Abstract
In this study, SAE 1020 steel samples were boronized at 850 °C for 4 h with different boronizing mixtures by powder-pack boronizing method. H3BO3 or Na2B8O13 was used as the boron source, KBF4 or NaBF4 was used as the activator and SiC was used as the diluent. Thus, 4 different boronizing mixtures (M1-M4) were prepared. Thickness, morphology and phase structure of the formed boride layers were studied by X-ray diffraction and microstructural analyzes. The single phase (Fe2B) boride layer with saw-tooth morphology was formed on surface of the samples. The thickest boride layers were obtained by using M1 and M2 boronizing mixtures. Microhardness measurements were performed to determine hardness of the 3 zones (core, transition zone and boride layer). The means of boride layer hardness of the samples were compared according to 95% Confidence Intervals analysis. It was determined that the average hardness value of the boride layers was about 1475 HV. Wear tests were fulfilled by ball on disc type wear test method under dry sliding condition and at 25 °C. According to the friction coefficient and specific wear rate values of boronized samples, it was identified that the sample SM4 boronized with M4 boronizing mixture has the lowest wear rate (1.64 mm3/N.m) and friction coefficient value (0.63).
Graphic Abstract
Similar content being viewed by others
References
I. Gunes, J. Mater. Sci. Technol. 29, 662 (2013)
A. Motallebzadeh, E. Dilektasli, M. Baydogan, E. Atar, H. Cimenoglu, Wear 328–329, 110 (2015)
Y. Kayali, A. Büyüksağiş, Y. Yalçin, Met. Mater. Int. 19, 1053 (2013)
A. Günen, İH. Karahan, M.S. Karakaş, B. Kurt, Y. Kanca, V.V. Çay, M. Yıldız, Met. Mater. Int. 26, 1329 (2020)
L.L. Qian, G.A. Stone, J. Mater. Eng. Perform. 4, 59 (1995)
P. Jurči, M. Hudáková, J. Mater. Eng. Perform. 20, 1180 (2011)
M. Elias-Espinosa, M. Ortiz-Domínguez, M. Keddam, M.A. Flores-Rentería, O. Damián-Mejía, J. Zuno-Silva, J. Hernández-Ávila, E. Cardoso-Legorreta, A. Arenas-Flores, J. Mater. Eng. Perform. 23, 2943 (2014)
I. Campos-Silva, M. Ortiz-Domínguez, C. Tapia-Quintero, G. Rodriguez-Castro, M.Y. Jiménez-Reyes, E. Chavez-Gutiérrez, J. Mater. Eng. Perform. 21, 1714 (2012)
R.S. Petrova, N. Suwattananont, V. Samardzic, J. Mater. Eng. Perform. 17, 340 (2008)
L.S. Ma, Y.H. Duan, P. Li, J. Mater. Eng. Perform. 26, 4544 (2017)
G. Palombarini, M. Carbucicchio, J. Mater. Sci. Lett. 6, 415 (1987)
İ Türkmen, E. Yalamaç, J. Alloy. Compd. 744, 658 (2018)
O.A. Gómez-Vargas, M. Keddam, M. Ortiz-Domínguez, High Temp. Mater. Proc. 36, 197 (2017)
İ Türkmen, E. Yalamaç, M. Keddam, Surf. Coat. Tech. 377, 124888 (2019)
A.K. Sinha, in ASM Handbook, Vol. 4, Heat Treating (ASM International, Materials Park, 1991), pp. 437–447
M. Ipek, G. Celebi Efe, I. Ozbek, S. Zeytin, C. Bindal, J. Mater. Eng. Perform 21, 733 (2012)
I. Uslu, H. Comert, M. Ipek, F.G. Celebi, O. Ozdemir, C. Bindal, Mater. Design 28, 1819 (2007)
E. Atar, E.S. Kayali, H. Cimenoglu, Surf. Coat. Tech. 202, 4583 (2008)
M. Kul, K.O. Oskay, A. Temizkan, B. Karaca, L.C. Kumruoğlu, B. Topçu, Vacuum 126, 80 (2016)
B. Selçuk, R. Ipek, M.B. Karamış, J. Mater. Process. Tech. 141, 189 (2003)
ASTM C1327–15, Standard Test Method for Vickers Indentation Hardness of Advanced Ceramics (ASTM International, West Conshohocken, 2015)
ASTM G99–17, Standard Test Method for Wear Testing with a Pin-on-Disk Apparatus (ASTM International, West Conshohocken, 2017)
D. Mu, B.L. Shen, Adv. Mater. Sci. Eng. 2013, 751971 (2013)
E. Medvedovski, Adv. Eng. Mater. 18, 11 (2016)
O. Allaoui, N. Bouaouadja, G. Saindernan, Surf. Coat. Tech. 201, 3475 (2006)
V.N.E. Robinson, Scanning 3, 15 (1980)
A.A. Joshi, S.S. Hosmani, Mater. Manuf. Process. 29, 1062 (2014)
I. Campos-Silva, M. Ortiz-Domínguez, N. López-Perrusquia, A. Meneses-Amador, R. Escobar-Galindo, J. Martínez-Trinidad, Appl. Surf. Sci. 256, 2372 (2010)
A. Kaouka, O. Allaoui, M. Keddam, Mater. Tech. 101, 705 (2013)
I. Campos-Silva, E. Hernández-Sánchez, G. Rodríguez-Castro, H. Cimenoglu, J.L. Nava-Sánchez, A. Meneses-Amador, R. Carrera-Espinoza, Surf. Coat. Tech. 232, 173 (2013)
H.L. Yang, N. He, G.Z. Tang, Y.G. Li, Y.Z. Zhang, Adv. Mater. Res. 179-180, 508 (2011)
T.W. Spence, M.M. Makhlouf, J. Mater. Process. Tech. 168, 127 (2005)
Y. Kayali, S. Taktak, J. Adhes. Sci. Technol. 29, 2065 (2015)
M. Carbucicchio, G. Palombarini, J. Mater. Sci. Lett. 6, 1147 (1987)
N. Suwattananont, R.S. Petrova, Oxid. Met. 70, 307 (2008)
J.A. Payne, R.S. Petrova, H.J. White, A. Chauhan, J. Bai, J. Mater. Eng. Perform. 17, 730 (2008)
I. Altinsoy, F.G. Celebi Efe, M. Ipek, I. Ozbek, S. Zeytin, C. Bindal, AIP Conf. Proc. 1569, 43 (2013)
E. Hernández-Sanchez, G. Rodriguez-Castro, A. Meneses-Amador, D. Bravo-Bárcenas, I. Arzate-Vazquez, H. Martínez-Gutiérrez, M. Romero-Romo, I. Campos-Silva, Surf. Coat. Tech. 237, 292 (2013)
I. Gunes, Y. Kayali, S. Ulu, Indian J. Eng. Mater. S. 19, 397 (2012)
M.A. Bejar, E. Moreno, J. Mater. Process. Tech. 173, 352 (2006)
A.M. Delgado-Brito, D. López-Suero, A. Ruiz-Rios, R.A. García-León, J. Martínez-Trinidad, J. Oseguera-Peña, I. Campos-Silva, Ceram. Int. 45, 7767 (2019)
D. Mu, B. Shen, X. Zhao, Mater. Design 31, 3933 (2010)
M. Keddam, Appl. Surf. Sci. 236, 451 (2004)
C. Martini, G. Palombarini, M. Carbucicchio, J. Mater. Sci. 39, 933 (2004)
A.P. Krelling, F. Teixeira, C.E. Costa, E.A.S. Almeida, B. Zappelino, J.C.G. Milan, J. Mater. Technol. 8, 766 (2019)
N.L. Perrusquia, M.A.D. Ruiz, E.D.G. Bustos, M. Lores Martínez, G.M.U. Calderón, C.R.T. San Miguel, Mater. Lett. 280, 128573 (2020)
A.K. Litoria, M.D. Joshi, V. Antunes, D. Singh, C.A. Figueroa, F. Alvarez, S.S. Hosmani, Philos. Mag. 101, 777 (2021)
R. Carrera-Espinoza, U. Figueroa-López, J. Martínez-Trinidad, I. Campos-Silva, E. Hernández-Sánchez, A. Motallebzadeh, Wear 362-363, 1–7 (2016)
C.C. Viáfara, A. Sinatora, Wear 267, 425 (2009)
K. De Moerlooze, F. Al-Bender, Wear 269, 183 (2010)
E.A. Gallardo-Hernandez, R. Lewis, Wear 265, 1309 (2008)
S. Taktak, Surf. Coat. Tech. 201, 2230 (2006)
M.S. Gök, Y. Küçük, A. Erdoğan, M. Öge, E. Kanca, A. Günen, Surf. Coat. Tech. 328, 54 (2017)
J. Subrahmanyam, K. Gopinath, Wear 95, 287 (1984)
E. Takeuchi, K. Fujii, T. Katagiri, Wear 55, 121 (1979)
M. Carbucicchio, R. Reverberi, G. Palobarini, G. Sambogna, Hyperfine Interact. 46, 473 (1989)
A. Erdemir, Surf. Coat. Tech. 200, 1792 (2005)
M. Ortiz-Domínguez, M. Elias-Espinosa, M. Keddam, O.A. Gómez-Vargas, R. Lewis, E.E. Vera-Cárdenas, J. Zuno-Silva, Indian J. Eng. Mater. S. 22, 231 (2015)
B.S. Ünlü, E. Atik, Mater. Design 31, 2690 (2010)
N. Vidakis, A. Antoniadis, N. Bilalis, J. Mater. Process. Tech. 143–144, 481 (2003)
S. Taktak, S. Tasgetiren, J. Mater. Eng. Perform. 15, 570 (2006)
Acknowledgements
The experiments in this paper were partially performed at Manisa Celal Bayar University (Turkey)- Applied Science and Research Center (DEFAM).
Author information
Authors and Affiliations
Corresponding author
Additional information
Publisher's Note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
About this article
Cite this article
Türkmen, İ., Yalamaç, E. Effect of Alternative Boronizing Mixtures on Boride Layer and Tribological Behaviour of Boronized SAE 1020 Steel. Met. Mater. Int. 28, 1114–1128 (2022). https://doi.org/10.1007/s12540-021-00987-8
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s12540-021-00987-8