Cu/Cr co-stabilization mechanisms in a simulated Al2O3-Fe2O3-Cr2O3-CuO waste system

  • Research Article
  • Published:
Frontiers of Environmental Science & Engineering Aims and scope Submit manuscript

Abstract

Chromium slag usually contains various heavy metals, making its safe treatment difficult. Glass-ceramic sintering has been applied to resolve this issue and emerged as an effective method for metal immobilization by incorporating heavy metals into stable crystal structures. Currently, there is limited knowledge about the reaction pathways adopted by multiple heavy metals and the co-stabilization functions of the crystal structure. To study the Cu/Cr co-stabilization mechanisms during thermal treatment, a simulated system was prepared using a mixture with a molar ratio of Al2O3:Fe2O3:Cr2O3: CuO = 1:1:1:3. The samples were sintered at temperatures 600–1300°C followed by intensive analysis of phase constitutions and microstructure development. A spinel phase (CuFexAlyCr2−xyO4) started to generate at 700°C and the incorporation of Cu/Cr into the spinel largely complete at 900°C, although the spinel peak intensity continued increasing slightly at temperatures above 900°C. Fe2O3/Cr2O3 was more easily incorporated into the spinel at lower temperatures, while more Al2O3 was gradually incorporated into the spinel at higher temperatures. Additionally, sintered sample microstructures became more condensed and smoother with increased sintering temperature. Cu / Cr leachability substantially decreased after Cu/Cr incorporation into the spinel phase at elevated temperatures. At 600°C, the leached ratios for Cu and Cr were 6.28% and 0.65%, respectively. When sintering temperature was increased to 1300°C, the leached ratios for all metal components in the system were below 0.2%. This study proposes a sustainable method for managing Cu/Cr co-exist slag at reasonable temperatures.

This is a preview of subscription content, log in via an institution to check access.

Access this article

Price excludes VAT (USA)
Tax calculation will be finalised during checkout.

Instant access to the full article PDF.

Institutional subscriptions

Similar content being viewed by others

References

  • Ballesteros S, Rincón J M, Rincón-Mora B, Jordán M M (2017). Vitrification of urban soil contamination by hexavalent chromium. Journal of Geochemical Exploration, 174: 132–139

    Article  CAS  Google Scholar 

  • Bragg W H, Bragg W L (1913). The reflection of X-rays by crystals. Proceedings of the Royal Society of London. Series A, Containing Papers of a Mathematical and Physical Character, 88(605): 428–438

    Google Scholar 

  • Brown M E, Gallagher P K (2011). Handbook of Thermal Analysis and Calorimetry: Recent Advances, Techniques and Applications. Amsterdam: Elsevier Science

    Google Scholar 

  • Cerbo A A V, Ballesteros F Jr, Chen T C, Lu M C (2017). Solidification/stabilization of fly ash from city refuse incinerator facility and heavy metal sludge with cement additives. Environmental Science and Pollution Research International, 24(2): 1748–1756

    Article  CAS  Google Scholar 

  • Chen Q, Zhang L, Ke Y, Hills C, Kang Y (2009). Influence of carbonation on the acid neutralization capacity of cements and cement-solidified/stabilized electroplating sludge. Chemosphere, 74(6): 758–764

    Article  CAS  Google Scholar 

  • El-Shobaky G A, Fagal G A, Amin N H (1989). Thermal solid-solid interaction between CuO and pure Al2O3 solids. Thermochimica Acta, 141: 205–216

    Article  CAS  Google Scholar 

  • Fu F, Xie L, Tang B, Wang Q, Jiang S (2012). Application of a novel strategy—Advanced fenton-chemical precipitation to the treatment of strong stability chelated heavy metal containing wastewater. Chemical Engineering Journal, 189–190: 283–287

    Article  Google Scholar 

  • Kim J H, Kim J S, Han S H, Kang H W, Lee H G, Cheon C I (2017). Low-temperature sintering and piezoelectric properties of CuO-doped (K,Na)NbO3 ceramics. Materials Research Bulletin, 96: 121–125

    Article  CAS  Google Scholar 

  • Liao C, Tang Y, Liu C, Shih K, Li F (2016). Double-Barrier mechanism for chromium immobilization: A quantitative study of crystallization and leachability. Journal of Hazardous Materials, 311: 246–253

    Article  CAS  Google Scholar 

  • Ma G, Garbers-Craig A (2006). A review on the characteristics, formation mechanisms and treatment processes of Cr (VI)-containing pyrometallurgical wastes. Journal of the Southern African Institute of Mining and Metallurgy, 106: 753–763

    CAS  Google Scholar 

  • Ma W, Meng F, Qiu D, Tang Y (2020). Co-stabilization of Pb/Cu/Zn by beneficial utilization of sewage sludge incineration ash: Effects of heavy metal type and content. Resources, Conservation and Recycling, 156: 104671

    Article  Google Scholar 

  • Mao L, Tang R, Wang Y, Guo Y, Su P, Zhang W (2018). Stabilization of electroplating sludge with iron sludge by thermal treatment via incorporating heavy metals into spinel phase. Journal of Cleaner Production, 187: 616–624

    Article  CAS  Google Scholar 

  • Naja G M, Volesky B (2009). Treatment of metal-bearing effluents: Removal and recovery. Heavy Metals in the Environment, 247–292

    Google Scholar 

  • Okuno N, Ishikawa Y, Shimizu A, Yoshida M (2004). Utilization of sludge in building material. Water science and technology: A journal of the International Association on Water Pollution Research, 49: 225–232

    Article  CAS  Google Scholar 

  • OuYang S, Zhang Y, Chen Y, Zhao Z, Wen M, Li B, Shi Y, Zhang M, Liu S (2019). Preparation of glass-ceramics using chromium-containing stainless steel slag: Crystal structure and solidification of heavy metal chromium. Scientific Reports, 9(1): 1964–1973

    Article  Google Scholar 

  • Qu Y, Yang Y, Zou Z, Zeilstra C, Meijer K, Boom R (2014). Thermal decomposition behaviour of fine iron ore particles. ISIJ International, 54(10): 2196–2205

    Article  CAS  Google Scholar 

  • Roessler J G, Oehmig W N, Blaisi N I, Townsend T G (2014). Chemical characterization of high-temperature arc gasification slag with a focus on element release in the environment. Environmental Science & Technology, 48(14): 7781–7788

    Article  CAS  Google Scholar 

  • Sarıkaya Y, Ada K, Önal M (2008). A model for initial-stage sintering thermodynamics of an alumina powder. Powder Technology, 188(1): 9–12

    Article  Google Scholar 

  • Shih K, Tang Y (2011). Prolonged toxicity characteristic leaching procedure for nickel and copper aluminates. Journal of Environmental Monitoring, 13(4): 829–835

    Article  CAS  Google Scholar 

  • Shih K, Tang Y (2012). Incorporating simulated zinc ash by kaolinite- and sludge-based ceramics: Phase transformation and product leachability. Chinese Journal of Chemical Engineering, 20(3): 411–416

    Article  CAS  Google Scholar 

  • Stumm W, Morgan J J (2013). Aquatic Chemistry: Chemical Equilibria and Rates in Natural Waters. London: Wiley Blackwell

    Google Scholar 

  • Tang Y, Chan S W, Shih K (2014a). Copper stabilization in beneficial use of waterworks sludge and copper-laden electroplating sludge for ceramic materials. Waste Management (New York, N.Y.), 34(6): 1085–1091

    Article  CAS  Google Scholar 

  • Tang Y, Chui S S Y, Shih K, Zhang L (2011). Copper stabilization via spinel formation during the sintering of simulated copper-laden sludge with aluminum-rich ceramic precursors. Environmental Science & Technology, 45(8): 3598–3604

    Article  CAS  Google Scholar 

  • Tang Y, Lu X, Shih K (2014b). Alumina polymorphs affect the metal immobilization effect when beneficially using copper-bearing industrial sludge for ceramics. Chemosphere, 117: 575–581

    Article  CAS  Google Scholar 

  • Tang Y, Shih K, Chan K (2010). Copper aluminate spinel in the stabilization and detoxification of simulated copper-laden sludge. Chemosphere, 80(4): 375–380

    Article  CAS  Google Scholar 

  • Tang Y, Shih K, Liu C, Liao C (2016). Cubic and tetragonal ferrite crystal structures for copper ion immobilization in an iron-rich ceramic matrix. RSC Advances, 6(34): 28579–28585

    Article  CAS  Google Scholar 

  • Tsuchida T, Furuichi R, Sukegawa T, Furudate M, Ishii T (1984). Thermoanalytical study on the reaction of the CuO—Al2O3(η, γ AND α) systems. Thermochimica Acta, 78(1–3): 71–80

    Article  CAS  Google Scholar 

  • Wu F, Tang Y, Lu X, Liu C, Lv Y, Tong H, Ning Z, Liao C, Li F (2019). Simultaneous immobilization of Zn(II) and Cr(III) in spinel crystals from beneficial utilization of waste brownfield-site soils. Clays and Clay Minerals, 67(4): 315–324

    Article  CAS  Google Scholar 

  • Wu P, Tang Y, Cai Z (2018). Dual role of coal fly ash in copper ion adsorption followed by thermal stabilization in a spinel solid solution. RSC Advances, 8(16): 8805–8812

    Article  CAS  Google Scholar 

Download references

Acknowledgements

This work is supported financially by the National Natural Science Foundation of China (Grant No. 21707063), the National Key R&D Program of China (Grant No. 2018YFC1902904), and the Natural Science Foundation of Guangdong Province in China (No. 2019A15150-11836). This work is also sponsored by State Environmental Protection Key Laboratory of Integrated Surface Water-Groundwater Pollution Control. The authors are sincerely grateful for the help of SUSTech Core Research Facilities.

Author information

Authors and Affiliations

Authors

Corresponding author

Correspondence to Yuanyuan Tang.

Additional information

Highlights

• Cu and Cr can be mostly incorporated into CuFexAlyCr2−xyO4 with a spinel structure.

• Spinel phase is the most crucial structure for Cu and Cr co-stabilization.

• Compared to Al, Fe and Cr are easier to be incorporated into the spinel structure.

• ‘Waste-to-resource’ by thermal process at attainable temperatures can be achieved.

Electronic supplementary material

Rights and permissions

Reprints and permissions

About this article

Check for updates. Verify currency and authenticity via CrossMark

Cite this article

Meng, F., Xia, Y., Zhang, J. et al. Cu/Cr co-stabilization mechanisms in a simulated Al2O3-Fe2O3-Cr2O3-CuO waste system. Front. Environ. Sci. Eng. 15, 116 (2021). https://doi.org/10.1007/s11783-021-1408-4

Download citation

  • Received:

  • Revised:

  • Accepted:

  • Published:

  • DOI: https://doi.org/10.1007/s11783-021-1408-4

Keywords

Navigation