research-Cell Efficiency Chart https://www.nrel.gov/pv/cell-efficiency.html (accessed 17 March 2021).
Zheng, X. et al. Managing grains and interfaces via ligand anchoring enables 22.3%-efficiency inverted perovskite solar cells. Nat. Energy 5, 131–140 (2020).
Liu, Z. et al. A holistic approach to interface stabilization for efficient perovskite solar modules with over 2,000-hour operational stability. Nat. Energy 5, 596–604 (2020).
Saliba, M. et al. Cesium-containing triple cation perovskite solar cells: improved stability, reproducibility and high efficiency. Energy Environ. Sci. 9, 1989–1997 (2016).
Kim, M. et al. Methylammonium chloride induces intermediate phase stabilization for efficient perovskite solar cells. Joule 3, 2179–2192 (2019).
Min, H. et al. Efficient, stable solar cells by using inherent bandgap of α-phase formamidinium lead iodide. Science 366, 749–753 (2019).
Yang, S. et al. Thiocyanate assisted performance enhancement of formamidinium based planar perovskite solar cells through a single one-step solution process. J. Mater. Chem. A 4, 9430–9436 (2016).
Kim, D. H. et al. Bimolecular additives improve wide-band-gap perovskites for efficient tandem solar cells with CIGS. Joule 3, 1734–1745 (2019).
Kim, D. et al. Efficient, stable silicon tandem cells enabled by anion-engineered wide-bandgap perovskites. Science 368, 155–160 (2020).
Walker, B., Kim, G. H. & Kim, J. Y. Pseudohalides in lead-based perovskite semiconductors. Adv. Mater. 31, 1807029 (2019).
Moore, D. T. et al. Direct crystallization route to methylammonium lead iodide perovskite from an ionic liquid. Chem. Mater. 27, 3197–3199 (2015).
Seo, J. et al. Ionic liquid control crystal growth to enhance planar perovskite solar cells efficiency. Adv. Energy Mater. 6, 1600767 (2016).
Nayak, P. K. et al. Mechanism for rapid growth of organic–inorganic halide perovskite crystals. Nat. Commun. 7, 13303 (2016).
Meng, L. et al. Improved perovskite solar cell efficiency by tuning the colloidal size and free ion concentration in precursor solution using formic acid additive. J. Energy Chem. 41, 43–51 (2020).
Khan, Y. et al. Waterproof perovskites: high fluorescence quantum yield and stability from a methylammonium lead bromide/formate mixture in water. J. Mater. Chem. C 8, 5873–5881 (2020).
Askar, A. M. et al. Composition-tunable formamidinium lead mixed halide perovskites via solvent-free mechanochemical synthesis: decoding the Pb environments using solid-state NMR spectroscopy. J. Phys. Chem. Lett. 9, 2671–2677 (2018).
Kubicki, D. J. et al. Cation dynamics in mixed-cation (MA)x(FA)1−xPbI3 hybrid perovskites from solid-state NMR. J. Am. Chem. Soc. 139, 10055–10061 (2017).
Zhou, Z. et al. Synthesis, microwave spectra, X-ray structure, and high-level theoretical calculations for formamidinium formate. J. Chem. Phys. 150, 094305 (2019).
Ross, R. et al. Some thermodynamics of photochemical systems. J. Chem. Phys. 46, 4590–4593 (1967).
Tress, W. et al. Predicting the open-circuit voltage of CH3NH3PbI3 perovskite solar cells using electroluminescence and photovoltaic quantum efficiency spectra: the role of radiative and non-radiative recombination. Adv. Energy Mater. 5, 1400812 (2015).
Jiang, Q. et al. Surface passivation of perovskite film for efficient solar cells. Nat. Photonics 13, 460–466 (2019).
Yang, D. et al. Surface optimization to eliminate hysteresis for record efficiency planar perovskite solar cells. Energy Environ. Sci. 9, 3071–3078 (2016).
Kuik, M., Koster, L. J., Wetzelaer, G. A. & Blom, P. W. Trap-assisted recombination in disordered organic semiconductors. Phys. Rev. Lett. 107, 256805 (2011).
Green, M. Accuracy of analytical expressions for solar cell fill factors. Solar Cells 7, 337–340 (1982).
Wang, Y. et al. Stabilizing heterostructures of soft perovskite semiconductors. Science 365, 687–691 (2019).
Acknowledgements
We thank W. R. Tress for discussions, and the staff at beamlines BL17B1, BL14B1, BL11B, BL08U and BL01B1 of the SSRF for providing the beamline, and the Swiss National Supercomputing Centre (CSCS) and EPFL computing center (SCITAS) for their support. This research was supported by the Technology Development Program to Solve Climate Changes of the National Research Foundation (NRF) funded by the Ministry of Science, ICT & Future Planning (2020M1A2A2080746). This work was also supported by ‘The Research Project Funded by U-K Brand’ (1.200030.01) of Ulsan National Institute of Science & Technology (UNIST). D.S.K. acknowledges the Development Program of the Korea Institute of Energy Research (KIER) (C0-2401 and C0-2402). L.E. acknowledges support from the Swiss National Science Foundation, grant number 200020_178860. U.R. acknowledges funding from the Swiss National Science Foundation via individual grant number 200020_185092 and the NCCR MUST. A.H. acknowledges the Swiss National Science Foundation, project ‘Fundamental studies of dye-sensitized and perovskite solar cells’, project number 200020_185041. M.G. acknowledges financial support from the European Union’s Horizon 2020 research and innovation programme under grant agreement number 881603, and the King Abdulaziz City for Science and Technology (KACST).
Author information
Authors and Affiliations
Contributions
J.J., B.W. and J.Y.K. conceived the project. J.J., Minjin Kim and H.L. prepared the samples, performed the relevant photovoltaic measurements, analysed the data and wrote the manuscript. J.S. synthesised the FAHCOO material. Minjin Kim and D.S.K. certified the efficiency of the PSCs. Y.J.Y. carried out photoluminescence and UV–vis absorption spectroscopy. S.J.C. and I.W.C. performed the time-resolved photoluminescence, SEM and XRD measurements. Y.J. and H.L. collected the light-intensity-dependent J–V data. P.A. and U.R. designed and performed all the DFT calculations and molecular dynamics simulations. Maengsuk Kim and J.H.L contributed to the DFT calculations. A.M., M.A.H. and L.E. conducted the solid-state NMR measurements and analysis. B.P.D. performed the atomic force microscopy measurements. H.L. conducted the long-term operational stability measurements, EQEEL measurements and analysed the data. Y.Y. performed the two-dimensional grazing-incidence XRD measurements. F.T.E contributed to the analysis of the time-resolved photoluminescence data. S.M.Z. coordinated the project. A.H. and M.G. proposed experiments and M.G. wrote the final version of the manuscript. A.H., D.S.K., M.G. and J.Y.K. directed the work. All authors analysed the data and contributed to the discussions.
Corresponding authors
Ethics declarations
Competing interests
The authors declare no competing interests.
Additional information
Peer review information Nature thanks the anonymous reviewers for their contribution to the peer review of this work.
Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Extended data figures and tables
Extended Data Fig. 1 Characterization of the perovskite films with and without FAFo.
a, The Tauc plot of the 2% Fo-FAPbI3 perovskite film. b, A full photoluminescence decay of the reference, 2% Fo-FAPbI3 and 4% Fo-FAPbI3 perovskite films. c, The distribution of the grain sizes of the reference and 2% Fo-FAPbI3 films. The box + whisker plots show the distribution of the grain sizes for both reference and 2% Fo-FAPbI3 perovskite films. The distribution is based on 22 data points each. d, e, The top-view SEM image (d) and the cross-sectional SEM image (e) of the 4% Fo-FAPbI3 perovskite film. f, g, AFM images of the reference (f) and the 2% Fo-FAPbI3 (g) perovskite films. h, The XRD patterns of the reference, 2% Fo-FAPbI3 and 4% Fo-FAPbI3 perovskite films. Peaks labelled with an asterisk are assigned to the FTO substrates, which can be seen for the 4% sample owing to the lower intensity of the perovskite reflections. i, Integrated one-dimensional grazing-incidence XRD pattern of the reference and 2% Fo-FAPbI3 films.
Extended Data Fig. 2 The composition of the Fo-FAPbI3 perovskite film.
a, b, 1H–13C cross-polarization spectra of mechanosynthesized FAPbI3 with 5% FAHCOO (a) and a scraped thin film of 2% Fo-FAPbI3 (b), recorded at 12 kHz MAS and 100 K. In b the formate signal can be seen as a minor shoulder on the FAPbI3 peak. A minor signal arising from the PTFE that is used to seal the rotor is also visible. c, d, TOF-SIMS measurements of the reference (c) and the 2% Fo-FAPbI3 (d) films. e, Quantitative, directly detected 13C solid-state NMR measurement of 2% Fo-FAPbI3 scraped thin film at 12 kHz MAS and 100 K.
Extended Data Fig. 3 Ab initio molecular dynamics simulations.
a, Molecular dynamics snapshot showing the coordination of Pb2+ ions with HCOO− anions in the perovskite precursor solution. As a guide to the eye, we highlight only Pb2+ and HCOO− ions; the remaining ions and solvent molecules are shown as transparent. b, The radial distribution function g(r) between the oxygen atoms of HCOO− and Pb2+ over the full ab initio molecular dynamics trajectory of around 11 ps. c, Initial configuration of FAPbI3 with surface iodide replaced by HCOO− anions. d, The top view of surface atoms on the FA+-terminated side. e, The top view of the surface atoms on the Pb2+-terminated side. Pb2+–HCOO− and FA+–HCOO− bonding and hydrogen-bonding networks are illustrated with magenta dashed lines. All ions are shown in ball-and-stick representation. Pb2+ ions, yellow; iodide, light pink; oxygen, red; carbon, light blue; nitrogen, dark blue; sulfur, light yellow; hydrogen, white.
Extended Data Fig. 4 DFT-relaxed slabs of FAPbI3 with different anions adsorbed at an iodide-vacancy site on the surface.
a, Structure of a pure FAPbI3 slab with a Pb–I terminated surface on the top and an FA–I terminated surface on the bottom side. b–e, Front view of the Cl− (b), Br− (c), BF4− (d) and HCOO− (e) passivated surface. f, An illustration of iodide-vacancy passivation by HCOO−. g, h, DFT-relaxed FAPbI3 slab with HCOO− adsorbed at the iodide-vacancy site on the Pb–I (g) and the FA–I (h) terminated surface. All chemical species are shown in ball-and-stick representation. Pb2+, grey; iodide, violet; oxygen, red; carbon, dark brown; nitrogen, light blue; bromide, red-brown; chloride, light green; boron atoms, dark green; fluoride, yellow; hydrogen atoms, white.
Extended Data Fig. 5 Bonding between formamidinium and different anions on the surface of FAPbI3.
a, Structure of a pure FAPbI3 slab with FA–I termination on the top and Pb–I termination on the bottom side. b, c, The front view (b) and the side view (c) of the HCOO− passivated surface. d–f, Cl− (d), Br− (e) and BF4− (f) passivated surface. All chemical species are shown in ball-and-stick representation. Pb2+, grey; iodide, violet; oxygen, red; carbon, dark brown; nitrogen, light blue; bromide, red-brown; chloride, light green; boron atoms, dark green; fluoride, yellow; hydrogen, white. g, Relative desorption strength of FA+ cations on different passivated surfaces.
Extended Data Fig. 6 Photovoltaic performance of the PSCs under different conditions.
a, J–V curve of the target PSC measured without a metal mask. b, J–V curves of the reference PSC and the PSC with 2% formamidinium acetate. c, J–V curves of the reference and 2% Fo-FAPbI3 PSCs without the MACl additive. d, J–V curves of the reference and the 2% Fo-FAPbI3 PSCs without using octylammonium iodide passivation. FF, fill factor.
Extended Data Fig. 7 J–V metrics of the reference and target PSCs during the operational stability test.
a–c, The change in Jsc (a), Voc (b) and fill factor (c) of the reference and target cells over the 450-h MPP tracking measurement.
Supplementary information
Supplementary Information
This file contains Supplementary Notes 1-6, Supplementary Figs 1-3 and Supplementary References.
Video 1
The coordination of HCOO- anions with Pb2+cations.
Video 2
MD of HCOO- passivated FA-I terminated interface of FAPbI3.
Video 3
MD of HCOO- passivated Pb-I terminated interface of FAPbI3.
Video 4
Perovskite fabrication process.
Rights and permissions
About this article
Cite this article
Jeong, J., Kim, M., Seo, J. et al. Pseudo-halide anion engineering for α-FAPbI3 perovskite solar cells. Nature 592, 381–385 (2021). https://doi.org/10.1038/s41586-021-03406-5
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1038/s41586-021-03406-5
This article is cited by
-
Inhibition of halide oxidation and deprotonation of organic cations with dimethylammonium formate for air-processed p–i–n perovskite solar cells
Nature Energy (2024)
-
All-perovskite-based unassisted photoelectrochemical water splitting system for efficient, stable and scalable solar hydrogen production
Nature Energy (2024)
-
Multifunctional sulfonium-based treatment for perovskite solar cells with less than 1% efficiency loss over 4,500-h operational stability tests
Nature Energy (2024)
-
Toward stabilization of formamidinium lead iodide perovskites by defect control and composition engineering
Nature Communications (2024)
-
Ultrastable halide perovskite CsPbBr3 photoanodes achieved with electrocatalytic glassy-carbon and boron-doped diamond sheets
Nature Communications (2024)
Comments
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.