Abstract
In present work, a novel SiCf reinforced (Al3Ti + Al3Ni)-based metallic–intermetallic laminate (Ti–(Al3Ti + Al3Ni)/SiCf-MIL) composite without centerline defect was prepared using Ti, Al foils, NiTi wires and SiC fibers by vacuum hot pressing sintering method. Electron backscatter diffraction was employed to characterize the microstructure and phase constituents of Ti–(Al3Ti + Al3Ni)/SiCf-MIL composite during various stages of preparation process. The elimination mechanism of intermetallic centerline was discussed. Besides, quasi-static compressive performance and fracture toughness of the synthesized composite were investigated. The experimental results indicated that as reaction time increasing, the NiTi/Al interfacial reaction occurred prior to the Ti/Al interfacial reaction to form an Al3Ti/Al3Ni zone. Then, the oxides gathered at the front of Ti/Al interfacial reaction layer were dispersed in the intermetallic layer rather than being pushed together to generate the centerline due to the Al3Ti/Al3Ni zone. After reaction, there were no residual NiTi phases and intermetallic layers mainly consisting of Al3Ti and Al3Ni phases were obtained in this composite. In addition, high angle grain boundaries in Al3Ti grains occupied a large proportion, conversely, low angle grain boundaries dominated in Al3Ni grains. Furthermore, stress concentration appears at the interface between layers instead of along the middle plane of intermetallic layer. Moreover, both compressive strength and fracture toughness of the composite are superior in comparison with SiCf reinforced Ti–Al3Ti metallic–intermetallic laminate composite (Ti–Al3Ti/SiCf-MIL) ascribed to the elimination of centerline.
Graphic Abstract
Similar content being viewed by others
Availability of Data and Materials
All data generated or analysed during this study are included in this article.
Code Availability
Not applicable.
References
J.C. Rawers, D.E. Alman, Compos. Sci. Technol. 54, 379 (1995)
D.E. Alman, C.P. Dogn, J.A. Hawk, J.C. Rawers, Mater. Sci. Eng. A 192–193, 624 (1995)
H. Wang, J. Han, S. Du, D.O. Northwood, Mater. Sci. Eng. A 445–446, 517 (2007)
D.J. Harach, K.S. Vecchio, Metall. Mater. Trans. A 32, 1493 (2001)
K.S. Vecchio, JOM-J. Min. Met. Mat. S. 57, 25 (2005)
F. Jiang, R.M. Kulin, K.S. Vecchio, JOM-J. Min. Met. Mat. S. 62, 34 (2010)
X. Fan, M. Yuan, Q. Qin, Rare Metal Mat. Eng. 47, 2615 (2018)
Z. Wei, M. Yuan, X. Shen, F. Han, Y. Yao, L. Xin, L. Yao, Mater. Charact. 165, 110374 (2020)
D.R. Bloyer, R.O. Ritchie, K.T. Venkateswara Rao, Metall. Mater. Trans. A 29, 2483 (1998)
M. Konieczny, Kovove Mater. 45, 313 (2007)
K.S. Vecchio, Nano Microstruct. Design Adv. Mater. 649, 243 (2003)
A. Rohatgi, D.J. Harach, K.S. Vecchio, K.P. Harvey, Acta Mater. 51, 2933 (2003)
R.R. Adharapurapu, K.S. Vecchio, F. Jiang, A. Rohatgi, Metall. Mater. Trans. A 36, 3217 (2005)
T. Li, F. Grignon, D.J. Benson, K.S. Vecchio, E.A. Olevsky, F. Jiang, A. Rohatgi, R.B. Schwarz, M.A. Meyers, Mater. Sci. Eng. A 374, 10 (2004)
T. Li, E.A. Olevsky, M.A. Meyers, Mater. Sci. Eng. A 473, 49 (2008)
L.M. Peng, J.H. Wang, H. Li, J.H. Zhao, L.H. He, Scripta Mater. 52, 243 (2005)
L.M. Peng, H. Li, J. H. Wang, Mater. Sci. Eng. A 406, 309 (2005)
Y.V. Milman, D.B. Miracle, S.I. Chugunova, I.V. Voskoboinik, N.P. Korzhova, T.N. Legkaya, Y.N. Podrezov, Intermetallics 9, 839 (2001)
Y. Cao, C. Guo, S. Zhu, N. Wei, R.A. Javed, F. Jiang, Mater. Sci. Eng. A 637, 235 (2015)
P. Zhou, C. Guo, E. Wang, Z. Wang, Y. Chen, F. Jiang, Mater. Sci. Eng. A 665, 66 (2016)
W. Zhang, Y.Q. Yang, G.M. Zhao, B. Huang, Z.Q. Feng, X. Luo, M.H. Li, J.H. Lou, Intermetallics 33, 54 (2013)
Z. Lu, F. Jiang, Y. Chang, Z. Niu, Z. Wang, C. Guo, Mater. Design 143, 274 (2018)
R.A. MacKay, P.K. Brindley, F.H. Froes, JOM-J. Min. Met. Mat. S. 43, 23–29 (1991)
S. Nourbakhsh, H. Margolin, Mater. Manuf. Process. 81, 283 (2013)
S. Djanarthany, J.C. Viala, J. Bouix, Mater. Sci. Eng. A 300, 211 (2001)
K.S. Vecchio, F. Jiang, Mater. Sci. Eng. A 649, 407 (2016)
C. Lin, Y. Han, C. Guo, Y. Chang, X. Han, L. Lan, F. Jiang, J. Alloy. Compd. 722, 427 (2017)
C. Lin, F. Jiang, Y. Han, E. Wang, D. Yuan, C. Guo, J. Alloy. Compd. 743, 52 (2018)
Y. Han, C. Lin, X. Han, Y. Chang, C. Guo, F. Jiang, Mater. Sci. Eng. A 688, 338 (2017)
Y. Han, F. Jiang, C. Lin, D. Yuan, H. Huang, E. Wang, Z. Wang, C. Guo, J. Alloy. Compd. 729, 1145 (2017)
M. Mirjalili, M. Soltanieh, K. Matsuura, M. Ohno, Intermetallics 32, 297 (2013)
Y. Wang, H. Wang, X. Liu, K.S. Vecchio, Mater. Sci. Eng. A 682, 454 (2017)
E. Wang, F. Kang, H. Wang, Y. Cao, F. Jiang, J. Alloy. Compd. 775, 1307 (2019)
A. Školáková, J. Leitner, P. Salvetr, P. Novák, D. Deduytsche, J. Kopeček, C. Detavernier, D. Vojtěch, Mater. Chem. Phys. 230, 122 (2019)
R.D. Price, F. Jiang, R.M. Kulin, K.S. Vecchio, Mater. Sci. Eng. A 528, 3134 (2011)
Y. Du, G. Fan, Q. Wang, L. Geng, Metall. Mater. Trans. A 48, 168 (2016)
H. Nie, W. Liang, H. Chen, F. Wang, T. Li, C. Chi, X. Li, J. Alloy. Compd. 781, 696 (2019)
L. Qin, M. Fan, X. Guo, J. Tao, Vacuum 155, 96 (2018)
F. Jiao, M. Liu, F. Jiang, J. Zhao, P. Li, Z. Wang, Mater. Sci. Eng. A 765, 138255 (2019)
Y. Tan, L. Xu, Z. Xu, T. Ali, Z. Ma, X. Cheng, H. Cai, Mater. Sci. Eng. A 767, 138296 (2019)
Acknowledgements
The authors gratefully acknowledge the financial supports of this study by the Initial Scientific Research Fund in Changshu Institute of Technology (KYZ2018044Q, KYZ2018043Q) and the National Natural Science Foundation of China (No. 51901058).
Author information
Authors and Affiliations
Corresponding author
Ethics declarations
Conflict of interest
The authors declare that they have no conflict of interest.
Additional information
Publisher's Note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
About this article
Cite this article
Han, Y., Que, Q., Cheng, R. et al. Microstructure Evolution and Mechanical Performances of SiCf Reinforced (Al3Ti + Al3Ni)-Based Metallic–Intermetallic Laminate Composite. Met. Mater. Int. 27, 4035–4046 (2021). https://doi.org/10.1007/s12540-020-00942-z
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s12540-020-00942-z